Anti-aging anti-fogdrop greenhouse film and preparation method thereof

An anti-fog and greenhouse film technology, applied in the field of composite materials, can solve the problems of increased cost and short aging time of greenhouse film, and achieve the effect of long anti-aging time and broad application prospects.

Inactive Publication Date: 2015-01-28
SUZHOU POLYMER NEW MATERIALS TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the aging time of the common greenhouse film is short, and it is generally replaced within one year when the greenhouse is closed, which greatly increases the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-aging anti-fogdrop greenhouse film and preparation method thereof
  • Anti-aging anti-fogdrop greenhouse film and preparation method thereof
  • Anti-aging anti-fogdrop greenhouse film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An anti-aging and anti-fog droplet greenhouse film, the components and the mass fraction of each component are as follows: polyethylene (52 parts of LDPE and 8 parts of LLDPE) 60 parts, 0.1 part of triphenyl phosphite, dilaurin thiodipropionate 0.15 part of ester, 0.05 part of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, 3 parts of sodium alkylbenzene sulfonate, 4 parts of polyvinylpyrrolidone, dibutyl sulfide 1 part of dioctyl acid, 0.1 part of antioxidant 1010.

[0021] The preparation method of the anti-aging and anti-fog droplet greenhouse film is to weigh each component in proportion, add it into a high-speed mixer, and mix at a high speed. 10min, and then extruded and granulated through a twin-screw extruder, blow-molded to obtain the finished product; the temperatures of each section of the twin-screw extruder are: 130°C for the first zone, 150°C for the second zone, and 150°C for the third zone. 160℃, four-zone temperature control 170℃, head temperature 170℃,...

Embodiment 2

[0027] An anti-aging and anti-fog droplet greenhouse film, the components and the mass fraction of each component are as follows: 80 parts of polyethylene (67 parts of LDPE and 13 parts of LLDPE), 0.9 part of triphenyl phosphite, and dilaurin thiodipropionate 0.2 part of ester, 0.18 part of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, 6 parts of sodium alkylbenzene sulfonate, 1 part of polyvinylpyrrolidone, dibutyl sulfide 3 parts of dioctyl acid, 0.5 part of antioxidant 1010.

[0028] The preparation method of the anti-aging and anti-fog droplet greenhouse film is to weigh each component in proportion, add it into a high-speed mixer, and mix at a high speed. 10min, and then extruded and granulated through a twin-screw extruder, blow-molded to obtain the finished product; the temperatures of each section of the twin-screw extruder are: 130°C for the first zone, 150°C for the second zone, and 150°C for the third zone. 160℃, four-zone temperature control 170℃, head temperatur...

Embodiment 3

[0034] Anti-aging and anti-fogging greenhouse film, the components and the mass fraction of each component are as follows: polyethylene (61 parts of LDPE and 9 parts of LLDPE) 70 parts, triphenyl phosphite 0.5 parts, dilauryl thiodipropionate 0.18 parts parts, 0.08 parts of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, 4 parts of sodium alkylbenzenesulfonate, 2 parts of polyvinylpyrrolidone, dibutyric acid disulfide 1 part of octyl ester, 0.2 part of antioxidant DLPP.

[0035]The preparation method of the anti-aging and anti-fog droplet greenhouse film is to weigh each component in proportion, add it into a high-speed mixer, and mix at a high speed. 10min, and then extruded and granulated through a twin-screw extruder, blow-molded to obtain the finished product; the temperatures of each section of the twin-screw extruder are: 130°C for the first zone, 150°C for the second zone, and 150°C for the third zone. 160℃, four-zone temperature control 170℃, head temperature 170℃, ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-aging anti-fogdrop greenhouse film and a preparation method thereof. The anti-aging anti-fogdrop greenhouse film is prepared from the following components in parts by mass: 60-80 parts of polyethylene, 0.1-0.9 part of triphenyl phosphite, 0.15-0.2 part of dilauryl thiodipropionate, 0.05-0.18 part of 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, 3-6 parts of sodium alkyl benzene sulfonate, 1-4 parts of polyvinylpyrrolidone, 1-3 parts of dioctyl sulfodibutyrate and 0.1-0.5 part of antioxidant. The polyethylene is prepared by mixing LDPE (low-density polyethylene) and LLDPE (linear low-density polyethylene) according to a mass ratio of (6-8):1. The antioxidant is antioxidant 1010 or antioxidant DLPP. The greenhouse film has long anti-aging time, and does not need to be replaced within three years; the anti-fogdrop effective time of the greenhouse film is up to 900 hours; and thus, the greenhouse film has wide application prospects.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to an anti-aging and anti-fog droplet greenhouse film and a preparation method thereof. Background technique [0002] As the covering material of the greenhouse, the greenhouse film isolates the crops from the external environment, so that the crops are in a relatively closed and controllable growth environment. Through the greenhouse covering material, the exchange and circulation of energy (light, heat) and substances (water, air fertilizer, etc.) between the indoor or shed environment where crops are grown and the external environment are constantly carried out, and the two influence each other. interaction. Therefore, the greenhouse covering material is one of the most important components in the greenhouse. The varieties and characteristics of the greenhouse covering material directly affect the growth of crops in the greenhouse. The selection of g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L39/06C08K5/00C08K5/526C08K5/372C08K5/42B29C47/92B29C48/92
CPCC08L23/06B29C48/92B29C2948/92561B29C2948/9258B29C2948/92704C08J5/18C08J2323/06C08J2423/08C08K2201/014C08L2201/08C08L2203/16C08L2205/03C08L2207/066C08L23/0815C08L39/06C08K5/00C08K5/526C08K5/372C08K5/3437C08K5/42
Inventor 翟红波杨振枢韦洪屹
Owner SUZHOU POLYMER NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap