Additive for fracturing proppant, fracturing proppant and preparation method

A fracturing proppant and additive technology, used in chemical instruments and methods, earthwork drilling, and fluid production, can solve the problems of low cost performance and high production costs, and achieve the advantages of low cost, reduced preparation cost, and reduced firing temperature. Effect

Active Publication Date: 2017-02-08
ZHENGZHOU RUNBAO REFRACTORY MATERIAL CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The performance index of the fracturing proppant manufactured by these two methods has only reached the upper limit requirements of the petrochemical industry standard, and its production cost is high, but the cost performance is too low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Additive for fracturing proppant, fracturing proppant and preparation method
  • Additive for fracturing proppant, fracturing proppant and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The additive for fracturing proppant in this embodiment is composed of the following components in weight percent: 16% of industrial boric acid, 68% of magnesia clay, and 16% of silica fume.

[0030] The pressure proppant in this example is composed of the following components in weight percentage: 60% of low-grade bauxite, 12% of calcined kaolin, 20% of fracturing proppant production waste, and 8% of additives for fracturing proppant.

[0031] The preparation of pressure proppant in this embodiment comprises the following steps:

[0032] (1) The low-grade bauxite, fracturing proppant production waste, and calcined kaolin are respectively crushed into 30mm particles by a jaw crusher, and then loaded into the batching bin, and the ratio (weight percentage) is set for each bin. Then put the additive for fracturing proppant into the batching bin and set the ratio, each bin is fed according to the set ratio to the ball mill to be ground into a fine powder with a particle si...

Embodiment 2

[0035] The additive for fracturing proppant in this embodiment is composed of the following components in weight percent: 18% industrial boric acid, 65% magnesia clay, and 17% silica fume.

[0036] The pressure proppant in this example is composed of the following components in weight percentage: 55% of low-grade bauxite, 15% of calcined kaolin, 25% of fracturing proppant production waste, and 5% of additives for fracturing proppant.

[0037] The preparation of pressure proppant in this embodiment comprises the following steps:

[0038] (1) The low-grade bauxite, fracturing proppant production waste, and calcined kaolin are respectively crushed into 30mm particles by a jaw crusher, and then loaded into the batching bin, and the ratio (weight percentage) is set for each bin. Then put the additive for fracturing proppant into the batching bin and set the ratio, each bin is fed according to the set ratio to the ball mill to be ground into a fine powder with a particle size of 400...

Embodiment 3

[0041]The additive for fracturing proppant in this embodiment is composed of the following components in weight percent: 17.5% boric acid, 70% magnesia clay, and 12.5% ​​silica fume.

[0042] The pressure proppant in this example is composed of the following components in weight percentage: 65% of low-grade bauxite, 8% of calcined kaolin, 15% of fracturing proppant production waste, and 15% of additives for fracturing proppant.

[0043] The preparation of pressure proppant in this embodiment comprises the following steps:

[0044] (1) The low-grade bauxite, fracturing proppant production waste, and calcined kaolin are respectively crushed into 30mm particles by a jaw crusher, and then loaded into the batching bin, and the ratio (weight percentage) is set for each bin. Then put the additive for fracturing proppant into the batching bin and set the ratio, each bin is fed according to the set ratio to the ball mill to be ground into a fine powder with a particle size of 400 mesh ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an additive for a fracturing propping agent, the fracturing propping agent and a preparation method, belonging to the technical field of oil field chemical industry. The additive for the fracturing propping agent comprises the following components by weight: 15.5 to 18% of boric acid, 65 to 70% of attaclay and 12.5 to 18% of silica fume. The fracturing propping agent comprises the following components by weight: 52 to 82% of low-grade bauxitic clay, 5 to 15% of calcined kaolin, 10 to 25% of waste produced fracturing propping agents and 3 to 8% of the additive for the fracturing propping agent. The additive for the fracturing propping agent prepared in the invention has low cost; the prepared fracturing propping agent has the advantages of low volume density, low apparent density, low acid solubility, a low broken rate, etc., enables production cost and fracturing cost to be reduced and is favorable for yield increase of oil and gas fields. According to the invention, the waste produced fracturing propping agents are added as a raw material, so cyclic utilization of a waste material is realized.

Description

technical field [0001] The invention specifically relates to an additive for a fracturing proppant, a fracturing proppant using the additive and a preparation method thereof, and belongs to the technical field of oilfield chemicals. Background technique [0002] The purpose of the fracturing proppant is to split the oil-gas-bearing rock strata after the high closure pressure and low permeability deposits are fractured when the oil and gas wells are exploited, and the oil and gas are collected from the channels formed by the cracks. The ceramsite proppant material is used together with the high-pressure solution to enter the formation and fill in the rock fractures to support the cracks from closing due to stress release, thereby maintaining high conductivity, allowing oil and gas to flow smoothly, and increasing production. Ceramsite proppant is widely used in the exploitation of oil and gas to increase oil and gas production and support the ground from subsidence. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/80C04B33/13
CPCC04B35/10C04B2235/349C09K8/80
Inventor 贾勤长朱现峰
Owner ZHENGZHOU RUNBAO REFRACTORY MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap