Environmental-friendly gel plugging agent applicable to low-temperature oil pool and applications of gel plugging agent

A technology of cryogenic oil and jelly, which is applied in drilling compositions, production fluids, wellbore/well components, etc., can solve problems that are unfavorable to environmental protection, the health of operators, difficult to meet on-site construction operations, and unfavorable mine construction operations. and other problems, to achieve the effect of controllable glue forming time, convenient construction and use, and good injection performance.

Active Publication Date: 2014-08-13
CHINA UNIV OF GEOSCIENCES (BEIJING)
View PDF7 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The gelling time of the plugging agent is short, which is not conducive to the construction operation of the mine, and it is difficult to meet the requirements of the on-site construction operation
The chromium-based polymer jelly plugging agent currently used on site is highly toxic due to the use of chromium-based cross-linking agents, which is not conducive to environmental protection and the health of operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-friendly gel plugging agent applicable to low-temperature oil pool and applications of gel plugging agent
  • Environmental-friendly gel plugging agent applicable to low-temperature oil pool and applications of gel plugging agent
  • Environmental-friendly gel plugging agent applicable to low-temperature oil pool and applications of gel plugging agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] An environment-friendly plugging agent suitable for low-temperature oil reservoirs, composed of 0.2% amphoteric polyacrylamide (LPAM), 0.5% organic zirconium crosslinking agent solution, and 99.3% water. The organic zirconium crosslinking agent is a combination of zirconium citrate and zirconium lactate in a mass ratio of 2:1.

[0047] Preparation:

[0048] Weigh zirconium citrate and zirconium lactate according to the mass ratio of 2:1, add into water under stirring, mix evenly, and make an organic zirconium crosslinking agent solution with a mass fraction of 30%;

[0049] Proportionally, take 10 g of amphoteric polyacrylamide aqueous solution with a mass fraction of 1.0%, add 0.25 g of organic zirconium crosslinking agent solution prepared while stirring, and then add 39.75 g of water and stir to obtain the product.

[0050] The gelling time of the plugging agent system at 25°C is 60 hours, and the gelling strength is grade E; at 30°C, the gelling time is 50 hours, a...

Embodiment 2

[0052] The environmentally friendly plugging agent suitable for low-temperature oil reservoirs is composed of: 0.4% amphoteric polyacrylamide, 1.0% organic zirconium crosslinking agent solution, and 98.6% water. The organozirconium crosslinking agent solution is zirconium citrate and zirconium lactate mixed in a mass ratio of 1:1, added into water under stirring, and mixed evenly to make an organozirconium crosslinking agent solution with a mass fraction of 25%;

[0053] In 20 g of nonionic polyacrylamide aqueous solution with a mass fraction of 1.0%, add 0.5 g of organic zirconium crosslinking agent solution while stirring, and then add 29.5 g of water and stir to obtain the product. The gelling time of the plugging agent system is 40 hours at 25°C, and the gelling strength is G grade; the gelling time is 23 hours at 30°C, and the gelling strength is G grade; the gelling time is 14 hours at 35°C, and the gelling strength is Grade G.

Embodiment 3

[0055] The environmentally friendly plugging agent suitable for low-temperature oil reservoirs is composed of: 0.6% amphoteric polyacrylamide, 2.0% organic zirconium crosslinking agent solution, and 97.4% water. The organic zirconium crosslinking agent solution is a combination of zirconium citrate and zirconium lactate in a mass ratio of 3:1, and water is added to make an organic zirconium crosslinking agent solution with a mass fraction of 20%;

[0056] In 30 g of amphoteric polyacrylamide aqueous solution with a mass fraction of 1.0%, 1.0 g of organic zirconium crosslinking agent solution was added while stirring, and then 19 g of water was added and stirred to obtain the product. The gelling time of the plugging agent system is 15 hours at 25°C, and the gelling strength is H grade; the gelling time is 10 hours at 30°C, and the gelling strength is H grade; the gelling time is 4 hours at 35°C, and the gelling strength is Grade H.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
solid contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to an environmental-friendly gel plugging agent applicable to a low-temperature oil pool and applications of the gel plugging agent. The gel plugging agent is prepared from 0.2%-0.6% of ampholytic polyacryamide, 0.5%-2.0% of an organic zirconium cross-linking agent solution, and the balance of water. The gel plugging agent is used for deep water shut-off and profile control constructions in the low-temperature oil pool of 25-35 DEG C and by virtue of the plugging agent, the recovery rate of crude oil can be raised. The gel plugging agent can form a non-flowing high-strength gel system at low temperature and has low viscosity and good injectivity; without toxic chemical materials such as chromium type cross-linking agents, the gel plugging agent is conductive to environmental friendliness.

Description

technical field [0001] The invention relates to a technology for further enhancing crude oil recovery in the technical field of oil and gas field development engineering, in particular to an environment-friendly jelly plugging agent for water shutoff and profile control in low-temperature oil reservoirs and its application. technical background [0002] my country is one of the countries with a relatively high proportion of oil fields developed by water flooding in the world, and the reserves developed by water flooding account for more than 60% of the total reserves. Oilfields developed by water flooding occupy a pivotal position in my country's oil development. As the water flooding development enters the middle and late stages, the uneven water flooding has further evolved into large channel channeling, which leads to further deterioration of the water flooding development effect. The basis for stable production is weakening. However, there is still a large amount of rem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/512E21B43/22
CPCC09K8/5083C09K8/512E21B33/13
Inventor 由庆戴彩丽赵光王磊赵明伟范洪富赵健慧杨帅熊伟王国辉王秀英崔亚赵福麟
Owner CHINA UNIV OF GEOSCIENCES (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com