Anti-aging and anti-tension plastic and preparation method thereof

A tensile and anti-aging technology, applied in the field of plastic materials, can solve the problems of poor anti-aging and anti-stretching effects of plastics, and achieve the effect of reasonable formula and simple preparation method.

Inactive Publication Date: 2014-07-30
LUHE SHOUCHUANG PLASTIC HARDWARE PROD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved: the problem of poor anti-aging and stretch resistance of conventional plastics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] In this embodiment, an anti-aging and stretch-resistant plastic is characterized in that it is composed of the following components according to the weight ratio: 52 parts of rubber, 28 parts of methylol fatty amine, 16 parts of amyl acetate, 10 parts of tridecyl ester, Zinc oxide 10 parts, coupling agent 30 parts. First, put rubber, methylol fatty amine and coupling agent in a reaction vessel, stir and react at a temperature of 50°C, after reacting for 60 minutes, raise the temperature, gradually add amyl acetate, tridecyl and zinc oxide, and stir Reaction, at the same time, the temperature is raised to 120°C for 2 hours, and then sent to an injection molding machine for injection molding.

[0009] The plastic tensile strength of this embodiment is 27MPa, and the 500h photoaging impact strength retention rate is 100%.

Embodiment 2

[0011] In this embodiment, an anti-aging and stretch-resistant plastic is characterized in that it is composed of the following components according to the weight ratio: 67 parts of rubber, 21 parts of methylol fatty amine, 34 parts of amyl acetate, 20 parts of tridecyl ester, Zinc oxide 20 parts, coupling agent 20 parts. First, put rubber, methylol fatty amine and coupling agent in a reaction vessel, stir and react at a temperature of 50°C, after reacting for 60 minutes, raise the temperature, gradually add amyl acetate, tridecyl and zinc oxide, and stir Reaction, at the same time, the temperature is raised to 120°C for 2 hours, and then sent to an injection molding machine for injection molding.

[0012] The plastic tensile strength of this embodiment is 29MPa, and the 500h photoaging impact strength retention rate is 100%.

Embodiment 3

[0014] In this embodiment, an anti-aging and stretch-resistant plastic is characterized in that it is composed of the following components according to weight ratio: 62 parts of rubber, 26 parts of methylol fatty amine, 20 parts of amyl acetate, 17 parts of tridecyl ester, Zinc oxide 15 parts, coupling agent 24 parts. First, put rubber, methylol fatty amine and coupling agent in a reaction vessel, stir and react at a temperature of 50°C, after reacting for 60 minutes, raise the temperature, gradually add amyl acetate, tridecyl and zinc oxide, and stir Reaction, at the same time, the temperature is raised to 120°C for 2 hours, and then sent to an injection molding machine for injection molding.

[0015] The tensile strength of the plastic in this embodiment is 30MPa, and the 500h photoaging impact strength retention rate is 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-aging and anti-tension plastic and a preparation method thereof. The plastic comprises the following components in parts by weight: 52-67 parts of rubber, 21-28 parts of hydroxymethyl aliphatic amine, 16-34 parts of amyl acetate, 10-20 parts of tridecyl, 10-20 parts of zinc oxide and 20-30 parts of coupling agent. The preparation method of the anti-aging and anti-tension plastic is characterized by firstly putting the rubber, hydroxymethyl aliphatic amine and the coupling agent in a reaction vessel, stirring the materials to react the materials at 50 DEG C, heating after reacting for 60 minutes, gradually adding amyl acetate, tridecyl and zinc oxide, stirring the materials to react the materials, simultaneously heating to 120 DEG C to react the materials for 2 hours, and sending the reactant to an injection molding machine to undergo injection molding. The plastic has a reasonable formula. The preparation method is simple. The prepared plastic is anti-aging and anti-tension. Experiments prove that the tensile strength of the plastic is 27-30MPa and the 500h photo-aging impact strength retention rate is 100%.

Description

technical field [0001] The invention relates to an anti-aging and tensile-resistant plastic and a preparation method thereof, belonging to the field of plastic materials. Background technique [0002] Plastic material is a material with good performance. Because plastic has the advantages of light weight, no rust, and good insulation, it is used in many aspects of electronic product production. Plastic is easy to process, has good dimensional stability and surface gloss, and is easy to paint. Coloring, widely used in the field of electronic appliances. In recent years, in the electronic and electrical market, plastics maintain their position in the electronic and electrical market, and their anti-aging performance must be improved. However, the quality of plastics on the market is not stable, the anti-aging performance is not good, and they are still prone to aging, cracking, and reduced service life. Some plastics with better effects are made through complicated processes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/00C08K5/17C08K3/22
Inventor 戴晓宸
Owner LUHE SHOUCHUANG PLASTIC HARDWARE PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap