EPS line mechanical plastering dedicated mortar

A technology for mechanically plastering surfaces and lines, applied in the field of construction mortar, can solve the problems of corner falling, mortar easy to aggregate, and particle size is too large, so as to avoid sagging and falling corners, improve mixing efficiency, and increase smooth performance.

Inactive Publication Date: 2014-07-23
奥捷科技股份有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the process of adding water and stirring, there will be bubbles with uneven pore size in the mortar, and in the process of mechanical plastering, spots and strips will be left on the surface of the lines, which will seriously affect the appearance quality of EPS lines.
Improper consistency and fluidity of the mortar will lead to poor smoothness during mechanical plastering, and the surface of the produced EPS lines will be rough
The particle size composition of the mortar is not well controlled, the particle size is too large, the mortar surface is not smooth and delicate; the particle size is too small, the mortar is easy to aggregate and difficult to disperse evenly, and the inner corner of the line is easy to crack
When the EPS line is stored and dried, the mortar is not dry and solidified, and there will be sagging and corner drop phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A special mortar for EPS line mechanical plastering, its components and parts by weight are: 300 parts of Lingyun brand 42.5 ordinary Portland cement, 400 parts of 100 mesh quartz sand, 100 parts of 120 mesh Shuangfei powder, 30 parts of ash calcium powder, Three-dimensional SW-05 redispersible latex powder 10 parts, Samsung pmc-15us hydroxypropyl methylcellulose ether 2 parts, wood fiber 3 parts, sodium tripolyphosphate dispersant 1 part, polyethylene glycol fat wetting agent 3 parts part, 0.3 part of sodium lauryl sulfate foam stabilizer. After the above raw materials are mixed, add water and stir evenly, and then use EPS line pusher for mechanical plastering, and the EPS lines with smooth and delicate surface, no falling corners, no sagging traces, and no cracks at the inner corners can be produced.

Embodiment 2

[0022] A special mortar for EPS line mechanical plastering, its components and parts by weight are: 325 parts of Lingyun brand 42.5 ordinary Portland cement, 450 parts of 120 mesh quartz sand, 150 parts of 150 mesh Shuangfei powder, 50 parts of ash calcium powder, 13 parts of Wacker 5044 redispersible latex powder, 3 parts of Hercules HK15M hydroxypropyl methylcellulose ether, 4 parts of wood fiber, 2 parts of sodium tetrapolyphosphate dispersant, 4 parts of polyethylene glycol fat wetting agent , 0.4 parts of sodium lauryl sulfate foam stabilizer. After the above raw materials are mixed, add water and stir evenly, and then use EPS line pusher for mechanical plastering, and the EPS lines with smooth and delicate surface, no falling corners, no sagging traces, and no cracks at the inner corners can be produced.

Embodiment 3

[0024] A special mortar for EPS line mechanical plastering, its components and parts by weight are: 350 parts of Leishan brand 42.5 ordinary Portland cement, 500 parts of 140 mesh quartz sand, 200 parts of 200 mesh Shuangfei powder, 60 parts of ash calcium powder, Wacker 5044 redispersible latex powder 15 parts, Samsung pmc-15us hydroxypropyl methylcellulose ether 4 parts, wood fiber 5 parts, sodium tetrapolyphosphate dispersant 3 parts, polyethylene glycol fat wetting agent 5 parts , 0.5 parts of sodium lauryl sulfate foam stabilizer. After the above raw materials are mixed, add water and stir evenly, and then use EPS line pusher for mechanical plastering, and the EPS lines with smooth and delicate surface, no falling corners, no sagging traces, and no cracks at the inner corners can be produced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an EPS line mechanical plastering dedicated mortar. The mortar is composed of the following components in parts by weight: 300 to 350 parts of cement, 400 to 500 parts of quartz sand, 100 to 200 parts of heavy calcium carbonate powder, 30 to 60 parts of ash calcium powder, 10 to 15 parts of redispersable latex powder, 2 to 4 parts of cellulose ether, 3 to 5 parts of wood fiber, 1 to 3 parts of dispersant, 3 to 5 parts of wetting agent, and 0.3 to 0.5 part of foam stabilizer. The EPS line mechanical plastering dedicated mortar has the advantages of good flexibility and good binding property, and above all, the mortar can well cooperate with an EPS line plastering machine. The EPS line produced by an EPS line plastering machine has the advantages of no pendant, no sagging, no cracking in the internal angle of lines, almost no bubble in the surface, and fine and smooth appearance.

Description

technical field [0001] The invention relates to a construction mortar, in particular to a special mortar for mechanical plastering with EPS lines. Background technique [0002] EPS line is a kind of facade decoration product used in ordinary houses, villas, hotels, and shopping malls. It can be decorated on the four sides of the window, the door, the hall wrapping pillars, the corner lines, etc., which can make the facade of the building more rich. Creative, more beautiful. EPS lines have many edges and corners. Only by using mechanical plastering method, that is, applying special mortar to each corner and surface of EPS lines at one time, can mass-produce EPS lines with low price and meet the exterior design of buildings. Generally, polymer mortar is applied to EPS lines, and there will be some difficulties in several links such as stirring, mechanical plastering, and EPS lines being stored and dried. Bubbles with uneven pore size appear in the mortar during the process o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B24/38C04B14/06
Inventor 张志峰周强詹克志
Owner 奥捷科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products