A method of modifying nano-carbon to improve soil matrix turfgrass regeneration

A technology for improving soil and nano-carbon, which is applied in the direction of soil lifting machinery, soil preparation methods, soil conditioning materials, etc., and can solve problems affecting the regeneration of lawn plants, etc.

Inactive Publication Date: 2016-01-13
TIANJIN NORMAL UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this case, it will greatly affect the regeneration of lawn plants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of modifying nano-carbon to improve soil matrix turfgrass regeneration
  • A method of modifying nano-carbon to improve soil matrix turfgrass regeneration

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A method for improving the regeneration of soil matrix turfgrass by modifying nano-carbon:

[0050] (1) Handling of materials:

[0051] The collected soil samples were passed through a 2mm sieve and mixed for later use; the soil properties were: pH 7.44, organic matter content 4.68, total nitrogen 0.21%, total phosphorus 22.03mg·kg -1 , saturated water content 0.58mL·g -1 , the soil sample was passed through a 2mm sieve and mixed for later use;

[0052] The plants are tall fescue ( Festuca arundinacea L . );

[0053] The nano-carbon particle size is 20nm, and the specific surface area is 1.2×10 5 m 2 kg -1 , with a pH value of 7, which were modified before application to obtain KMnO 4 、H 2 SO 4 or HNO 3 Modified nano carbon;

[0054] (2) Experimental method:

[0055] In the experiment, a plastic flowerpot with a height of 25cm and a diameter of 12cm was used. After washing and drying the gauze, it was cut into a round shape with a suitable size to fix the b...

Embodiment 2

[0057] A method for improving the regeneration of soil matrix turfgrass by modifying nano-carbon:

[0058] (1) Handling of materials:

[0059] The collected soil samples were passed through a 2mm sieve and mixed for later use; the soil properties were: pH 7.44, organic matter content 4.68, total nitrogen 0.21%, total phosphorus 22.03mg·kg -1 , saturated water content 0.58mL·g -1 , the soil sample was passed through a 2mm sieve and mixed for later use;

[0060] The plants are tall fescue ( Festuca arundinacea L . );

[0061] The particle size of nano carbon is 70nm, and the specific surface area is 1.2×10 5 m 2 kg -1 , with a pH value of 7, which were modified before application to obtain KMnO 4 、H 2 SO 4 or HNO 3 Modified nano carbon;

[0062] (2) Experimental method:

[0063] In the experiment, a plastic flowerpot with a height of 25cm and a diameter of 12cm was used. After washing and drying the gauze, it was cut into a round shape with a suitable size to fix th...

Embodiment 3

[0066] A method for improving the regeneration of soil matrix turfgrass by modifying nano-carbon:

[0067] (1) Handling of materials:

[0068] The collected soil samples were passed through a 2mm sieve and mixed for later use; the soil properties were: pH 7.44, organic matter content 4.68, total nitrogen 0.21%, total phosphorus 22.03mg·kg -1 , saturated water content 0.58mL·g -1 , the soil sample was passed through a 2mm sieve and mixed for later use;

[0069] The plants are tall fescue ( Festuca arundinacea L . );

[0070] The nano-carbon particle size is 50nm, and the specific surface area is 1.2×10 5 m 2 kg -1 , with a pH value of 7, which were modified before application to obtain KMnO 4 、H 2 SO 4 or HNO 3 Modified nano carbon;

[0071] (2) Experimental method:

[0072]In the experiment, a plastic flowerpot with a height of 25cm and a diameter of 12cm was used. After washing and drying the gauze, it was cut into a round shape with a suitable size to fix the bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving the reproducibility of soil matrix lawn grass through modified nanocarbon, wherein a plastic flower pot with the height of 25cm and the diameter of 12cm is adopted, a gauze is cleaned, dried and sheared into a proper-size round shape to fix the bottom of the flower pot, 2kg garden soil matrix is weighed in each container, the modified nanocarbon whose weight is 1-5% that of the garden soil matrix is added into the garden soil, 4.5g festuca arundinacea seeds are sown, water is fed timely and quantitatively every day during the experiment to meet the plant growth needs, the plant is cultured in a lab at the temperature of 25-34 DEG C and the relative humidity of 31%-48%, the light condition is natural incident light, the experiment is conducted for 120 days, the part of the festuca arundinacea on the ground is clipped on the sixtieth day of the experiment, 1cm crop is kept, the biomass of the first crop is measured, and the biomass of the second crop is measured at the end of the experiment. The experiment results show that 5% HNO3 modified nanocarbon can improve the reproducibility of the soil matrix festuca arundinacea.

Description

technical field [0001] The invention belongs to the technical field of environmental protection, and relates to urban afforestation, in particular to a method for improving the regeneration of soil matrix turfgrass by modifying nano-carbon. Background technique [0002] In the construction of lawn planting system, the method of laying turf is very common in cities at home and abroad. The turf is a lawn plant or lawn planting material that the lawn is flattened into a flat shape or stripped into squares, rectangles, columns and other shapes of different sizes, with a certain amount of soil attached thereto. At present, turf has become a hot-selling product in some countries, and the sales value of turf in the United States alone exceeds 10 billion US dollars per year. The prospect of turf production in our country is also broad, and the price per square meter in many cities is as high as 10 yuan. Although the application of turf establishment is very popular, its disadvanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A01B77/00A01B79/02C09K17/02
Inventor 赵树兰多立安贺璐
Owner TIANJIN NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com