Bainite structural steel used for high strength fastener

A bainite and structural steel technology, applied in the field of iron and steel metallurgy, can solve the problems of increasing production cost, reducing productivity, increasing energy consumption, etc., to achieve the effects of increasing productivity, reducing energy consumption and cost, and reducing pollution emissions

Inactive Publication Date: 2014-05-14
无锡市森信精密机械厂
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This quenched and tempered fastener production method, on the one hand, requires the addition of alloying elements to increase the production cost, and on the other hand, due to the need for subsequent heat treatment, it increases energy consumption and reduces productivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A bainitic structural steel for high-strength fasteners, the chemical composition of the bainitic structural steel consists of the following components in weight percentage: C: 0.04%, Mn: 1.80%, Si: 0.60%, S: ≤0.010%, P: ≤0.010%, Nb: 0.08%, V: 0.15%, Ti: 0.06%, N: 0.005%, B: 0.007%, Als: ≤0.035%, the balance is Fe and unavoidable impurities .

Embodiment 2

[0025] A bainitic structural steel for high-strength fasteners, the chemical composition of the bainitic structural steel consists of the following components in weight percentage: C: 0.08%, Mn: 1.20%, Si: 0.80%, S: ≤0.010%, P: ≤0.010%, Nb: 0.06%, V: 0.25%, Ti: 0.04%, N: 0.010%, B: 0.005%, Als: ≤0.035%, the balance is Fe and unavoidable impurities .

Embodiment 3

[0027] A bainitic structural steel for high-strength fasteners, the chemical composition of the bainitic structural steel consists of the following components in weight percentage: C: 0.05%, Mn: 1.60%, Si: 0.65%, S: ≤0.010%, P: ≤0.010%, Nb: 0.075%, V: 0.18%, Ti: 0.055%, N: 0.007%, B: 0.0065%, Als: ≤0.035%, the balance is Fe and unavoidable impurities .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bainite structural steel used for a high strength fastener. The bainite structural steel comprises the following chemical components by weight: 0.04%-0.08% of C, 1.20-1.80% of Mn, 0.60%-0.80% of Si, less than or equal to 0.010% of S, less than or equal to 0.010% of P, 0.06%-0.08% of Nb, 0.15%-0.25% of V, 0.04%-0.06% of Ti, 0.005%-0.010% of N, 0.005%-0.007% of B, less than or equal to 0.035% of Als, and the balance Fe and inevitable impurities.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to a bainitic structural steel for high-strength fasteners. Background technique [0002] Fasteners are one of the three basic mechanical components. Cold heading steel wire is the main raw material for making bolts, nuts, screws, rivets and other fasteners. For the production of high-strength fasteners, 40Cr, 35CrMo and other alloy structural steels can be used as materials, and quenched and tempered heat treatment is carried out after deep processing. Its production process: raw material inspection → spheroidizing annealing → pickling → phosphating treatment → primary drawing → annealing → pickling → phosphating treatment → secondary drawing → cold heading → wire rolling → quenching, tempering (quenching and tempering treatment ) → electroplating → product performance inspection. This quenched and tempered fastener production method, on the one hand, requires ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14
Inventor 华兆红
Owner 无锡市森信精密机械厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap