Frosted texture quartz sand plaster drawing board

A texture and frosting technology, applied in the field of art and painting equipment, can solve the problems of easy yellowing, cracking and deformation, lack of texture of gypsum material, hardness and three-dimensional effect, etc., to improve the three-dimensional effect, improve the hardness and improve the surface The effect of flatness

Active Publication Date: 2015-10-21
WUXI PHOENIX ARTIST MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The gypsum material is cheap and beautiful, and it is a very good coating material for drawing boards. However, gypsum drawing boards are prone to yellowing, cracking and deformation after long-term storage, and the gypsum material lacks texture, hardness and three-dimensional effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The preparation process of the frosted texture quartz sand gypsum drawing board in this embodiment is as follows:

[0019] (1) Add 250 parts of deionized water, 2 parts of defoamer, 20 parts of propylene glycol, and 5 parts of dispersant (product of Hantai Chemical, model NXZ) into the reaction kettle and stir evenly at a speed of 1800 rpm;

[0020] (2) Continue to add 100 parts of titanium dioxide, 250 parts of talc powder, 250 parts of 200-mesh quartz sand and disperse for 1 hour at a speed of 3000 rpm;

[0021] (3) Add 150 parts of pure acrylic emulsion and stir evenly at a speed of 3500 rpm, then add multifunctional additive AMP-95 to adjust the pH to 7.0, add 2 parts of defoamer and 10 parts of film-forming aid while stirring, increase Thickener (Shanghai Shicheng Chemical Co., Ltd. product, model TT935) 5 parts, continue to stir, the speed is 3000 rpm / min, to get the coating paint;

[0022] (4) Apply the prepared paint to the surface of the wooden picture frame b...

Embodiment 2

[0024] The preparation process of the frosted texture quartz sand gypsum drawing board in this embodiment is as follows:

[0025] (1) Add 240 parts of deionized water, 2.5 parts of defoamer, 18 parts of propylene glycol, and 6.5 parts of dispersant (product of Hantai Chemical, model NXZ) into the reactor and stir evenly at a speed of 1900 rpm;

[0026] (2) Continue to add 95 parts of titanium dioxide, 260 parts of talc powder, 240 parts of 200-mesh quartz sand and disperse for 1 hour at a speed of 3500 rpm;

[0027] (3) Add 160 parts of pure acrylic emulsion and stir evenly at a speed of 3000 rpm, then add multifunctional additive AMP-95 to adjust the pH to 7.0, add 1.8 parts of defoamer and 11.5 parts of film-forming aid while stirring, increase Thickener (Shanghai Shicheng Chemical Co., Ltd. product, model TT935) 4 parts, continue to stir, the speed is 3500 rpm / min, to get the coating paint;

[0028] (4) Use the flow coating process to apply the prepared paint to the surfac...

Embodiment 3

[0030] The preparation process of the frosted texture quartz sand gypsum drawing board in this embodiment is as follows:

[0031] (1) Add 260 parts of deionized water, 1.5 parts of defoamer, 23 parts of propylene glycol, and 3.5 parts of dispersant (product of Hantai Chemical, model NXZ) into the reactor and stir evenly at a speed of 2000 rpm;

[0032] (2) Continue to add 105 parts of titanium dioxide, 240 parts of talc powder, 245 parts of 200-mesh quartz sand and disperse for 1.5 hours at a speed of 3800 rpm;

[0033] (3) Add 140 parts of pure acrylic emulsion and stir evenly at a speed of 3200 rpm, then add multifunctional additive AMP-95 to adjust the pH to 7.0, add 2.5 parts of defoamer and 8.5 parts of film-forming aid while stirring, increase Thickener (Shanghai Shicheng Chemical Co., Ltd. product, model TT935) 6 parts, continue to stir, the speed is 3800 rpm / min, to get the coating;

[0034] (4) Use the flow coating process to apply the prepared coating on the surface...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a quartz sand gypsum palette with a grinding sand texture. A preparation method comprises the steps of adding 240 to 260 parts of deionized water, 1.5 to 2.5 parts of defoaming agent, 18 to 23 parts of propylene glycol and 3.5 to 6.5 parts of dispersing agent into a reaction kettle and stirring; continuously adding 95 to 105 parts of titanium dioxide powder, 240 to 260 parts of talcum powder and 240 to 250 parts of quartz sand of 200 meshes; dispersing for 1 to 1.5 hours; adding 140 to 160 parts of pure acrylic emulsion and evenly stirring; adding a multifunctional additive AMP-95 and regulating a pH value to 7.0; adding 1.8 to 2.5 parts of defoaming agent, 8.5 to 11.5 parts of film-forming aiding agent and 4 to 6 parts of thickening agent under a stirring condition; continuously stirring so as to obtain a coating paint; spraying the costing paint on a picture frame made of wood plates so as to obtain the quartz sand gypsum palette with a grinding sand texture. The quartz sand gypsum palette is excellent in water resistance and weather resistance; a coating layer has the grinding sand texture, and is good in firmness and flintiness, strong in stereoscopic impression and difficult to crack due to the fact that the coating paint is sprayed thickly. In addition, the coating layer can be polished to reach any thickness, and a good shower coating effect can be obtained if the coating paint is matched with a shower coating process.

Description

technical field [0001] The invention relates to an art painting utensil, in particular to a quartz sand hard gypsum drawing board with frosted texture. Background technique [0002] Gypsum material is cheap and beautiful, and it is a very good coating material for drawing boards. However, gypsum drawing boards are prone to yellowing, cracking and deformation after prolonged storage, and the gypsum material lacks texture, hardness and three-dimensional effect. Contents of the invention [0003] In view of the above-mentioned defects existing in the existing gypsum drawing board, the object of the present invention is to provide a kind of frosted texture quartz sand gypsum drawing board. The gypsum drawing board of the present invention has excellent water resistance and weather resistance, the coating has a frosted texture, good firmness and hardness, strong three-dimensional effect, thick coating is not easy to crack, and can be polished to any thickness, and the matching ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D7/12B05D7/24B05D5/02
Inventor 陈卫宏陈祎
Owner WUXI PHOENIX ARTIST MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com