Composite nanometer titanium dioxide for skin cream and preparation method thereof

A technology of nano-titanium dioxide and skin cream, applied in the field of skin care products, can solve the problems of not being easy to keep warm, poor skin repair function, etc., and achieve better effects, promote absorption, and obvious effects of use

Inactive Publication Date: 2013-12-18
句容亿格纳米材料厂
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional skin creams can whiten, resist aging, and lock in water. Skin creams contain oil to some extent. While moisturizing the skin, they also lock the nutrition and moisture tightly into the skin before the cream, but the repair function of the skin is poor. , when used in winter, it is not easy to keep warm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of composite nano-titanium dioxide used for skin cream, its components are composed of the following ingredients by weight percentage: 18 parts of nano-titanium dioxide, 8 parts of 400 mesh mulberry leaf extract powder, 12 parts of talcum powder, 18 parts of silicone powder, far 15 parts of infrared ceramic powder, 20 parts of iron oxide red, 15 parts of iron oxide yellow, 0.5 parts of colloidal silver, 0.5 parts of fragrance, 0.1 part of vanillyl butyl ether, 0.5 parts of borax, 2 parts of silicone oil, 7 parts of vaseline, propylene glycol 5 parts, 50 parts of deionized water.

[0021] The above-mentioned preparation method of composite nano-titanium dioxide for skin cream, said preparation method comprises the steps:

[0022] (1) Weighing the raw material components according to the weight parts of the components according to claim 1;

[0023] (2) Heat and mix nano-titanium dioxide, deionized water, silicone oil, propylene glycol, vaseline, and iron oxide eve...

Embodiment 2

[0027] A kind of composite nano-titanium dioxide used for skin care cream, its components are composed of the following components by weight percentage: 8 parts of nano-titanium dioxide, 12 parts of 600-mesh mulberry leaf extract powder, 5 parts of talcum powder, 25 parts of silicone powder, far 18 parts of infrared ceramic powder, 40 parts of iron oxide, 2 parts of colloidal silver, 1 part of spice, 0.5 part of vanillyl butyl ether, 0.8 part of borax, 4 parts of silicone oil, 9 parts of vaseline, 8 parts of propylene glycol, 60 parts of deionized water share.

[0028] The above-mentioned preparation method of composite nano-titanium dioxide for skin cream, said preparation method comprises the steps:

[0029] (1) Weighing the raw material components according to the weight parts of the components according to claim 1;

[0030] (2) Heat and mix nano-titanium dioxide, deionized water, silicone oil, propylene glycol, vaseline, and iron oxide evenly, and heat to 82~85°C;

[003...

Embodiment 3

[0034] A kind of composite nano-titanium dioxide used for skin cream, its component is made up of following composition by weight percentage: 15 parts of nano-titanium dioxide, 10 parts of 500 mesh mulberry leaf extract powder, 13 parts of talcum powder, 20 parts of silicone powder, far 16 parts of infrared ceramic powder, 38 parts of iron oxide yellow, 0.5 part of colloidal silver, 0.5 part of fragrance, 0.1 part of vanillyl butyl ether, 0.5 part of borax, 2 parts of silicone oil, 7 parts of vaseline, 5 parts of propylene glycol, deionized water 55 servings.

[0035] The above-mentioned preparation method of composite nano-titanium dioxide for skin cream, said preparation method comprises the steps:

[0036] (1) Weighing the raw material components according to the weight parts of the components according to claim 1;

[0037] (2) Heat and mix nano-titanium dioxide, deionized water, silicone oil, propylene glycol, vaseline, and iron oxide evenly, and heat to 82~85°C;

[0038...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses composite nanometer titanium dioxide for skin cream, which is composed of the following components in parts by weight: 8-18 parts of nanometer titanium dioxide, 8-12 parts of mulberry leaf extract powder, 12-15 parts of talcum powder, 18-25 parts of silicone powder, 15-18 parts of far infrared ceramic powder, 35-40 parts of ferric oxide, 0.5-2 parts of colloidal silver, 0.5-1 part of spice, 0.1-0.5 part of vanillyl butyl ether, 0.5-0.8 part of borax, 2-4 parts of silicone oil, 7-9 part of vaseline, 5-8 parts of propylene glycol and 50-60 parts of de-ionized water. Composite nanometer titanium dioxide contains colloidal silver and the mulberry leaf extract powder; colloidal silver is capable of achieving convergence and repair effects on the existing wounds and the mulberry leaf extract powder is capable of removing acnes and freckles so that the skin becomes fine and smooth; the colloidal silver ions are also capable of promoting the skin to absorb the mulberry leaf extract powder so that the effect of the mulberry leaf extract powder is better; the far infrared ceramic powder and vanillyl alcohol in composite nanometer titanium dioxide serve as heating sources, as long as infrared rays are present, a biological heat source can be generated, and the two heating sources are matched with each other to generate heat uninterruptedly; besides, the product obtained by a preparation method provided by the invention is free of toxic and side effects, free of irritation, safe and reliable, and obvious in using effect.

Description

technical field [0001] The invention relates to a skin care product, in particular to a composite nano-titanium dioxide used in skin care cream and a preparation method thereof. Background technique [0002] Traditional skin creams can whiten, resist aging, and lock in water. Skin creams contain oil to some extent. While moisturizing the skin, they also lock the nutrition and moisture tightly into the skin before the cream, but the repair function of the skin is poor. , when used in winter, it is not easy to keep warm. Contents of the invention [0003] Purpose of the invention: In order to overcome the deficiencies in the prior art, the present invention provides a composite nano-titanium dioxide used in skin care cream. [0004] The present invention also provides a preparation method of the above skin cream. [0005] Technical solution: In order to achieve the above object, the present invention provides a composite nano-titanium dioxide used in skin care cream, its c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/97A61K8/33A61K8/29A61K8/19A61Q19/00
Inventor 潘峥嵘
Owner 句容亿格纳米材料厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com