Abrasion-resisting priming paint

A technology of wear-resistant primer and weight percentage, applied in the field of wear-resistant primer, can solve the problems of paint pollution, general wear resistance, difficult cleaning and rewashing, etc., and achieve the effect of strong wear resistance, easy cleaning and rewashing

Inactive Publication Date: 2013-12-04
南通优尼科化工有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing traditional home decoration chemical building materials are usually based on paint and latex paint, but the paint pollutes the air and affects the quality of the environment. At the same time, these products have general wear resistance and are difficult to clean and wash.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of wear-resistant primer, described wear-resistant primer is made up of following components (by weight percentage):

[0010] Titanium dioxide 10%, soybean oil lecithin 0.1%, carbon fiber 0.6%, drier 0.4%,

[0011] Anti-skinning agent 4%.

Embodiment 2

[0013] A kind of wear-resistant primer, described wear-resistant primer is made up of following components (by weight percentage):

[0014] Titanium dioxide 25%, soybean oil lecithin 0.3%, carbon fiber 0.8%, drier 0.8%,

[0015] Anti-skinning agent 6%.

Embodiment 3

[0017] A kind of wear-resistant primer, described wear-resistant primer is made up of following components (by weight percentage):

[0018] Titanium dioxide 17.5%, soybean oil lecithin 0.2%, carbon fiber 0.7%, drier 0.6%,

[0019] Anti-skinning agent 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses abrasion-resisting priming paint. The abrasion-resisting priming paint is composed of, by weight percentage, 10-25% of titanium dioxide, 0.1-0.3% of soybean-oil phosphatidyl choline, 0.6-0.8% of carbon fibers, 0.4-0.8% of dryer and 4-6% of anti-skinning agents. The abrasion-resisting priming paint will not pollute air, guarantees that environment quality will not be damaged, and meanwhile is strong in abrasion resistance and easy to clean and wash.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a wear-resistant primer. Background technique [0002] Existing traditional home decoration chemical building materials are usually based on paint and latex paint, but paint pollutes the air and affects environmental quality. At the same time, these products have general wear resistance and are difficult to clean and rewash. Contents of the invention [0003] The purpose of the invention: to solve the above problems, a kind of wear-resistant primer is provided. [0004] Technical solution: A wear-resistant primer according to the present invention, the wear-resistant primer is composed of the following components (by weight percentage): [0005] Titanium dioxide 10-25%, soybean oil lecithin 0.1-0.3%, carbon fiber 0.6-0.8%, drier 0.4-0.8%, [0006] Anti-skinning agent 4-6%. [0007] Beneficial effects: the wear-resistant primer of the invention does not pollute the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12C09D5/00
Inventor 葛坤祥
Owner 南通优尼科化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com