Tunnel fire prevention pigment

A technology of fire-resistant pigments and tunnels, applied in the field of fire-resistant pigments, can solve the problems of low fire-resistant limit and easy fire, and achieve the effect of low cost and good water resistance

Active Publication Date: 2013-11-20
WUJIANG HUACHENG COMPOSITE MATERIAL SCI & TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the fire resistance limit of tunnel building materials is low, which is prone to fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A tunnel fire-resistant pigment of this embodiment has the following components by weight:

[0042] Expanded vermiculite: 13 parts;

[0043] Hydroxymethyl cellulose: 18 parts;

[0044] Styrene acrylic emulsion: 40 parts;

[0045] Hydrochloric acid: 15 parts;

[0046] Zinc acetate: 7 parts;

[0047] Calcium acetate: 12 parts;

[0048] Nano titanium dioxide: 5 parts;

[0049] 16 parts of hexamethylcellulose;

[0050] Low alkalinity sulphoaluminate cement: 35 parts;

[0051] Aluminum hydroxide: 7 parts.

Embodiment 2

[0053] A tunnel fire-resistant pigment of this embodiment has the following components by weight:

[0054] Expanded vermiculite: 10 parts;

[0055] Hydroxymethyl cellulose: 15 parts;

[0056] Styrene acrylic emulsion: 30 parts;

[0057] Hydrochloric acid: 12 parts;

[0058] Zinc acetate: 3 parts;

[0059] Calcium acetate: 6 parts;

[0060] Nano titanium dioxide: 2 parts;

[0061] Hexamethylcellulose: 11 parts;

[0062] Fast hardening sulphoaluminate cement: 25 parts;

[0063] Magnesium hydroxide: 4 parts.

Embodiment 3

[0065] A tunnel fire-resistant pigment of this embodiment has the following components by weight:

[0066] Expanded vermiculite: 12 parts;

[0067] Hydroxymethyl cellulose: 16 parts;

[0068] Styrene acrylic emulsion: 35 parts;

[0069] Hydrochloric acid: 14 parts;

[0070] Zinc acetate: 5 parts;

[0071] Calcium acetate: 9 parts;

[0072] Nano titanium dioxide: 3 parts;

[0073] Hexamethylcellulose: 15 parts;

[0074] Composite sulphoaluminate cement: 30 parts;

[0075] Calcium formate: 6 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a tunnel fire prevention pigment which comprises the following ingredients in parts by weight: 10-13 parts of expanded vermiculite, 15-18 parts of hydroxymethyl cellulose, 30-40 parts of styrene-acrylic emulsion, 12-15 parts of hydrochloric acid, 3-7 parts of zinc acetate, 6-12 parts of lime acetate, 2-5 parts of nano titanium dioxide, 11-16 parts of hexamethyl cellulose, 25-35 parts of sulphate aluminium cement and 4-7 parts of auxiliary agent. The tunnel fire prevention pigment is nontoxic and smoke-free, meets an environmental requirement, has the characteristics of good water resistance and low cost, and overcomes the defect that the existing tunnel fire prevention pigment is low in fire endurance.

Description

technical field [0001] The invention relates to a fireproof pigment, in particular to a tunnel fireproof coating. Background technique [0002] With the rapid development of my country's road traffic construction, highways, railways, subways and urban cross-street tunnels have developed rapidly. In addition, tunnels are also important channels for optical cables, oil transportation and water supply. Therefore, once a fire occurs in the tunnel, it will often cause heavy losses. Therefore, it is imperative to strengthen tunnel fire protection, and doing a good job in tunnel fire protection has obvious social and economic significance for traffic safety. At present, the building materials of tunnels have low fire resistance limit and are prone to fire. Contents of the invention [0003] The object of the present invention is to provide a kind of pigment, more specifically a kind of tunnel fire-proof pigment with high fire-resistance limit and not prone to fire. [0004] In o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/28
Inventor 李小福
Owner WUJIANG HUACHENG COMPOSITE MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com