A kind of graphene radiation heating film and its preparation method and application

A graphene and heating film technology, applied in graphene radiation heating film and its preparation and application fields, can solve the problems of non-folding or cutting, fast material decay speed, high power of heating material, etc. Utilization rate, the effect of improving thermal insulation

Active Publication Date: 2015-12-02
南京天脉健康科技发展有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a new heating film for the problems of low electrothermal conversion rate, high power of heating material, fast material attenuation speed, short life, low safety performance, high hardness, and cannot be folded or cut. Graphene radiation heating film and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene radiation heating film and its preparation method and application
  • A kind of graphene radiation heating film and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Outsourcing:

[0017] Graphene powder, specifications: powder, particle size: 30-60nm.

[0018] Infrared emitter, specification: powder.

[0019] High temperature resistant phenolic resin, specification: liquid.

[0020] Weigh 4 parts of graphene powder, 2 parts of far-infrared emitter, and 5 parts of high-temperature-resistant phenolic resin, mix the graphene powder and far-infrared emitter and stir evenly, then add bonding diluent and mix to form a slurry.

Embodiment 2

[0022] Apply the slurry described in Example 1 evenly to the film formed on one surface of the fiber fabric, and dry (or dry) to form a graphene radiation heating film.

[0023] The fiber fabric containing the graphene radiation heating film and the same fiber fabric without the graphene radiation heating film were simultaneously carried out under the condition of simulated body temperature (37°C) to compare the heat preservation and radiation effects of the heat source, as shown in Table 1:

[0024] Table 1:

[0025]

[0026] The results prove that the graphene radiative heating film can radiate heat and is used to make bed sheets, quilt covers or underwear. Under the action of a heat source, it can radiate infrared wavelengths of 8-14um, and has a good heat preservation effect.

Embodiment 3

[0028] The fiber fabric containing the graphene radiation heating film obtained in Example 2, in the absence of a heat source, is only stimulated by the external environment temperature to generate heat, which emits little heat and also has a small amount of infrared wavelength radiation of 8-14um.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a graphene radiation heating film and the preparation method and application thereof. The graphene radiation heating film is formed by coating graphene sizing agent on a surface of fiber fabric; the graphene sizing agent is formed by mixing the following components in part by weight: 3 to 5 parts of graphene powder, 1 to 3 parts of far-infrared cast charge and 4 to 6 parts of bonding diluent; the preparation method comprises the following steps: weighting graphene powder of 3 to 5 parts by weight, far-infrared cast charge of 1 to 3 parts by weight and bonding diluent of 4 to 6 parts by weight, after mixing the graphene powder with far-infrared cast charge, stirring the mixture uniformly firstly, then adding bonding diluent and mixing, so as to form sizing agent; coating the sizing agent on the surface of the fiber fabric to form a film, and after the film is dried in the air or dried by baking, the graphene radiation heating film is formed. During use, the graphene radiation heating film emits heating by radiation under the effect of external temperature.

Description

technical field [0001] The invention relates to a graphene radiation heating film and a preparation method and application thereof. Background technique [0002] Graphene (Graphene) has been reported by Professor Geim of the University of Manchester in 2004, and has attracted widespread attention and great interest of scientists due to its peculiar properties. It is predicted that it is likely to cause revolutionary changes in many fields. Single-layer graphene exists in a two-dimensional crystal structure with a thickness of only 01334nm. It is the basic unit for constructing carbonaceous materials of other dimensions. It can be wrapped up to form zero-dimensional fullerenes, rolled up to form one-dimensional carbon nanotubes and stacked layer by layer to form three-dimensional ones. graphite. Graphene is a semiconductor without an energy gap. It has a carrier mobility 100 times higher than that of silicon (2×10cm / v). It has a micron-scale free path and a large coherence l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H05B3/36B29C41/00
Inventor 王尤山田芝亮
Owner 南京天脉健康科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com