A technology of binders and additives, which is applied in the field of offset printing, can solve the problems of low resin solvent consumption, large resin solvent consumption, and high process cost, and achieve the effects of enhancing compatibility, improving water resistance and leveling

Inactive Publication Date: 2013-07-10
ZHEJIANG KEXIN INK
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For this reason, the first technical problem to be solved by the present invention is the problem that the viscosity of the connecting material is low and the amount of resin solvent used in the prior art is low, and a kind of connecting material with high viscosity and low amount of resin solvent is provided; The second technical problem is that the preparation process steps of the connecting material in the prior art are complicated and the problem of high process cost is to provide a preparation method with a simple preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The connecting material described in the present embodiment, its component is:

[0035] 44 kilograms of rosin modified octylphenol phenolic resins;

[0036] 24 kg of linseed oil;

[0037] 30 kg of mineral oil;

[0038] Resin oil 1.1 kg;

[0039] Myristyl alcohol 0.2 kg;

[0040] Anti-skinning agent 0.4 kg;

[0041] Liquid gel 0.2 kg;

[0042] BHT0.1 kg.

[0043] The preparation method of described connecting material is:

[0044] S1, weigh the modified tert-butylphenol novolac resin, the linseed oil, the mineral oil, the resin oil, the myristyl alcohol, the anti-skinning agent successively by the selected parts by weight of the rosin , the liquid gel and the BHT, wherein 5wt% of the mineral oil is reserved and placed in the reactor with the rest of the components, and stirred evenly;

[0045] S2. Under the condition of stirring, heat the mixture prepared in S1 to 230°C within 100 minutes and then keep it warm for 1 hour;

[0046]S3. Add the mineral oil reserved...

Embodiment 2

[0048] The connecting material described in the present embodiment, its component is:

[0049] 40 kilograms of rosin modified octylphenol phenolic resins;

[0050] 30 kg of linseed oil;

[0051] Mineral oil 28 kg;

[0052] Resin oil 1.8 kg;

[0053] Myristyl alcohol 0.1 kg;

[0054] Anti-skinning agent 0.1 kg.

[0055] The preparation method of described connecting material is:

[0056] S1, weigh the modified tert-butylphenol novolac resin, the linseed oil, the mineral oil, the resin oil, the myristyl alcohol, the anti-skinning agent successively by the selected parts by weight of the rosin , where the mineral oil is reserved for 10wt% and placed in the reactor with the rest of the components, and stirred evenly;

[0057] S2. Under the condition of stirring, heat the mixture prepared in S1 to 225°C within 100 minutes and then keep it warm for 1 hour;

[0058] S3. Add the mineral oil reserved in step S1 to the mixture prepared in step S2 to adjust the viscosity, the adju...

Embodiment 3

[0060] The connecting material described in the present embodiment, its component is:

[0061] 50 kilograms of rosin modified octylphenol phenolic resins;

[0062] 20 kg of linseed oil;

[0063] Mineral oil 27 kg;

[0064] Resin oil 1.7 kg;

[0065] Myristyl alcohol 0.3 kg;

[0066] Anti-skinning agent 0.2 kg;

[0067] Liquid gel 0.7 kg;

[0068] BHT0.1 kg.

[0069] The preparation method of described connecting material is:

[0070] S1, weigh the modified tert-butylphenol novolac resin, the linseed oil, the mineral oil, the resin oil, the myristyl alcohol, the anti-skinning agent successively by the selected parts by weight of the rosin , the liquid gel and the BHT, wherein 15wt% of the mineral oil is reserved and placed in the reactor with the rest of the components, and stirred evenly;

[0071] S2. Under the condition of stirring, heat the mixture prepared in S1 to 235° C. within 100 minutes and then keep it warm for 1 hour;

[0072] S3. Add the mineral oil reserve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a binder and a preparation method thereof and belongs to the offset printing field. The binder comprises 40-50 parts of rosin modified octylphenol phenolic resin, 20-30 parts of linseed oil, 25-35 parts of mineral oil, 1-2 parts of resin oil, 0.1-0.3 part of tetradecyl alcohol and 0.1-1 part of auxiliaries. As the binder is added with the resin oil component, the mineral oil compatibility, the pigment wettability, the water resistance and the leveling property of the binder can be enhanced; besides, the rosin modified octylphenol phenolic resin is in partial addition reaction with the linseed oil at the temperature of 220-240 DEG C, so that the molecular crosslinking degree in the rosin modified octylphenol phenolic resin is increased; as a result, the viscosity of the binder can be improved. The viscosity of the binder provided by the invention is capable of reaching 40000-47000 mPa.S / 25 DEG C.

Description

technical field [0001] The invention relates to an ink binder and a preparation method thereof, belonging to the field of offset printing. Background technique [0002] With the prosperity of the packaging and printing market, high-grade offset printing inks have developed rapidly. [0003] Binder is a liquid substance made by miscible polymer substances, also known as varnish, vehicle or vehicle. It is the main component of ink and the carrier for dispersing pigments and fillers. The material can be transferred to the surface of the substrate through the printing machine to play the role of adjusting the gloss, abrasion resistance, rheology, viscosity and transfer performance of the ink; therefore, different types of binders can be prepared For inks, the properties of the binder often determine the performance of the ink. [0004] In the prior art, the binder is usually composed of resin, vegetable oil, mineral oil, organic solvent and other additives. For example, Chines...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/06C09D11/103
Inventor 黄时舫
Owner ZHEJIANG KEXIN INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap