Blending silky single jersey cloth of polyester fiber and modal fiber and preparation method thereof

A technology of modal fiber and polyester fiber, which is applied in the field of textile industry, can solve the problems of stuffy heat and airtightness, high cost of garments, poor comfort, etc., and achieve the effect of good drape, bright color and crisp fabric

Active Publication Date: 2014-12-17
GAOMI FUYUAN PRINTING & DYEING
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a polyester fiber and modal fiber blended mercerized single jersey fabric and a preparation method thereof, which can make the fabric have a silk feel and Coolmax fiber moisture absorption and sweat-wicking effect, and solve the problem of making T-shirts and sportswear from ordinary polyester fabrics. Poor moisture permeability, hot and airtight feeling, poor comfort and other problems, and the cost of garments made of single Modal fiber is relatively high, and the stretching feeling is relatively poor, so it is not suitable for high-end outerwear fabrics such as T-shirts and sportswear in summer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blending silky single jersey cloth of polyester fiber and modal fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] Such as figure 1 Shown: a kind of preparation method of common polyester fiber and modal fiber blended mercerized jersey fabric, comprises the following steps:

[0039] (1) Spinning: According to the weight percentage, 55-75% of polyester fiber and 25-45% of modal fiber are blended into yarn;

[0040] (2) Weaving: use a knitting machine to weave the yarn obtained in step (1) into a single-sided jersey, the weight of the single-sided jersey is 140 grams, and the length of the weaving line: 24.3CM / 100G;

[0041] (3) Blank inspection: Check whether there is oil and holes on the single-sided cloth surface. If there is too much oil, remove the oil first and then mercerize. Check out the holes and sew them up to prevent cloth scraping during the mercerizing process;

[0042] (4) Original body mercerizing: perform mercerizing treatment on single jersey, the conditions of the mercerizing treatment are: caustic soda concentration 220-240g / l, mercerizing penetrant 2-3g / l, lye te...

Embodiment 1

[0046] A kind of preparation method of common polyester fiber and modal fiber blended mercerized jersey fabric, comprises the following steps:

[0047] (1) Spinning: According to the weight percentage, 55% of polyester fiber and 45% of modal fiber are blended into yarn, and the specification of the obtained yarn is: 25S;

[0048] (2) Weaving: use a knitting machine to weave the yarn obtained in step (1) into a single-sided jersey, the weight of the single-sided jersey is 140 grams, and the length of the weaving line: 24.3CM / 100G;

[0049] (3) Blank inspection: Check whether there is oil and holes on the single-sided cloth surface. If there is too much oil, remove the oil first and then mercerize. Check out the holes and sew them up to prevent cloth scraping during the mercerizing process;

[0050] (4) Original body mercerizing: Use a cylinder mercerizing machine to perform mercerizing treatment on single-sided jersey. The conditions for the mercerizing treatment are: caustic s...

Embodiment 2

[0065] A kind of preparation method of common polyester fiber and modal fiber blended mercerized jersey fabric, comprises the following steps:

[0066] (1) Spinning: According to the weight percentage, 65% of polyester fiber and 35% of modal fiber are blended into yarn, and the specification of the obtained yarn is: 30S;

[0067] (2) Weaving: use a knitting machine to weave the yarn obtained in step (1) into a single-sided jersey, the weight of the single-sided jersey is 140 grams, and the length of the weaving line: 24.3CM / 100G;

[0068] (3) Blank inspection: Check whether there is oil and holes on the single-sided cloth surface. If there is too much oil, remove the oil first and then mercerize. Check out the holes and sew them up to prevent cloth scraping during the mercerizing process;

[0069] (4) Original body mercerizing: Use a cylinder mercerizing machine to perform mercerizing treatment on single-sided jersey. The conditions for the mercerizing treatment are: caustic s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to blending silky single jersey cloth of polyester fiber and modal fiber and a preparation method thereof. The polyester fiber and the modal fiber serve as raw materials and the single jersey cloth is prepared. According to weight percentages, the raw materials comprise 55% to 75% of the polyester fiber and 25% to 45% of the modal fiber. The cloth is glossy like silky cloth, bright in color, anti-fade after being washed for a plurality of times and good in wet permeability. The knitted cloth blended with the modal fiber has good wet permeable effect and is widely used for sewing top grade T-shirts and sportswear, sweat generated when a person does exercise can be discharged to surfaces of clothes rapidly and be evaporated, the skin stays fresh and cool and the exercise can be done comfortably. The size of the cloth is stable, hanging down feeling is good, the cloth is stiff and smooth, anti-wrinkle performance is good and teasing, pilling and wrinkling do not occur.

Description

technical field [0001] The invention relates to a polyester fiber and modal fiber blended mercerized jersey fabric and a preparation method thereof, belonging to the field of textile industry. Background technique [0002] With the gradual improvement of people's living standards, the requirements for clothing comfort, functionality and aesthetics are getting higher and higher. Ordinary polyester fabrics made of T-shirts and sportswear have disadvantages such as poor moisture conductivity, feeling stuffy and airtight, and poor comfort. Modal (Modal) is a cellulose regenerated fiber of high wet modulus viscose fiber developed by Lenzing Company of Austria. The process is processed into fibers. The raw materials of this product are all natural materials, which are harmless to the human body, can be decomposed naturally, and are harmless to the environment. The raw material of Modal fiber is produced in European shrubs. It is made of wood pulp and then processed through a sp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/14D04B1/16D06B7/08D06B3/18D06M11/38D06M15/643D06M13/207D06P3/872D06M101/32D06M101/06
Inventor 傅深环吉海东曹明利李玉仁张步强
Owner GAOMI FUYUAN PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com