Compressive strength test method for surface strengthening layer and substrate of axial part

A technology of surface strengthening layer and shaft parts, which is applied in the field of compressive strength testing of the surface strengthening layer and matrix of shaft parts, to achieve the effect of strong operability, reliable and accurate data

Active Publication Date: 2013-04-17
TIANJIN ENG MACHINERY INST
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in order to ensure the normal use of the parts and the safe operation of the machine, the compressive strength of the carburized shaft must be measured, but so far, there is no published data

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compressive strength test method for surface strengthening layer and substrate of axial part
  • Compressive strength test method for surface strengthening layer and substrate of axial part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to further understand the content of the invention, features and effects of the present invention, the following embodiments are exemplified and described in detail with the accompanying drawings as follows:

[0026] The structural shape of a workpiece that has been ground to a flat side such as figure 1 figure 2 shown.

[0027] A method for testing the compressive strength of a surface strengthening layer and a matrix of a shaft part, comprising the following steps:

[0028] a. Carburizing heat treatment steps: The gas carburizing method is used for the machined workpiece, the heating temperature is 900-930 °C, the holding time is 4-7 h, the carburizing test block is cooled to 760-850 °C and directly quenched, and then quenched at 160 °C. Temper at ~200℃ for 2~3h.

[0029] b. The finishing step of the surface of the shaft part, the finishing step is to grind the outer circle of the part on the cylindrical grinding machine, and the surface roughness of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a compressive strength test method for the surface strengthening layer and the substrate of an axial part. The method comprises the following steps: loading workpieces step by step to determine the pressure range for realizing damage on the workpieces, and then adopting a bisection approach method to precisely determine the pressure value for realizing damage. The method is simple, convenient and intuitive and has the advantages of strong operability reliable and accurate data and the like.

Description

technical field [0001] The invention belongs to the technical field of mechanical property detection technology of metal materials, in particular to a method for testing the compressive strength of a surface strengthening layer and a matrix of a shaft part. Background technique [0002] In practical applications, shaft parts are often required to have comprehensive properties such as high strength, toughness, surface hardness and wear resistance. Carburizing is a chemical heat treatment process that is often used. After carburizing, the parts are quenched and tempered at low temperature, which can improve the surface and core structure, and obtain a surface layer with high hardness and high strength, a subsurface layer and a core with certain toughness. Hard inner toughness, combining high strength and certain toughness on the same part. [0003] Under certain conditions of use, the compressive strength of the carburized shaft is an important factor in determining the servi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N3/08G01N1/44G01N1/28
Inventor 刘俊英蒋伯平张慧星胡晓丽张国胜
Owner TIANJIN ENG MACHINERY INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap