Composite fiber and preparation method thereof

A composite fiber and cellulose technology, which is applied in fiber treatment, spinning solution preparation, cellulose/protein conjugated artificial filament, etc., can solve the problems of kapok fiber spinning difficulty, and achieve the solution of spinning difficulty and production cost Low, easy to produce effects

Active Publication Date: 2014-09-03
GUANGDONG JUNAN JEANS RES INST +1
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the various deficiencies in the above-mentioned prior art, and provide a composite fiber of kapok fiber powder and cellulose with low production cost and excellent performance; solve the problem of kapok fiber spinning difficulty, and keep kapok The fiber is hollow to keep warm, natural antibacterial and other advantages, and the kapok fiber is effectively used to expand its application field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The average particle size of the cleaned kapok fiber powder is 68.5 μm, soaked in 35% sodium hydroxide aqueous solution at a ratio of 1:2.5,

[0039] Mix the kapok fiber powder thoroughly and disperse in an ultrasonic oscillator for 4.5 hours at a temperature of 26°C. A kapok fiber powder solution is obtained.

[0040] In addition, the cellulose bamboo pulp with a polymerization degree of 550 is prepared by conventional cellulose viscose preparation processes such as alkali staining, pressing, crushing, aging, yellowing, dissolving, mixing, filtering, aging and degassing to obtain cellulose viscose spinning Stock solution, control the composition of this viscose spinning stock solution to be α cellulose 8.8%, contain alkali 4.5%.

[0041] Then get the kapok fiber powder solution and the cellulose spinning stock solution according to the production needs, mix and pass through no less than 10 minutes in a static mixer. 5 Mix for the first time to mix evenly. After pre-f...

Embodiment 2

[0043] Take the cleaned kapok fiber powder with an average particle size of 72.8 μm, soak it in 30% sodium hydroxide aqueous solution at a ratio of 1:3, fully mix the kapok fiber powder, and disperse it in an ultrasonic oscillator for 5 hours. is 25°C. A kapok fiber powder solution is obtained.

[0044] In addition, the cellulose hemp pulp with a degree of polymerization of 580 and the cellulose bamboo pulp with a degree of polymerization of 750 are processed by alkali staining, pressing, crushing, aging, yellowing, dissolving, mixing, filtering, aging and degassing. The cellulose viscose spinning stock solution is obtained in the viscose preparation process, and the composition of the viscose spinning stock solution is controlled to be 8.8% of α-cellulose and 4.5% of alkali.

[0045] Then get the kapok fiber powder solution and the cellulose spinning stock solution according to the production needs, mix and pass through no less than 10 minutes in a static mixer. 5 Mix for t...

Embodiment 3

[0047] Take the cleaned kapok fiber powder with an average particle size of 72.8 μm, soak it in 30% sodium hydroxide aqueous solution at a ratio of 1:3, fully mix the kapok fiber powder, and disperse it in an ultrasonic oscillator for 5 hours. is 25°C. A kapok fiber powder solution is obtained.

[0048] In addition, the cellulose bamboo pulp with a degree of polymerization of 780 and the cellulose straw pulp with a degree of polymerization of 450 are subjected to alkali staining, pressing, crushing, aging, yellowing, dissolving, mixing, filtering, ripening and degassing. The cellulose viscose spinning stock solution is obtained in the plain viscose preparation process, and the composition of the viscose spinning stock solution is controlled to be 8.8% of α-cellulose and 4.5% of alkali.

[0049] Then get the kapok fiber powder solution and the cellulose spinning stock solution according to the production needs, mix and pass through no less than 10 minutes in a static mixer. 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite fiber of kapok fiber powder and cellulose and a preparation method thereof, in particular to a preparation method of kapok fiber powder modified cellulose composite fiber; the method provided by the invention comprises cleaning the kapok fiber powder , the cleaned kapok fiber powder, cellulose polymer, various additives, and solvents are prepared into a spinning solution, and the kapok fiber powder and cellulose composite fiber are obtained by wet spinning through coagulation bath spinning. The invention prepares the kapok fiber powder and cellulose composite fiber with low production cost and excellent performance by adding different contents of kapok fiber powder to spinning solution and changing process conditions. The preparation method of kapok fiber powder and cellulose composite fiber of the present invention will solve the problem of difficult spinning of kapok fiber, maintain the advantages of hollow kapok fiber to keep warm, natural antibacterial, etc., and effectively use kapok fiber to expand its application field of clothing.

Description

technical field [0001] The invention relates to a functional fiber material, in particular to a composite fiber of kapok fiber powder and cellulose, and a preparation method of the composite fiber. Background technique [0002] As the earliest man-made fiber, cellulose fiber has a history of more than 100 years, and the current output of cellulose fiber has reached more than 2.6 million tons. Cellulose fibers produced by nature have attracted much attention. However, because the traditional cotton and hemp natural cellulose fibers have certain limitations in the development scale, such as the problem of cotton "competing for land with grain", people are focusing more and more on new natural and regenerated cellulose fibers. development and utilization. [0003] Kapok fiber is a kind of fruit fiber of the woody plant kapok tree, which is attached to the inner wall of the kapok capsule shell and developed and grown from the inner wall cells. The adhesion force between the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01D5/30D01D5/06D01D10/06D01D1/02
Inventor 陈玉波田磊易长海余刚
Owner GUANGDONG JUNAN JEANS RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com