Method for processing ultra-thin cast porcelain laminate veneer capable of preventing tooth grinding
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A processing method and porcelain veneer technology, applied in dentures and other directions, can solve problems such as protruding deformity, changing tooth protrusion, and large tooth damage.
Active Publication Date: 2014-12-03
深圳市金悠然科技有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The existing porcelain veneer technology requires a thickness of more than 0.7 mm due to manual operation of the wax pattern, strength of the material, manufacturing process, and technology, which will significantly change the protrusion of the teeth and cause protrusion deformity
Therefore, it is necessary to grind the teeth to eliminate this effect, so the damage to the teeth is great.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] A method for processing an ultra-thin cast porcelain veneer without grinding teeth, the steps are as follows:
[0015] Specifically: use a 3D scanner to scan the dental model to form a 3D stereoscopic image, design an ultra-thin veneer below 0.5mm on the virtual image, and output the data to the 3D resin wax molding machine after completion, and spray the resin wax with light to cure the printed one. Then, the formed resin wax pattern is embedded and casted, adjusted and tried on, and glazed.
Embodiment 2
[0017] A method for processing an ultra-thin cast porcelain veneer without grinding teeth, the steps are as follows:
[0018] For the following situations:
[0019] Whitening of yellow teeth, tetracycline teeth, fluorosis teeth, closing gaps between teeth, missing teeth, and undersized teeth.
[0020] step:
[0021] Doctor color comparison and mold taking model repair Scanning (3shape scanner in Denmark)
[0022] Design (SensAble Sculpting Pen, USA) Processing (3D system wax printer in the United States) embedding Casting (Ivoclar Porcelain Casting Furnace EP3000 from Switzerland) polished glazed
[0023] Parameters involved:
[0024] 1. Design: The design thickness is generally judged according to the protrusion and face shape of the patient's teeth. Those with sunken faces can have a thickness of 0.5 mm; those with protruding teeth and normal faces can have a thickness of 0.2-0.3 mm.
[0025] 2. Embedding: When embedding, pay attention to the angl...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the field of dental prosthesis, in particular to a method for processing ultra-thin cast porcelain laminate veneer capable of preventing tooth grinding. The method comprises the following steps: a three-dimensional scanner is adopted to scan a dental cast, a three-dimensional stereoscopic image is formed, an ultra-thin veneer with the thickness of less than 0.5 mm is designed on the virtual image, after the ultra-thin veneer is designed, data is output to a 3D (three-dimensional) resin wax forming machine, the ultra-thin veneer is formed in the manners of resin-spraying, irradiation curing and printing, and then the formed resin wax pattern is subjected to embedded casting, grinding adjustment, try-in and glazing. Compared with the prior art, the method adopts a computer to design, and the conventional hand-made wax pattern is replaced by the resin wax pattern processed by the digital resin wax spraying, irradiation curing and printing processing, so that fabrication of porcelain laminate veneer with the thickness of less than 0.5 mm is realized. An aesthetic seeking patient with discolored teeth does not need tooth grinding and can receive tooth-whitening treatment without hurting teeth.
Description
technical field [0001] The invention relates to the field of dentures, in particular to a processing method for an ultra-thin cast porcelain veneer without grinding teeth. Background technique [0002] The existing porcelain veneer technology needs to have a thickness of more than 0.7 mm due to the manual operation of the wax pattern, the strength of the material, and the manufacturing process and technology. This will obviously change the protrusion of the teeth and cause protrusion deformity. Therefore, it is necessary to grind the teeth to eliminate this effect, so the damage to the teeth is large. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the invention provides a method for processing an ultra-thin cast porcelain veneer without grinding teeth. The thickness of the cast porcelain veneer obtained by the method of the present invention is less than 0.5 mm, and the thickness can be as thin as 0.2 mm. After the porcelain ven...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.