Polyphenyl ether/ABS (Acrylonitrile Butadiene Styrene) alloy and preparation method thereof

A polyphenylene ether and alloy technology, which is applied in the field of polyphenylene ether/ABS alloy and its preparation, achieves the effects of low manufacturing cost, broad application prospect and excellent processing performance

Active Publication Date: 2012-10-10
上海日之升科技有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there is no report about this type of PPE material and preparation method at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenyl ether/ABS (Acrylonitrile Butadiene Styrene) alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Example 1 Preparation of polyphenylene ether / ABS alloy of the present invention (1)

[0059] (1) Weigh it according to the following weight percentage: PPE LXR045: 99.5%, maleic anhydride: 0.5%, put it into the high mixer and mix it for 2-5 minutes, and then add it from the first section of the twin-screw extruder. mixed extrusion, granulation;

[0060] (2) Weigh raw materials according to the following weight percentages: step (1) extruded PPE LXR045: 40%, ABS: 40%, Karton G1651: 10%, polystyrene (PS) graft: 9.2%, antioxidant Agent 1098: 0.2%, antioxidant 168: 0.2%, lubricant SR: 0.4%;

[0061] (3) The above-mentioned raw materials were blended in a high-speed mixer for 5 minutes, and then extruded and granulated by a twin-screw extruder. The rotation speed of the screw machine was 500 rpm and the temperature was 245°C.

Embodiment 2

[0062] Example 2 Preparation of polyphenylene ether / ABS alloy of the present invention (2)

[0063] (1) Weigh it according to the following weight percentage: PPE LXR045: 99%, maleic anhydride: 1%, put it into the high mixer and mix it for 2-5 minutes, and then add it from the first section of the twin-screw extruder. mixed extrusion, granulation;

[0064] (2) Weigh raw materials according to the following weight percentages: step (1) extruded PPE LXR045: 45% and ABS: 39.2%, Karton G1650: 5%, hydrogenated triblock copolymer (SEBS) graft: 10 %, antioxidant 1098: 0.2%, antioxidant 168: 0.2%, lubricant paraffin: 0.4%;

[0065] (3) The above-mentioned materials were blended in a high-speed mixer for 5 minutes, and then extruded and granulated by a twin-screw extruder. The rotation speed of the screw machine was 400 rpm and the temperature was 255°C.

Embodiment 3

[0066] Example 3 Preparation of polyphenylene ether / ABS alloy of the present invention (3)

[0067] (1) Weigh it according to the following weight percentage: PPE LXR035: 98%, maleic anhydride: 2%, put it into the high mixer and mix it for 2-5 minutes, and then add it from the first section of the twin-screw extruder. mixed extrusion, granulation;

[0068] (2) Weigh raw materials according to the following weight percentages: step (1) extruded PPE LXR035: 40% and ABS: 53%, Karton G1657: 4.3%, SAN-GMA copolymer: 1.8%, antioxidant 1098: 0.2 %, antioxidant 168: 0.2%, lubricant polyethylene wax: 0.5%;

[0069] (3) The above-mentioned materials were blended in a high-speed mixer for 4 minutes, and then extruded and granulated by a twin-screw extruder. The rotation speed of the screw machine was 450 rpm and the temperature was 240°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a polyphenyl ether / ABS (Acrylonitrile Butadiene Styrene) alloy which is prepared from the following raw materials in percentage by weight: 10-60% of polyphenyl ether, 10-60% of ABS, 2-20% of flexibilizer, 1-10% of compatilizer, 0.2-0.6% of antioxidant and 0.2-0.6% of lubricant. The invention also provides a preparation method which comprises the following steps of: firstly blending and extruding the polyphenyl ether and the compatilizer (maleic anhydride), and then extruding with other raw materials and granulating. In the preparation process of the polyphenyl ether / ABS alloy, the compatibility between polyphenyl ether and ABS is improved by use of the fractional mixing compatibility technology and unique compatilizer, thus the polyphenyl ether / ABS alloy has the advantages of good mechanical properties, excellent appearance, high impact resistance and insulating property, low cost and the like, is easy to process and form and resistant to solvents, can be electroplated, and has wide application prospects.

Description

technical field [0001] The invention relates to a modified polyphenylene ether material, in particular to a polyphenylene ether / ABS alloy and a preparation method thereof. Background technique [0002] The chemical name of polyphenylene ether (Polypheylene ether, PPE) is poly 2,6-dimethyl-1,4-phenylene ether, which has good mechanical properties, chemical stability, dielectric properties, heat resistance and flame retardancy. Is a high-performance thermoplastic engineering plastics. However, the molecular chain of PPE is relatively rigid and is very sensitive to notch impact. At the same time, due to its high melt viscosity, it cannot be injection molded, which greatly limits its use. At present, PPE is rarely used alone, and more than 90% of commercial products are obtained by blending with other polymers or chemically modifying them. [0003] Acrylonitrile-butadiene-styrene copolymer (ABS) has excellent impact resistance, heat resistance, low temperature resistance, chem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/12C08L55/02C08L51/06C08L51/00C08L51/08C08L25/12C08K5/1539B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 王尹杰郭建鹏才勇张强苏吉英
Owner 上海日之升科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com