Special reinforcing composite calcium carbonate for polyvinyl chloride pipes

A technology of polyvinyl chloride and calcium carbonate, applied in the field of calcium carbonate, can solve the problems of poor strength and toughness of polyvinyl chloride pipes, deformation and softening of polyvinyl chloride pipes, difficulty in adapting to market demand, etc., to achieve low prices and improve products Quality, creative effect

Inactive Publication Date: 2012-10-10
PLASTIC UNION NEW MATERIAL TECH HUBEI
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, the calcium carbonate used in traditional polyvinyl chloride pipes is easy to deform and soften polyvinyl chloride pipes, which cannot meet the ideal product quality requirements
Therefore, the strength and toughness of the produced polyvinyl chloride pipes are relatively poor, and the production cost is relatively high, the quality is unstable, and it is difficult to meet the needs of the market, which also limits its popularization and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Rigid compound calcium carbonate of the present invention is formulated by the following process procedures:

[0015] One, prepare the preparation of each component and parts by weight of the described stiffened synthetic calcium carbonate

[0016] 1. Preparation of polyvinyl chloride functional regulator:

[0017] According to the ratio of polyvinyl chloride functional regulator, take 1.5% of ethylene vinyl acetate and vinyl chloride graft copolymer, and 0.05% of aluminate coupling agent, put them together in the agitator, stir at room temperature, and stir evenly Then it can be ready for use.

[0018] 2. The preparation of each component and parts by weight:

[0019] Calcium carbonate 80; polyvinyl chloride function regulator 5; stearic acid 1, spare. (The calcium carbonate is heavy calcium carbonate or light calcium carbonate)

[0020] two. The preparation of described stiffened synthetic calcium carbonate:

[0021] Mixing: mix the above prepared components by ...

Embodiment 2

[0023] This embodiment is basically the same as Embodiment 1, the difference is that:

[0024] One, prepare the preparation of each component and parts by weight of the stiffened synthetic calcium carbonate:

[0025] 1. Preparation of polyvinyl chloride functional regulator:

[0026] According to the ratio of polyvinyl chloride functional regulator, take ethylene vinyl acetate and vinyl chloride graft copolymer 2, and aluminate coupling agent 0.07, put them into the mixer together, stir at room temperature, and stir evenly Then it can be ready for use.

[0027] 2. The preparation of each component and parts by weight:

[0028] Calcium carbonate 100; polyvinyl chloride function regulator 8; stearic acid 1.5, spare. (The calcium carbonate is heavy calcium carbonate or light calcium carbonate)

Embodiment 3

[0030] This embodiment is basically the same as Embodiment 1, the difference is that:

[0031] One, prepare the preparation of each component and parts by weight of the stiffened synthetic calcium carbonate:

[0032] 1. Preparation of polyvinyl chloride functional regulator:

[0033] According to the ratio of the polyvinyl chloride functional regulator, take 2.5% of ethylene vinyl acetate and vinyl chloride graft copolymer, and 0.10% of the aluminate coupling agent, put them together in the agitator, stir at room temperature, and stir evenly Then it can be ready for use.

[0034] 2. The preparation of each component and parts by weight:

[0035] Calcium carbonate 120; polyvinyl chloride function regulator 10; stearic acid 2, spare. (The calcium carbonate is heavy calcium carbonate or light calcium carbonate)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special reinforcing composite calcium carbonate for polyvinyl chloride pipes. The reinforcing composite calcium carbonate is made of, by weight, 80-120 parts of calcium carbonate, 5-10 parts of polyvinyl chloride functional modifier and 1-2 parts of stearic acid. The preparation process of the reinforcing composite calcium carbonate is mixing. The special reinforcing composite calcium carbonate has the advantages of reasonable conception, standard process, simplicity in operation, low cost and freeness of pollution, and using the special reinforcing composite calcium carbonate for processing of polyvinyl chloride pipes can improve product performance, lower product cost and the like. The special reinforcing composite calcium carbonate is applicable to industrial batch production and can be widely used for the field of processing of the polyvinyl chloride pipes.

Description

technical field [0001] The invention relates to a kind of calcium carbonate used for plastics, in particular to a kind of rigidified calcium carbonate specially used for polyvinyl chloride pipes. Background technique [0002] As we all know, the calcium carbonate used in traditional polyvinyl chloride pipes is easy to deform and soften polyvinyl chloride pipes, which cannot meet the ideal product quality requirements. Therefore, the strength and toughness of the produced polyvinyl chloride pipes are relatively poor, and the production cost is relatively high, the quality is unstable, and it is difficult to meet the needs of the market, which also limits its popularization and application. Contents of the invention [0003] The purpose of the present invention is to overcome the defects of the above-mentioned background technology, replace the calcium carbonate used in traditional polyvinyl chloride pipes, improve the quality of polyvinyl chloride pipes, and reduce the prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/06C08K13/02C08K3/26C08K5/09
Inventor 邓丽邓军邓忠权陈绪煌
Owner PLASTIC UNION NEW MATERIAL TECH HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com