A frit and milky white technology, applied in the field of frit for preparing ceramics, can solve the problems of toxicity hazards and uneven color distribution of the glaze surface for users and producers, and achieve high environmental protection and safety performance, fine glaze surface, and uniform color and luster. Effect

Inactive Publication Date: 2012-10-10
CARLOBBIA GLAZE KUNSHAN
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the process of ceramic preparation, frit is the main material for making low glaze. The frit in the prior art is mostly added with a large amount of heavy metal lead, which brings great toxic hazards to users and producers, and the existing The color distribution of the glaze surface prepared by the frit is not uniform. As people's environmental protection seems to be strengthened, it is necessary to develop and design a lead-free milky white frit that is environmentally safe and uniform in color based on the existing technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of lead-free milky white frit, it is made of the raw material of following parts by weight:

[0020] SiO 2 50 parts, Al 2 o 3 5 parts, CaO 5 parts, ZnO 5 parts, B 2 o 3 10 parts, ZrO 2 10 copies, K 2 O 5 copies.

Embodiment 2

[0022] A kind of lead-free milky white frit, it is made of the raw material of following parts by weight:

[0023] SiO 2 60 parts, Al 2 o 3 10 parts, CaO10 parts, ZnO10 parts, B 2 o 3 20 parts, ZrO 2 20 parts, Na 2 O10 copies.

Embodiment 3

[0025] A kind of lead-free milky white frit, it is made of the raw material of following parts by weight:

[0026] SiO 2 55 parts, Al 2 o 3 8 parts, CaO8 parts, ZnO8 parts, B 2 o 3 15 parts, ZrO 2 15 copies, K 2 O 8 servings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses lead-free opalescent frit for ceramics preparation, which is prepared from the following raw materials in part by weight: 50-60 parts of SiO2, 5-10 parts of Al2O3, 5-10 parts of CaO, 5-10 parts of ZnO, 10-20 parts of B2O3, 10-20 parts of ZrO2 and 5-10 parts of alkali metal. The lead-free opalescent frit for ceramics preparation disclosed by the invention has the advantages of no added poisonous lead element, environment friendliness, safety, uniform opalescence and wide application scope.

Description

[0001] technical field [0002] The invention relates to a frit for preparing ceramics, in particular to a lead-free opalescent frit for ceramics. Background technique [0003] In the process of ceramic preparation, frit is the main material for making low glaze. The frit in the prior art is mostly added with a large amount of heavy metal lead, which brings great toxic hazards to users and producers, and the existing The color distribution of the glaze surface prepared by the frit is not uniform. As people seem to strengthen their awareness of environmental protection, it is necessary to develop and design a lead-free milky white frit that is environmentally safe and uniform in color based on the existing technology. Contents of the invention [0004] Purpose of the invention: The technical problem to be solved by the present invention is to overcome the deficiencies of the prior art and provide a lead-free milky white frit that does not add metal lead, is safe and environ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 赵白弟
Owner CARLOBBIA GLAZE KUNSHAN
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com