Color-unchangeable lead-containing opalescent frit

A frit and milky white technology, which is applied in the field of frit for preparing ceramics, can solve the problems of low density of frit, poor covering ability, narrow firing range, etc., and achieves milky white color, which is not easy to change color, has good smoothness, and is easy to be fired. wide range of effects

Inactive Publication Date: 2012-10-10
CARLOBBIA GLAZE KUNSHAN
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the rapid development of the economy and the improvement of people's living standards, ceramic products have become indispensable products for people. However, the frits used for pottery making in the prior art generally have low density, poor covering ability, and narrow firing range. Disadvantages such as easy discoloration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A non-discoloration leaded opalescent frit, which is made from the following raw materials in parts by weight:

[0020] SiO 2 50 parts, Al 2 o 3 10 parts, CaO 5 parts, PbO 40 parts, ZrO 2 5 copies, K 2 O 5 copies.

Embodiment 2

[0022] A non-discoloration leaded opalescent frit, which is made from the following raw materials in parts by weight:

[0023] SiO 2 40 parts, Al 2 o 3 5 parts, 1 part of CaO, 30 parts of PbO, ZrO 2 1 part, Na 2 O1 copies.

Embodiment 3

[0025] A non-discoloration leaded opalescent frit, which is made from the following raw materials in parts by weight:

[0026] SiO 2 45 parts, Al 2 o 3 8 parts, CaO3 parts, PbO35 parts, ZrO 2 3 parts, LiO 2 3 copies.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses color-unchangeable lead-containing opalescent frit which is prepared from the following raw materials in part by weight: 40-50 parts of SiO2, 5-10 parts of Al2O3, 1-5 parts of CaO, 30-40 parts of PbO, 1-5 parts of ZrO2 and 1-5 parts of alkali metal. The color-unchangeable lead-containing opalescent frit disclosed by the invention has the beneficial effects that the composition proportion is determined through a lot of experimental screening, experimental results show that all the components are more scientifically and reasonably proportioned, ceramics prepared by the frit disclosed by the invention has good glazed smoothness, good enamel, uniform opalescence and wide application scope.

Description

[0001] technical field [0002] The invention relates to a frit for preparing ceramics, in particular to a non-discoloring lead-containing opalescent frit for ceramics. Background technique [0003] With the rapid development of the economy and the improvement of people's living standards, ceramic products have become indispensable products for people. However, the frits used for pottery making in the prior art generally have low density, poor covering ability, and narrow firing range. Disadvantages such as easy discoloration. Therefore, be very necessary on the basis of prior art, develop and design a kind of good enamel, uniform color and luster, good enamel, the lead-containing opalescent frit that does not change color. Contents of the invention [0004] Purpose of the invention: The technical problem to be solved by the present invention is to overcome the deficiencies of the prior art and provide a glaze with good smoothness, good enamel, especially uniform milky wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 赵白弟
Owner CARLOBBIA GLAZE KUNSHAN
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com