Low temperature metal color glaze material and application method thereof

A low-temperature metal and pigment technology, which is applied in the field of low-temperature metallic color glaze and its preparation, can solve the problems of complicated production process, high firing temperature, complicated formula, etc., and achieves the effects of simple formula, bright glaze and convenient use.

Inactive Publication Date: 2012-08-01
东莞市高诚陶瓷制品有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The disadvantages of the above-mentioned patents are: complex formula, high firing temperature, complicated manufacturing process and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0017] (1) Raw materials used:

[0018] Pigment P924 is produced by Dongguan Jinyifa Ceramics Pigment Co., Ltd.;

[0019] Pigment 22605 produced by Dongguan Jinyifa Ceramics Pigment Co., Ltd.;

[0020] Pigment 56401 produced by Dongguan Jinyifa Ceramics Pigment Co., Ltd.;

[0021] Pigment 72503 is produced by Dongguan Jinyifa Ceramics Pigment Co., Ltd.;

[0022] Pigment SVSK-6068 produced by Carobia Glaze (Kunshan) Co., Ltd.;

[0023] Matting agent 3007 produced by Carobia Glaze (Kunshan) Co., Ltd.;

[0024] Blending oil 80003 is produced by Dongguan Jinyifa Ceramics Pigment Co., Ltd.

[0025] (2) Mix 5 parts by weight of colorant P924, 2.5 parts by weight of colorant 22605, 5 parts by weight of colorant 56401, 2 parts by weight of matting agent 3007 and 2.5 parts by weight of colorant 72503 to obtain the bottom glaze; colorant SVSK- 6068 as top glaze;

[0026] (3) Mix the base glaze, blending oil and industrial alcohol according to the weight ratio of 100:35:30, spray t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a low temperature metal color glaze material and an application method thereof. The low temperature metal color glaze material comprises a ground glaze and a cover glaze and is characterized in that the ground glaze is a mixture of 5 parts by weight of pigments P924, 2-3 parts by weight of pigments 22605, 4-6 parts by weight of pigments 56401, 1-3 parts by weight of flatting agents 3007 and 2-3 parts by weight of pigments 72503; the cover glaze is composed of a pigment SVSK-6068. According to the low temperature metal color glaze material and the application method thereof, obtained products have metallic luster.

Description

technical field [0001] The invention relates to a low-temperature metallic color glaze and a preparation method thereof. Background technique [0002] As ceramic products enter millions of households, ceramic glazes are indispensable decorative materials for ceramic products. The existing ceramic glazes can be roughly classified according to their categories and uses as follows: 1. Lead glaze and lead-free glaze; 2. Raw glaze and frit glaze; 3. Glaze for primary firing or secondary firing; 4. Glaze for ceramic tiles, tableware, sanitary ceramics and electric porcelain; 5. Dip glaze, spray glaze, pouring glaze according to the glaze method; Glaze and low temperature glaze; 7. High expansion glaze and low expansion glaze; 8. Firing atmosphere oxidation flame, neutral flame and reducing flame; 9. Color glaze and colorless glaze; 10. Transparent glaze and opacity glaze; 11. Gloss glaze, matt glaze, semi-matt glaze or pattern glaze and so on. The stability and diversity of cera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 蔡世山
Owner 东莞市高诚陶瓷制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com