Jade-like Ru porcelain and preparation method thereof

A kind of Ru porcelain and jade technology, applied in the field of ceramic manufacturing, can solve the problems of lack of innovation in the development of Ru kiln porcelain, and achieve the effect of enriching cultural connotation, increasing added value and transparent texture.

Active Publication Date: 2012-07-11
河南弘宝汝瓷坊有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Today, when people's aesthetic concepts tend to be diversified and consumer demand is constantly changing, in the face of the market, lack of innovation has become a bottleneck restricting the development of Ru kiln porcelain.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1 The preparation method of a jade Ru porcelain bowl (caliber 15cm, height 7cm, foot diameter 6.5cm):

[0019] (1) Green body preparation: check, select and rinse kaolin raw materials (including SiO 2 72%, Al 2 o 3 21%, CaO 0.4%, MgO 0.3%, K 2 O 5%, Na 2 O 0.5%, MnO 0.04%, and Fe 2 o 3 Content2 content <0.3%, the same below), after being crushed, it will be ground in a ball mill, and after iron removal, it will be filtered, smelted, stale, and hand-drawn to form a green body;

[0020] (2) Preparation of plain tire: put the green body into the kiln and burn it for 3 hours at 800°C to 900°C (it takes 40 minutes before 500°C, and then the temperature can be raised evenly), after cooling, it leaves the kiln to obtain the plain tire;

[0021] (3) Glaze preparation: take aphanitic quartz and calcinate it at 1250-1300°C for 7 hours, and then crush it into particles suitable for ball milling for later use; take bone ash and roast it at 850-950°C for 2 hours, and...

Embodiment 2

[0023] Example 2 The preparation method of a jade Ru porcelain water cup (diameter 8cm, height 10cm) is basically the same as Example 1, the difference is:

[0024] ①Glaze preparation: take aphanitic quartz and calcinate at 1250-1300°C for 6 hours, then crush it into particles suitable for ball milling for later use, and take bone ash at 850-950°C for 2.5 hours, then crush it into granules suitable for ball milling for later use , and take feldspar, calcite and soda stone respectively, and then crush them according to the glaze ratio (60% feldspar, 20% calcite, 12% aphanitic quartz, 4% soda stone, 2% ashes, and 2% plant ash). The ingredients are mixed and then put into a ball mill for grinding, after passing through a 250-mesh sieve, iron is removed, and glaze is applied on the above-mentioned plain tire;

[0025] ② Firing: Put the plain body into the kiln after glazing, oxidize and evaporate at 300°C-600°C for 1.5 hours (during which the temperature rises at a constant speed)...

Embodiment 3

[0027] Example 3 The preparation method of a jade Ru porcelain vase (bottom foot diameter 12.5cm, height 36cm) is basically the same as Example 1, except that:

[0028] ①Glaze preparation: take cryptocrystalline quartz and calcinate at 1250-1300°C for 8 hours, then crush it into particles suitable for ball milling for later use, and take bone ash at 850-950°C for 2.5 hours, then crush it into granules suitable for ball milling for later use , and take feldspar, calcite, soda stone to break, and then according to the glaze ratio (feldspar 72%, calcite 10%, aphanitic quartz 7%, soda stone 3%, bone ash 4%, plant ash 4%) The ingredients are mixed and ground into a ball mill, and iron is removed after passing through a 180-mesh sieve, and glaze is applied on the above-mentioned plain tire;

[0029] ② Firing: Put the plain body into the kiln after glazing, oxidize and evaporate at 300°C-600°C for 2.5 hours (the temperature rises at a constant speed during the period), and then oxidi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a jade-like Ru porcelain and a preparation method thereof. The jade-like Ru porcelain comprises a body and a glaze, wherein the preparation raw material of the body is of kaolin, and the preparation raw materials of the glaze comprises the following components in percentage by weight: 55%-80% of feldspar, 10%-25% of calcite, 5%-15% of cryptocrystalline quartz, 2%-10% of alkaline stone, 1%-8% of bone ash and 1%-8% of plant ash. According to the jade-like Ru porcelain disclosed by the invention, the Ru porcelain glaze with jade quality is combined with the body with thejade quality, a traditional Ru porcelain firing process is adopted for enabling the porcelain body to show the jade-like translucent state, color and luster are elegant, pale and graceful, a brand new visual impact and an artistic effect can be further generated, and the millenary Ru porcelain can further realize the historic breakthrough. A new species is added in the family of the Ru porcelain,the cultural connotation of the Ru porcelain is enriched, and the added value and the market share of Ru porcelain products are further improved.

Description

technical field [0001] The invention relates to the field of ceramic manufacturing, in particular to a jade-quality Ru porcelain and a preparation method thereof. Background technique [0002] Ru Porcelain is one of the five famous porcelains of Song Dynasty in my country. Famous in the world, known as "Ru porcelain is the first" in the world. The enamel of traditional Ru porcelain is warm and moist like jade, and the body is like incense ash. It is thick and has the air of a king. Ru porcelain was determined by the court of the Song Dynasty as official kiln porcelain exclusively for the royal family, and it was forbidden to be used among the common people. Due to the short firing time of Ru porcelain, there are less than a hundred pieces handed down from generation to generation, so each piece of Ru porcelain is extremely valuable. There is a folk proverb: "A rich family is not as good as a piece of Ru porcelain", which shows the preciousness of Ru porcelain. [0003] Ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B41/86C04B33/34
Inventor 范晨雨王振芳范随州
Owner 河南弘宝汝瓷坊有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com