B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent and preparation and application thereof

A b-p-mg-si, density board technology, applied in the field of chemical materials, can solve the problem that inorganic flame retardants are difficult to achieve flame retardant effect, and achieve the effect of ensuring anti-mold effect, high safety, and improving mixing uniformity.

Inactive Publication Date: 2013-07-03
SHANDONG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult for a single-component inorganic flame retardant to achieve the ideal flame retardant effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent and preparation and application thereof
  • B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent and preparation and application thereof
  • B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A kind of B-P-Mg-Si series density board flame retardant antifungal agent, raw material composition is as follows:

[0057] Sodium borate (Na 2 B 4 o 7 10H 2 O): 60 kg;

[0058] Ammonium polyphosphate ((NH 4 PO 3 ) n ): 80 kg;

[0059] Magnesium Hydroxide (Mg(OH) 2 ): 48 kg;

[0060] 40% ethanol solution of organic silicon quaternary ammonium salt: 30 kg, wherein the content of organic silicon quaternary ammonium salt is 12 kg.

[0061] Preparation method, the steps are as follows:

[0062] Dry sodium borate at 60-70°C for 6 hours, then mix it with 40% ethanol solution of organic silicon quaternary ammonium salt, stir for 20 minutes to make it evenly mixed, let it stand for 12 hours, then add ammonium polyphosphate and magnesium hydroxide respectively , stirred for 30min, that is.

[0063] Prepare flame-retardant and mildew-proof density boards 1A, 1B, and 1C by using a flame-retardant and anti-mold agent for density boards. The steps are as follows:

[006...

Embodiment 2

[0072] B-P-Mg-Si series density board flame retardant antifungal agent as described in Example 1, the difference is that the raw material components are as follows:

[0073] Sodium borate (Na 2 B 4 o 7 10H 2 O): 80 kg;

[0074] Ammonium polyphosphate ((NH 4 PO 3 ) n ): 60 kg;

[0075] Magnesium Hydroxide (Mg(OH) 2 ): 44 kg;

[0076] 40% ethanol solution of organic silicon quaternary ammonium salt: 40 kg, that is, 16 kg of pure organic silicon quaternary ammonium salt.

[0077] The preparation method is the same as in Example 1.

[0078] Utilize density board flame retardant antimold agent to prepare flame retardant antimildew density board 2A, 2B, 2C, the preparation method of flame retardant antimold density board 2 is as described in embodiment 1, the difference is that 200 kilograms of prepared antifungal Flame-proof and mildew-proof agents were added to 3100 kg, 3800 kg, and 4800 kg of dry wood obtained by washing and heat-grinding qualified fibers, and processe...

Embodiment 3

[0086] The B-P-Mg-Si series density board flame retardant antifungal agent as described in Example 1, the difference is that the raw material components are as follows:

[0087] Sodium borate (Na 2 B 4 o 7 10H 2 O): 100 kg;

[0088] Ammonium polyphosphate ((NH 4 PO 3 ) n ): 40 kg;

[0089] Magnesium Hydroxide (Mg(OH) 2 ): 40 kg;

[0090] Organosilicon quaternary ammonium salt ([(CH 3 CH 2 O) 3 Si(CH 2 ) 3 N(CH 3 ) 2 (C 18 h 37 )] + Cl - ) 40% ethanol solution: 50 kilograms, that is, pure organic silicon quaternary ammonium salt: 20 kilograms.

[0091] The preparation method is the same as in Example 1.

[0092]Utilize density board flame retardant antimold agent to prepare flame retardant antimold density board 3A, 3B, 3C, the preparation method of flame retardant antimold density board 3 is as described in embodiment 1, the difference is that 200 kilograms of prepared antifungal 3,100 kg, 3,800 kg, and 4,800 kg of absolute-dried wood were added to the qu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent and a preparation method and application thereof. The density fiber board inflaming-retarding mildewproof agent comprises the raw materials in parts by weight: 30-100 parts of sodium borate, 20-90 parts of polyammonium phosphate, 40-60 parts of magnesium hydroxide and 6-20 parts of organosilicon quaternary ammonium salt. When used for preparing a density fiber board, the B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent has the addition amount of 4-6 percent of the mass of oven-dry wood as the density fiber board. An inflaming-retarding mildewproof density fiber board prepared by adopting the B-P-Mg-Si series density fiber board inflaming-retarding mildewproof agent has combustion oxygen indexes of exceeding 39.0 percent, can reach the B1-level standard of the combustion performance of building finishing materials, and accords with the requirement of fire service law.

Description

technical field [0001] The present invention relates to a density board flame-retardant anti-mildew material and its preparation method and application, in particular to a density board flame-retardant anti-mold agent containing B-P-Mg-Si element and its preparation method and application, belonging to chemical materials technology field. Background technique [0002] With the rapid development of the national economy, people's living standards have been greatly improved, and the per capita housing area is getting larger and larger. At present, the per capita housing construction area of ​​our residents has exceeded 30 square meters per person. The unprecedented prosperity of the interior decoration industry has led to a large consumption of various materials. In 2009, my country's timber consumption reached 330 million cubic meters, becoming the second largest timber consumer in the world after the United States. my country's forest resources are scarce, and the timber is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27N3/04B27N1/00A01N55/10A01P1/00
Inventor 刘少杰陆玮洁刘华飞刘渊
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com