Elastic fuzz polyurethane paint

A polyurethane coating and fluff technology, applied in the direction of polyurea/polyurethane coating, coating, etc., to achieve the effect of good construction tolerance, good water resistance, and improved coating efficiency

Active Publication Date: 2011-07-13
GUANGDONG SANVO CHEM IND TECH
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The distribution ratio of each component formula by weight is as follows:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Elastic fuzz polyurethane paint
  • Elastic fuzz polyurethane paint
  • Elastic fuzz polyurethane paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Component A: 20 parts by weight of elastic polyurethane resin Japan Tiancheng CM-6089, 25 parts of fluff pulp (by weight proportion: fluff powder: hand feeling agent: solvent = 8: 0.9: 4) dispersant German Qian 9100.2 parts, under stirring, add 15 parts of nano-prepolymer (the proportion by weight is mica powder: nano-montmorillonite: dispersant: solvent = 45: 18: 0.1: 36.9); grind to fineness ≤ 30 μm; put 0.2 part of leveling agent BYK306 in Germany, and 39.6 parts of remaining diluent (distribution ratio by weight: butyl acetate: propylene glycol methyl ether acetate = 3:7); after passing the inspection, it can be made into a group. points A;

[0027] Component B: 30 parts of HDI trimer polyisocyanate, 40 parts of HDI-TDI trimer, and 30 parts of butyl acetate by weight ratio are mixed evenly, and then component B can be prepared;

[0028] Component C: 70 parts of butyl acetate and 30 parts of propylene glycol methyl ether acetate are mixed evenly by weight, and then ...

Embodiment 2

[0031] Component A: 25 parts of elastic polyurethane resin Japan Tiancheng TM-6080 and 20 parts of fluff pulp (in proportion by weight: fluff powder: hand feeling agent: solvent = 10: 0.6: 6) are put into the dispersing cylinder Add 0.3 part of dispersant Deqian 903, and under stirring, add 17 parts of nano-prepolymer (the proportion by weight is mica powder: nano-montmorillonite: dispersant: solvent = 50: 15: 0.1: 34.9) , dispersed for 10min; ground to a fineness of ≤30 μm; put into leveling agent BYK358N 0.3 part, the remaining diluent (by weight distribution ratio: butyl acetate: propylene glycol methyl ether acetate = 5: 10) 37.4 parts ; After passing the inspection, it can be made into component A;

[0032] Component B: 40 parts of HDI trimer polyisocyanate, 30 parts of HDI-TDI trimer, and 30 parts of butyl acetate by weight ratio are mixed evenly, and then component B can be prepared;

[0033] Component C: by weight, 80 parts of butyl acetate and 20 parts of propylene g...

Embodiment 3

[0036] Component A: 30 parts of elastic polyurethane resin Japan Tiancheng M1783 and 25 parts of fluff pulp (in proportion by weight: fluff powder: hand feeling agent: solvent=10: 0.7: 6) are put into the dispersing cylinder in proportion by weight, Add 0.5 part of dispersant Huaxia HX-4030, under stirring, add 20 parts of nano-prepolymer (the proportion by weight is mica powder: nano-montmorillonite: dispersant: solvent=60: 18: 0.2: 21.8), Disperse for 30min; grind to a fineness of ≤30μm; put in 0.5 part of leveling agent Deqian 435 and the remaining amount of diluent (distribution ratio by weight: butyl acetate: propylene glycol methyl ether acetate = 15:5) 24 parts; inspection After qualified, it can be made into component A;

[0037] Component B: 35 parts of HDI trimer polyisocyanate, 35 parts of HDI-TDI trimer, and 30 parts of butyl acetate by weight ratio are mixed evenly, and then component B can be prepared;

[0038] Component C: 90 parts by weight of butyl acetate an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
acid valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an elastic fuzz polyurethane paint which is prepared by evenly mixing a component A, a component B and a component C in weight ratio, wherein the component A is prepared from elastic polyurethane resin, fuzz slurry, a dispersant, nano prepolymer, a leveling agent and the balance of a diluter; the component B is prepared from HDI (hexamethylene diisocyanate) tripolymer polyisocyanate, HDI-TDI (toluene diisocyanate) tripolymer and butyl acetate; and the component C is prepared from butyl acetate and propylene glycol monomethyl ether acetate. Compared with similar paints on the market, the invention has the following advantages: 1. by selecting optimal elastic resin, the elastic fuzz polyurethane paint feels more elastic and looks more fuzzy; 2. the elastic fuzz polyurethane paint is preferably compounded from inert pigment mica powder, fuzz powder and nano materials, thereby having the advantages of weather resistance, scoring resistance, water resistance, anti-static property and high surface gloss; and 3. the elastic fuzz polyurethane paint has great construction tolerance, thereby enhancing the painting efficiency.

Description

technical field [0001] The invention relates to a functional coating of polymer materials, in particular to an elastic fluff polyurethane coating. Background technique [0002] The development of industry and the improvement of people's living standards are widely used as polymer materials in the coating industry. Polyurethane coating is one of them, because of its good performance, the output is getting bigger and bigger. [0003] As a functional paint, "fleece paint" refers to a highly decorative paint with a "fleece effect" that people feel the soft, soft and slippery feel of fabric and suede on its coating film visually and tactilely. Fleece paint was first developed by Japan's Musashi Paint Company in 1971 because of its good decorative and protective effects. It gives people a comfortable feel and a soft and high-level visual experience, so it has been greatly developed in the coatings industry as a high-performance and high-decorative coating. In 1992, Japan Riyu P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C09D5/00
Inventor 陈炳耀董颖许耀魁
Owner GUANGDONG SANVO CHEM IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com