Fog sealing layer asphalt emulsion admixture and use method thereof

A technology of asphalt emulsion and asphalt emulsifier, which is applied in the field of materials, can solve the problems of inability to regenerate asphalt materials, poor cohesion, and poor penetration, and achieve the effects of preventing water damage to asphalt pavement, strong adhesion, and enhanced penetration

Inactive Publication Date: 2011-04-13
陕西长大博源公路养护科技有限公司
View PDF4 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the defects of poor adhesion and poor penetration of the above-mentioned mist seal layer asphalt emulsion and the original old road surface, and can not regenerate the aging asphalt material of the old road surface, and provide a kind of effective improvement in fog seal layer asphalt emulsion. Fog-sealed asphalt emulsion admixture with excellent adhesion, durability, impermeability and pavement regeneration performance and its application method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fog sealing layer asphalt emulsion admixture and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Taking the preparation of the present invention's mist seal layer asphalt emulsion admixture 100kg as an example, the mass proportioning of the raw materials used is as follows:

[0041] Aromatic oil 50kg

[0042] Coal tar 6kg

[0043] Penetrant JFC 2kg

[0044] Alkylphenol polyoxyethylene ether OP-10 2kg

[0045] Neoprene latex 5kg

[0046] water 35kg

[0047] Its preparation method is as follows:

[0048] Heat aromatic oil and coal tar to a molten state, add penetrant JFC and alkylphenol polyoxyethylene ether OP-10 into water at 50°C, stir and dissolve, dissolve aromatic oil and coal tar in molten state, dissolve penetrant JFC and Add the aqueous solution of alkylphenol polyoxyethylene ether OP-10 and neoprene latex into the emulsifier, and emulsify for 3 minutes to form a dispersed and uniform emulsion, and prepare the asphalt emulsion admixture for the mist seal layer.

[0049] The using method of the mist seal layer asphalt emulsion admixture of the present inv...

Embodiment 2

[0057] Taking the preparation of the present invention's mist seal layer asphalt emulsion admixture 100kg as an example, the mass proportioning of the raw materials used is as follows:

[0058] Furfural extraction oil 30kg

[0059] Kerosene 5kg

[0060] Penetrant JFC-1 1kg

[0061] Nonylphenol polyoxyethylene ether TX-10 1kg

[0062] Neoprene latex 2kg

[0063] water 61kg

[0064] Its preparation method is as follows:

[0065] Heat the furfural oil and kerosene to a molten state, add penetrant JFC-1 and nonylphenol polyoxyethylene ether TX-10 into water at 30°C, stir and dissolve, extract the furfural oil and kerosene in the molten state, and dissolve the penetrant The aqueous solution of JFC-1, nonylphenol polyoxyethylene ether TX-10, and neoprene latex are added to the emulsifier, and emulsified for 1 minute to form a dispersed and uniform emulsion, which is prepared as an asphalt emulsion admixture for fog seal layer.

[0066] The using method of the mist seal layer a...

Embodiment 3

[0074] Taking the preparation of the present invention's mist seal layer asphalt emulsion admixture 100kg as an example, the mass proportioning of the raw materials used is as follows:

[0075] Aromatic oil 60kg

[0076] Diesel 10kg

[0077] Penetrant JFC-2 3kg

[0078] Alkylphenol polyoxyethylene ether OP-9 5kg

[0079] Nitrile Latex 8kg

[0080] water 14kg

[0081] Its preparation method is as follows:

[0082] Heat aromatic oil and diesel oil to a molten state, add penetrant JFC-2 and alkylphenol polyoxyethylene ether OP-9 into water at 70°C, stir and dissolve, and dissolve aromatic oil and diesel oil in molten state, and dissolve penetrant JFC- 2 and the aqueous solution of alkylphenol polyoxyethylene ether OP-9 and nitrile latex are added to the emulsifier, and emulsified for 5 minutes to form a dispersed and uniform emulsion, which is prepared as a mist seal layer asphalt emulsion admixture.

[0083] The using method of the mist seal layer asphalt emulsion admixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetration depthaaaaaaaaaa
Login to View More

Abstract

The invention provides a fog sealing layer asphalt emulsion admixture and a use method thereof. The admixture consists of the following raw materials in percentage by mass: 30 to 60 percent of asphalt reclaiming agent, 5 to 10 percent of asphalt reclaiming aid, 1 to 3 percent of penetrant, 1 to 5 percent of emulsifier, 2 to 8 percent of tackifier, and the balance water. When the admixture is added into a fog sealing material, the infiltrability of the fog sealing layer asphalt emulsion can be reinforced, thus the emulsion can be quickly filled in pores and microcracks on road surfaces, so that the water seepage resistance of the pavement is reinforced, and the asphalt pavement is prevented from water damage; the admixture can be quickly infiltrated to an aged asphalt layer to harmonize the components in the aged asphalt, so that the aged asphalt is regenerated; the admixture has strong bonding capability with the asphalt pavement, after traffic is open, the fog sealing layer material and the pavement are bonded firmly, and the admixture is not easy to adhere to vehicle wheels; and the molded admixture has accordant color with the newly built pavement, thus the road appearance is beautified.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to an asphalt emulsion admixture for fog seal layer used in road preventive maintenance and a using method thereof. Background technique [0002] The full name of the fog seal is the fog seal, which is a new preventive maintenance technology for road surfaces. The fog seal layer is a layer of fluid material evenly sprayed on the pavement surface layer by using a special fog seal layer asphalt sprinkler. Improve the appearance of the road, so as to prolong the service life of the road surface and save maintenance funds. Common mist seal materials mainly include emulsified asphalt, modified emulsified asphalt and road maintenance agents, etc., because when the materials are sprayed, they appear in the form of mist, so they are collectively referred to as fog seal. [0003] The performance of the fog seal layer material directly affects the quality of the fog seal layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L11/02C08L9/04C08L23/08C08L31/04C08L23/22C08K5/00C08K5/01C08L9/08E01C7/35
Inventor 蔡乾东王安玲商博明贾晓放徐培华
Owner 陕西长大博源公路养护科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com