Novel flame redundant material and preparation method thereof

A flame-retardant material and a new technology, applied in the field of new flame-retardant materials and their preparation, can solve the problems of secondary combustion, molten dripping, small fire and flammability, etc., and achieve reduced harm, good fire resistance, and reduced fire hazards The effect of the probability of occurrence

Active Publication Date: 2010-12-29
北京东方绿达科技发展有限责任公司
View PDF5 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at various problems existing in the actual use of the existing polypropylene plastic foaming materials, such as low fire flammability, long self-extinguishing time after leaving the fire, and molten drips that easily cause secondary combustion during the combustion process. These have buried hidden dangers for the occurrence of fire and the expansion of fire hazards. To provide a new type of flame retardant material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Mix 100 parts of polypropylene, 3 parts of maleic anhydride grafted polypropylene, 0.5 parts of MD-NA-28, 8 parts of HDC103 and 30 parts of compound flame retardant through a high-mixer, and mix them in a screw extruder Plasticized and melted, mixed with butane injected in the middle of the screw extruder, and then extruded and foamed to obtain a flame-retardant material with flame-retardant properties. The weight ratio of ammonium polyphosphate, pentaerythritol, melamine and nano-montmorillonite in the compound flame retardant is 3:1:1:0.5.

Embodiment 2

[0026] Mix 100 parts of polypropylene, 3 parts of maleic anhydride grafted polypropylene, 0.5 parts of MD-NA-28, 8 parts of HDC103 and 10 parts of compound flame retardant through a high-mixer, and mix them in a screw extruder Plasticized, melted and extruded, and then foamed through a dipping tank filled with pentane to obtain a flame-retardant material with flame-retardant properties. The weight ratio of ammonium polyphosphate, pentaerythritol, melamine and nano-montmorillonite in the compound flame retardant is 1:2:2:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel flame redundant material and a preparation method thereof. The flame redundant material comprises the following raw materials in part by weight: 100 parts of polypropylene, 5 to 16 parts of modifier, and 5 to 50 parts of compound flame redundant. The novel flame redundant material has better flame redundancy, and can effectively reduce the occurrence probability of fire disasters and damage caused by the fire disasters compared with other polypropylene plastic foaming materials. In the same foam expansion ratio, the method can prepare flame redundant materials with different flame redundancy by controlling the content of the compound flame redundant.

Description

technical field [0001] The invention relates to a flame-retardant material and a preparation method thereof, in particular to a novel flame-retardant material and a preparation method thereof. Background technique [0002] At present, the existing EPP (Expanded polyproplene): polypropylene plastic foaming materials are all controlled by the expansion rate to control their flame retardancy, and they are all imported from abroad. There are many problems in these materials in the actual use process, such as small fire flammability, long self-extinguishing time from the fire, and molten drips that are easy to cause secondary combustion during the combustion process. And the expansion of fire hazards has buried hidden dangers. High price and easy burning characteristics limit the use of EPP materials. Contents of the invention [0003] The present invention aims at various problems existing in the actual use of the existing polypropylene plastic foaming materials, such as low...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K13/02C08K3/32C08K5/053C08K5/3492C08K3/34C08J9/14C08J9/12
Inventor 果占平唐锦学蒋亚静王建平张翠兰田海江张跃秋易海洋
Owner 北京东方绿达科技发展有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com