Method for dissolving antimonous sulfide into stibious
An antimony trisulfide, chemical dissolution technology, applied in chemical instruments and methods, inorganic chemistry, antimony compounds, etc., to achieve broad application prospects, low price, and complete dissolution effects
Inactive Publication Date: 2010-11-24
NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF2 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
There is no report on the method of dissolving antimony trisulfide into trivalent antimony with HCl, H3PO4 mixed acid after retrieval
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2
Embodiment 3
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
boiling point | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a method for dissolving antimonous sulfide, which utilizes the acidity and coordinating capability of hydrochloric acid and phosphoric acid to dissolve through a chemical dissolving method. In the method, a chemical product antimonous sulfide, the chemical purity of which is 97.0%, is utilized as a dissolving object, the content of antimonous sulfide can be measured after antimonous sulfide is dissolved under the optimum condition, and the measured result data can be used to illustrate the soluble completeness; the optimum condition of dissolving is as follows: adding 12ml of hydrochloric acid and 5ml of phosphoric acid; covering a watch glass, shaking the watch glass on an electric stove while slowly heating until the solution is boiling slightly, removing the watch glass, and maintaining slight boiling until the color of the solution is light yellow and transparent and is completely dissolved. Oxidation-reduction titration is used to measure the content of antimonous sulfide, therefore, the dissolved antimonous sulfide exists in the solution in the form of antimony (III), instead of in form of antimony (V). By using the dissolving method of antimonous sulfide in the invention, the measured result after a sample is dissolved reaches 96.82, which differs 0.18% to the actual value. In the method, the sample can be completely dissolved, and the solvent is non-toxic and safe and has low price, thereby meeting the requirements of environment protection and industrial production. The established dissolving method is also applied to dissolve antimonous sulfide in an antimonite and antimonous sulfide used as an additive in the industry and has wide application prospect.
Description
Method for dissolving antimony trisulfide into trivalent antimony technical field The invention relates to a method for dissolving antimony trisulfide, more particularly, relates to a method for dissolving antimony trisulfide into trivalent antimony with a nontoxic and safe mixed acid of hydrochloric acid and phosphoric acid. When determining the content of antimony trisulfide, redox titration is usually used. Therefore, after dissolving antimony trisulfide, it should exist in the form of trivalent antimony instead of pentavalent antimony in the solution. Background technique Antimony trisulfide is also called antimony sulfide (Sb2S3), black solid powder. Insoluble in water, acetic acid, slowly soluble in hot concentrated sulfuric acid, soluble in concentrated HCl, alcohol, ammonium hydrogen sulfide, potassium sulfide solution. The melting point is 548°C and the boiling point is 1080-1090°C. Antimony oxide is formed after pyrolysis. Sb(III) is soluble in concentrated H...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G30/00
Inventor 刘淑萍闫路省杜世巍
Owner NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com