Fiber decoration board with strong nail-holding ability and producing method thereof

A nail-holding strength and decorative board technology, which is applied in sustainable waste treatment, solid waste management, climate sustainability, etc. Strong nail effect

Inactive Publication Date: 2008-09-17
李学进
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the glass magnesium fiber decorative boards used are not strong enough to hold nails, and cannot meet the construction needs of nail holding power.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In this embodiment, a fiber decorative board with strong nail-holding power comprises the following raw material ratios according to the mass ratio

[0022] (1), 1 part of magnesium oxide, add 0.8 part of magnesium chloride water, 0.25 part of talcum powder, adjust it into a paste, and use it as a surface layer material;

[0023] (2), add 1 part of magnesium oxide, 4 parts of magnesium chloride water, 0.45 parts of talcum powder, 0.44 parts of crop fiber, 1.8 parts of wood fiber, add palm fiber, bamboo fiber, cotton fiber, nylon fiber, green fiber, hemp fiber 1.5 parts of any one or more of cloth fibers left over from clothing factories and waste clothing fibers are mixed into the main material.

[0024] Above a kind of production method of the fiber decorative board with strong nail-holding power comprises the following operations

[0025] A. Take the worktable template: 2500 mm long and 1300 mm wide, and apply the release agent to the template;

[0026] B. Take medi...

Embodiment 2

[0036] This embodiment is a kind of fiber decorative board with strong nail-holding power, which is different from Embodiment 1 in that: according to the mass ratio, it includes the following raw material ratio

[0037] (1), 1 part of magnesium oxide, add 0.9 part of magnesium chloride water, 0.4 part of talcum powder, adjust it into a paste, and use it as a surface layer material;

[0038] (2) Add 1 part of magnesium oxide, 3 parts of magnesium chloride water, 0.5 part of talcum powder, 0.5 part of crop fiber, 2.1 part of wood fiber, add palm fiber, bamboo fiber, cotton fiber, nylon fiber, green fiber, hemp fiber 0.5 parts of any one or more of cloth fibers left over from clothing factories and waste clothing fibers are mixed into the main material.

Embodiment 3

[0040] This embodiment is a kind of fiber decorative board with strong nail-holding power, which is different from Embodiment 1 in that: according to the mass ratio, it includes the following raw material ratio

[0041] (1), 1 part of magnesium oxide, add 1.1 parts of magnesium chloride water, 0.3 parts of talcum powder, adjust it into a paste, and use it as a surface layer material;

[0042] (2), add 1 part of magnesium oxide, 5 parts of magnesium chloride water, 0.3 part of talcum powder, 0.6 part of crop fiber, 2 parts of wood fiber, add palm fiber, bamboo fiber, cotton fiber, nylon fiber, green fiber, hemp fiber 1.2 parts of any one or more of cloth fibers left over from clothing factories and waste clothing fibers are mixed into the main material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fiber decorative board with high nail-holding ability and a production method thereof, and belongs to the technology field of glass / magnesium fiber decorative boards and production method thereof. The invention is characterized in that the fiber decorative board is made from the following materials according to mass percentage: (1) 1 part of magnesium oxide, 0.8-1.2 parts of aqueous solution of magnesium chloride and 0.2-0.4 parts of talc powder, which are mixed until pasty and serve as coating; (2) 1 part of magnesium oxide, 3-5 parts of aqueous solution of magnesium chloride, 0.3-0.5 parts of talc powder, 0.4-0.6 parts of crop fiber, 1.8-2.2 parts of wood fiber and 0.5-1.5 parts of at least one selected from palm fiber, bamboo fiber, cotton fiber, nylon fiber, polyacrylonitrile fiber, bast fiber, fabric fiber overleft from clothing factory, and waste fabric fiber, which are mixed and serve as major ingredient. The production method comprises the following steps: coating a demoulding agent on a template of work table top, paving neutral-alkaline glass fiber fabric on the template, spreading the coating paste on the glass fiber fabric, spreading the major ingredient on the coating and leveling, paving glass fiber fabric on the flat major ingredient, coating with the coating paste, curing to allow molding, demoulding, ageing, cutting and trimming, packaging and storing. The inventive fiber decorative board has high nail-holding ability and good resistance to fire and water.

Description

1. Technical field [0001] The invention relates to a fiber decorative board with strong nail-holding power and a production method, and belongs to the technical field of glass magnesium fiber decorative boards and production methods. 2. Background technology [0002] At present, the glass magnesium fiber decorative boards used have weak nail-holding power, which cannot meet the construction needs of nail-holding power. 3. Contents of the invention [0003] The object of the present invention is to solve the problems in the above-mentioned prior art, and provide a fiber decorative board with strong nail holding power. [0004] A fiber decorative board with strong nail-holding power of the present invention is special in that, according to the mass ratio, it includes the following raw material ratio [0005] (1), 1 part of magnesium oxide, add 0.8-1.2 parts of magnesium chloride water, 0.2-0.4 parts of talcum powder, adjust it into a paste, and use it as a surface layer mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/32C04B18/24C04B18/26
CPCC04B2111/28C04B2111/27C04B28/32C04B41/009C04B2111/30C04B41/52C04B2111/00612Y02W30/91C04B14/042C04B18/24C04B18/248C04B18/26C04B41/4501C04B41/4596C04B41/5024C04B41/509
Inventor 李学进
Owner 李学进
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com