Method for preparing synthetic soap

A technology for toilet soap and soap body, which is applied in the field of preparation of synthetic toilet soap, can solve the problems of rough soap body, mushy soap body, poor molding and the like, and achieves the effects of smooth surface of soap body, stable comprehensive performance and good printing effect.

Active Publication Date: 2008-01-09
安徽华谊日新科技有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the actual preparation process, because the plasticity of soap surfactants is better and easy to form, the plasticity of non-soap surfactants is poor and difficult to form, so the conventional soap soap making method is adopted to produce non-soap surfactants. Mainly synthetic soap, the prepared soap has a rough soap body, bubbles and white cores are prone to appear on the surface of the soap body, the appearance of the soap body is not beautiful, and the soap body is prone to rot when it meets water during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] According to the same dosage of Comparative Example 1, weigh 40 kg of sodium coconut oil isethionate, 20 kg of sodium lauryl sulfate, 10 kg of coconut oleic acid, 1 kg of glycerin, 0.5 kg of softener SG-6, H501 chelate Add 0.4 kg of mixture, 35 kg of dextrin, and 3 kg of water into the kneader, knead and mix evenly, the kneading and stirring time is 10 minutes, and the stirring temperature is 35 ° C; Enter the mill for soap body grinding, the thickness of the soap flakes after grinding is 0.4mm; the soap body after grinding is entered into the vacuum layering machine for vacuum layering, the outlet temperature of the layering nozzle is controlled at 35°C, and the layering The cooling water temperature of the machine is controlled at 10°C; the long soap body extruded by the plodder is directly sent to the printer for printing, and the temperature of the mold is at -25°C during printing, and the synthetic soap is obtained.

[0026] What this synthetic scented soap adopts ...

Embodiment 2

[0028] Weigh 60 kg of sodium coconut oil isethionate, 10 kg of sodium lauryl sulfate, 8 kg of coconut oleic acid, 1.5 kg of glycerin, 2.5 kg of softener SG-6, 0.2 kg of H501 chelating agent, 25 kg of dextrin , 4 kg of water was added to the kneader, kneaded and stirred to mix evenly, the kneading and stirring time was 15 minutes, and the stirring temperature was 30°C; then the kneaded and stirred mixed materials were put into the mill for soaping body grinding, the thickness of the soap flakes after grinding is 0.2 mm; the soap body after grinding is entered into the vacuum plodder for vacuum plodding, the outlet temperature of plodder nozzle is controlled at 40°C, and the cooling water temperature of plodder is controlled at 2 ℃; the long soap body extruded by the plodder directly enters the printer for printing, and the temperature of the mold during printing is -15 ℃, and the synthetic soap is obtained.

[0029] Through the method of the invention, the soap body of the synt...

Embodiment 3

[0031]According to the synthetic soap components and proportions provided in Chinese invention patent 200510095229.9, weigh 25 kg of sodium coconut oil isethionate, 25 kg of sodium lauryl sulfate, 8 kg of myristic acid, 20 kg of dextrin, essence 1.5 kg, 0.5 kg of titanium dioxide, 3 kg of deionized water, 0.2 kg of EDTA-4Na, 0.2 kg of trichlorocarbonanilide, 3 kg of glycerin, 9 kg of cocamidopropyl betaine, added to the kneader, Knead and stir to mix evenly, the kneading and stirring time is 15 minutes, and the stirring temperature is 30°C; then the kneading and stirring mixed materials are put into the mill for soap grinding, and the thickness of the soap flakes after grinding is It is 0.2 mm; the soap body after grinding is entered into the vacuum plodder for vacuum plotting, the outlet temperature of the plotting nozzle is controlled at 40°C, and the temperature of the cooling water of the plotting machine is controlled at 2°C; the long soap body extruded by the plotting mac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

Production of synthetic soap is carried out by weighing various raw materials, putting them kneader, kneading while agitating at 30-35 deg. C for 10-15 mins, putting kneaded raw materials into mill, milling to obtain soap flake with thickness 0.2-0.4 mm, putting milled soap flake into battening machine, vacuum battening at 35-40 deg. C, cooling at 2-10 deg. C, and printing at -15--25 deg. C. It's stable, smooth and fine. It has good effect and appearance and no foam and white core.

Description

technical field [0001] The invention relates to a preparation method of scented soap, in particular to a preparation method of synthetic scented soap. Background technique [0002] In the daily chemical washing industry, soaps can be divided into general soaps and synthetic soaps according to the composition of active substances. The active substances in general soaps are mainly soap surfactants of higher fatty acid salts. This kind of soaps have better plasticity and are easy to shape during processing. Synthetic soap refers to the compounding of soap surfactants and non-soap surfactants with calcium soap dispersing ability and other auxiliary agents, and also includes other non-soap surfactants with calcium soap dispersing ability It is a compounded product of non-soap surfactant and other additives. Non-soap surfactants in synthetic soaps are generally non-ionic surfactants, zwitterionic surfactants, and non-soap anionic surfactants. Easy to shape. [0003] In the pri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11D13/10C11D13/14
Inventor 薛志强刘伟毅
Owner 安徽华谊日新科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com