Base paint for cultural-relic protection and preparing method therefor

A technology for protection of cultural relics and base surface, applied in the field of base paint for protection of cultural relics, can solve the problems of floating sand, decreased adhesion, easy foaming of paint film, etc., and achieves leading technology, long service life and good permeability Effect

Active Publication Date: 2010-11-24
厦门富思特新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional acrylic resin seals the substrate to form a dense paint film, and moisture cannot be released. With the increase of moisture pressure on the wall, the paint film is prone to foaming, cracking and falling off due to condensation and other reasons, resulting in long-term moisture accumulation. Cause floating sand and decrease the cohesive force

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Base paint for cultural-relic protection and preparing method therefor
  • Base paint for cultural-relic protection and preparing method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

Embodiment 2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to art treasure protection using base top coat, manufacturing method and executing technology. The coat includes water, cinepazid emulsion 296DS, calcium carbonate 1250 screen mesh, aqueous purity silicone resin BS-45, calcium carbonate 800 screen mesh, sericite 1250 screen mesh, film forming auxiliary agent 296DS, antifreezing agent, aqueous purity silicone resin BS-1306, dispersing agent 1124, acrylic acid thickener 430, polyurethane thickener 278, pH value regulator AMP-95, antifoam agent NXZ, wetting agent, PE-100 and black carbon color paste. The invention has the advantages of asepsis, vapor permeability, weathering resistance, permeability, good adhesion, easy to gain raw material, simple producing method, and has great application prospect.

Description

Base paint for protection of cultural relics and preparation method thereof technical field The invention relates to the development and construction technology of coatings for cultural relics protection and architectural coatings, more precisely, a base paint (commonly known as a cultural relics protection agent) for cultural relics protection and a preparation method thereof. Background technique China is an ancient and civilized country with many historical and cultural heritages, which have very good research, preservation and appreciation value. However, many cultural relics have been damaged to varying degrees due to disrepair and environmental pollution. The lacquer used for the protection of cultural relics was developed and applied under this background. Traditional acrylic resin seals the substrate to form a dense paint film, and moisture cannot be released. With the increase of moisture pressure on the wall, the paint film is prone to foaming, cracking and fal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D183/00
Inventor 郭祥恩姜年超赵雅文刘东华
Owner 厦门富思特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com