Method for preparing 7055 aluminum alloy with high intensity and high toughness

A high-strength, high-toughness, aluminum alloy technology, applied in the field of aluminum alloy preparation technology, can solve the problems of elongation not exceeding 5%, small ingot size, inability to meet aviation and aerospace industries, etc., to solve structural efficiency, improve resistance The effect of compressive strength

Active Publication Date: 2009-02-18
NORTHEAST LIGHT ALLOY CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-strength and high-toughness 7055 aluminum alloy to solve the problem that the strength of the existing 7055 aluminum alloy is only about 500MPa, the elongation is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. Preparation method of aluminum alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing 7055 aluminum alloy with high intensity and high toughness
  • Method for preparing 7055 aluminum alloy with high intensity and high toughness

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0007] Specific Embodiment 1: The high-strength and high-toughness 7055 aluminum alloy of this embodiment consists of Si: 0.1%, Fe: 0.15%, Cu: 2-2.6%, Mn: 0.05%, Mg: 1.8-2.3%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurity 0.1%, and the balance made of Al.

specific Embodiment approach 2

[0008] Specific embodiment 2: In this embodiment, the weight percentage of Cu is 2.3% of the total weight of the high-strength and high-toughness 7055 aluminum alloy, that is, the high-strength and high-toughness 7055 aluminum alloy consists of Si: 0.1%, Fe: 0.15%, and Cu: 2.3% by weight percentage , Mn: 0.05%, Mg: 1.8-2.3%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurities 0.1% and the balance are made of Al.

specific Embodiment approach 3

[0009] Specific Embodiment Three: In this embodiment, the weight percentage of Mg is 2.1% of the total weight of the high-strength and high-toughness 7055 aluminum alloy, that is, the high-strength and high-toughness 7055 aluminum alloy consists of Si: 0.1%, Fe: 0.15%, and Cu: 2.3% by weight percentage , Mn: 0.05%, Mg: 2.1%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurities 0.1% and the balance are made of Al.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

This invention relates to a method for preparing high-strength and high-toughness 7055 Al alloy. Present 7055 Al alloy has strength of only 500 MPa, and elongation at breakage of only 5%. The high-strength and high-toughness 7055 Al alloy is prepared from: Si 0.1 wt.%, Fe 0.15 wt.%, Cu 2-2.6 wt.%, Mn 0.05 wt.%, Mg 1.8-2.3 wt.%, Cr 0.04 wt.%, Ti 0.06 wt.%, Zr 0.08-0.2 wt.%, Zn 7.6-8.4 wt.%, impurities 0.1 wt.%, and Al as balance. The strength of the high-strength and high-toughness 7055 Al alloy is greater than or equal to 610 MPa (100 MPa more than other 7055 Al alloys), and the elongation at breakage is greater than or equal to 6% (1% more than other 7055 Al alloys). The method can cast Phi 405X1000 mm and Phi 360X1000 mm ingots of the high-strength and high-toughness 7055 Al alloy.

Description

technical field [0001] The invention relates to a preparation process of aluminum alloy. Background technique [0002] The strength of the existing 7055 aluminum alloy is only about 500MPa, and the elongation rate is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. The main reason for the above problems is that the composition of the existing 7055 aluminum alloy is not reasonable enough, and the preparation process of the 7055 aluminum alloy still has defects. Contents of the invention [0003] The purpose of the present invention is to provide a high-strength and high-toughness 7055 aluminum alloy to solve the problem that the strength of the existing 7055 aluminum alloy is only about 500MPa, the elongation is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. Process for the preparation of aluminum alloys. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/10C22C1/02C22C1/06B22D21/04
Inventor 王凤春李念奎单长智王志超王国军陶志民
Owner NORTHEAST LIGHT ALLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com