Low expansion coefficient micro crystal glass and its heat processing method

A low-expansion-coefficient, glass-ceramics technology, applied in the field of low-expansion-coefficient glass-ceramics, can solve problems such as difficult heat treatment of bulk materials, and achieve the effects of easy forming and low crystallization tendency

Active Publication Date: 2011-02-02
CDGM OPTICAL GLASS
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing heat treatment method for glass-ceramics with low expansion coefficient is mainly a two-step method. This method is mainly aimed at thin plates or small pieces of glass that require rapid heat treatment, and it is difficult to heat treat bulk materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low expansion coefficient micro crystal glass and its heat processing method
  • Low expansion coefficient micro crystal glass and its heat processing method
  • Low expansion coefficient micro crystal glass and its heat processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0031] Table 1 is 5 embodiments of the present invention and 2 comparative examples, 5 embodiments of the present invention adopt the method of the present invention to carry out heat treatment, 2 comparative examples adopt existing method to carry out heat treatment.

[0032]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strain pointaaaaaaaaaa
Login to View More

Abstract

The present invention provides one kind of low expansion coefficient micro crystalline glass comprising SiO2 51.5-64 wt%, P2O5 6.8-11 wt%, Li2O 3-5.2 wt%, MgO 0.5-2.2 wt%, ZnO 0.4-2.1 wt%, CaO 0.2-2.5 wt%, BaO 0.5-4.5 wt%, SrO 0.2-3 wt%, and Sb2O3 0.6-2 wt%, Al2O3+SiO2 75-84 wt%, and TiO2+ZrO2 3.5-5 wt%. The micro crystalline glass has expansion coefficient at 20-100 deg.C of + / -0.6x10<-7> / K, visible light transmittance up to 90 %, low recrystallization trend and easy formation.

Description

technical field [0001] The present invention relates to a kind of glass ceramics with low expansion coefficient, particularly relate to a kind of Li 2 O-Al 2 o 3 -SiO 2 Systematic low-expansion-coefficient glass-ceramic and its heat treatment method. Background technique [0002] Japanese Patent Laid-Open No. 2005-89272 and Japanese Patent Laid-Open No. 2005-231994 disclose two kinds of low-expansion coefficient glass-ceramics. The chemical composition of these two technical solutions does not contain SrO, and its crystallization tendency and forming difficulty are not clear. [0003] The existing heat treatment method for glass-ceramics with low expansion coefficient is mainly a two-step method. This method is mainly aimed at thin plates or small pieces of glass that require rapid heat treatment, and it is difficult to heat treat bulk materials. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a glass-ceramic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C3/097C03C10/14C03B32/02
CPCC03C3/097C03C10/00
Inventor 孙伟李启甲黄刚
Owner CDGM OPTICAL GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com