Composite polymerzation inhibitor for producing methyl propenoic acid and its ester

A compound polymerization inhibitor and methacrylic acid technology, which is applied in the preparation of carboxylic acid esters, the separation/purification of carboxylic acid compounds, the preparation of organic compounds, etc., can solve the problems of weak electron donating performance and reduced polymerization inhibition effect, and achieve Large synergistic effect, prevention of polymerization, and the effect of inhibiting oxidation ability

Active Publication Date: 2006-08-23
SHANGHAI HUAYI NEW MATERIAL
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the electron-donating properties of methacrylic acid and its esters are weaker than those of styrene, the polymerization inhibition effect is relatively reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0010] Under the conditions of no air and a temperature of 120 ° C, using MAA raw materials with a purity of 99.8%, 2,2,6,6-tetramethyl-4-hydroxypiperidine nitroxide radical compound (ZJ-705) or phosphorous acid -3-(2,2,6,6-tetramethyl-4-hydroxypiperidine nitroxide free radical) ester (ZJ-7056) and copper salt complex as a polymerization inhibitor, in a 50ml pear-shaped bottle The polymerization inhibition experiment was carried out by heating with silicone oil, and the results are shown in Table 1.

[0011]

Embodiment 5-6

[0013] Experimental condition is the same as embodiment 1. The raw material is the solvent phase of the methacrylic acid aqueous solution produced by the catalytic oxidation of tert-butanol or isobutene after solvent extraction (composition: 0.76% of water, 79.06% of toluene, 2.86% of acetic acid, 1.49% of acrylic acid, and 14.97% of methacrylic acid), and Add 300ppm of binary composite polymerization inhibitor, and use a small glass sieve plate tower to carry out continuous rectification and desolventization at the bottom temperature of the rectification tower at 94°C and a vacuum degree of 13kPa. The experimental results are shown in Table 2.

[0014]

Embodiment 7-10

[0016] Experimental condition is the same as embodiment 1. Methyl methacrylate with a content of 99.5% was used as a raw material, and a polymerization inhibition experiment was carried out in a 50 ml pear-shaped bottle by heating with silicone oil, and the results are shown in Table 3.

[0017]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a kind of composite polymerization inhibitor for the production process of methylacrylic acid and its ester. The composite polymerization inhibitor is re-compounded with nitrogen and oxygen free radical type compound and copper salt type polymerization inhibitor. The composite polymerization inhibitor has high polymerization inhibiting effect and no requirement on oxygen content in the material system.

Description

technical field [0001] The invention relates to a composite polymerization inhibitor developed for preventing the polymerization of materials (methacrylic acid and its esters) during the production process of methacrylic acid and its esters. Background technique [0002] During the production (such as esterification, rectification or extraction) and storage and transportation of methacrylic acid (MAA) and its esters, due to the unsaturated carbon-carbon double bonds and carboxyl groups or esters in the molecular structure of methacrylic acid and its esters The base has extremely strong polymerization characteristics and is very easy to undergo polymerization reactions. Once polymerization occurs (sometimes implosion occurs, causing the entire material to condense into a block), it will not only cause production stoppage, but even cause damage to the entire equipment. Therefore, preventing the polymerization of MAA and its esters is very critical and is an important link in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C51/50C07C57/04C07C67/62C07C69/54
Inventor 马建学刘书举张庆怀罗明陨汪青海邵敬铭
Owner SHANGHAI HUAYI NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com