Optical composite sheet and display apparatus comprising same
A technology of optical composite sheets and light sources, applied in optics, optical components, nonlinear optics, etc., to achieve the effects of reducing color deviation, enhancing optical performance, and enhancing performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1-1
[0195] (A) In order to prepare the composition for the light absorbing layer, 0.05 parts by weight of a light absorber (PANAX NEC 584, Ukseung Chemical) and 1.0 parts by weight of a UV blocking agent (Tinuvin TM 928, BASF) was added to 100 parts by weight of the solution, which was mixed with acrylic binder resin (AOF-2914, Aekyung) and propylene glycol methyl ether (PGME) at a weight ratio of 30:70.
[0196] (B) A UV-curable resin was coated on one side of a base film (PET) having a thickness of 100 μm to form a prism pattern about 40 μm thick, thereby preparing a lower prism sheet. The composition for the light-absorbing layer was coated on the other side of the base film using a Mayer rod, dried and cured to form a 3 μm thick light-absorbing layer. A composition in which 15 parts by weight of polybutylmethacrylate (PBMA) beads, 35 parts by weight of urethane acrylic resin, and 50 parts by weight of methyl ethyl ketone (MEK) were mixed as a solvent was prepared. It was coa...
Embodiment 1-2
[0200] Repeat the steps of Example 1-1 to obtain the final optical composite sheet, provided that the other side of the lower prism sheet base film does not form a light-absorbing layer in step (B); but in step (C), on the upper prism sheet The other side of the light-absorbing layer forms a light-absorbing layer, and the surface of the light-absorbing layer is coated with an adhesive resin, which adheres to the lower prism sheet (see Figure 5a ).
Embodiment 2-1
[0206] Repeat steps (A)-(C) of Example 1-1 to obtain a composite sheet.
[0207] (D) A UV-curable adhesive resin was coated in a thickness of 0.5 to 1.0 μm on one side of a buffer film (PET) having a thickness of 100 μm. It is adhered to a pre-prepared composite sheet and UV cured.
[0208] (E) A composition in which 15 parts by weight of polymethylmethacrylate (PMMA) beads, 35 parts by weight of an acrylic binder resin, and 50 parts by weight of methyl ethyl ketone (MEK) were mixed as a solvent was prepared. The composition was coated on one side of a double brightness enhancement film (DBEF, Qv2, 3M) with a thickness of 95 μm, and dried to form an upper light diffusion layer with a thickness of 10 μm. The other side of the dual brightness enhancing film was coated with a UV curable adhesive resin to a thickness of 10 μm using a Mayer rod. It is adhered to the buffer film surface of the composite sheet prepared in the above-mentioned steps (D) and carried out UV curing to o...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
absorption wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com