NBRrubbermaterial with low compression set and preparation process thereof

A permanent deformation, low compression technology, applied in the field of rubber seals, can solve the problems of compression permanent deformation performance and comprehensive performance need to be improved, reduce compression permanent deformation rate and other problems, achieve strong adhesion, improve compression permanent deformation, heat resistance and other problems. good effect

Active Publication Date: 2022-01-04
南阳天一密封股份有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above two nitrile rubbers reduce the compression set rate to a certain extent, but the compression set performance and comprehensive performance need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • NBRrubbermaterial with low compression set and preparation process thereof
  • NBRrubbermaterial with low compression set and preparation process thereof
  • NBRrubbermaterial with low compression set and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032]In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions of the embodiments of the present invention are clearly and completely described below. Apparently, the described embodiments are some, not all, embodiments of the present invention. All other embodiments obtained by those skilled in the art based on the described embodiments of the present invention belong to the protection scope of the present invention.

[0033] A low compression set NBR rubber compound, made of the following raw materials in mass fraction: 44.15-44.75% of rubber body, 1.11-2.43% of vulcanizing agent, 1.32-1.34% of vulcanization auxiliary agent, 0.88-0.89% of protective agent, reinforcement Agent 48.57-49.22%, activator 2.65-2.70%.

[0034] The rubber main body is NBR-40 rubber and NBR-28 rubber; the weight ratio of the two is: NBR-40 rubber:NBR-28 rubber is 4:1.

[0035] Described vulcanizing agent is: 1,3-tw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an NBR rubber material with low compression set and a preparation process thereof, belonging to the technical field of rubber sealing elements. The NBR rubber material is prepared from the following raw materials by mass: 44.15-44.75% of a main rubber body, 1.11-2.43% of a vulcanizing agent, 1.32-1.34% of a vulcanizing aid, 0.88-0.89% of a protective agent, 48.57-49.22% of a reinforcing agent, and 2.65-2.70% of an activator. According to the invention, NBR rubber and various assistants are reasonably selected, so the compression set performance of the rubber material is improved, and the prepared product meets environmental protection requirements; product quality cost is controlled to be within a reasonable range; and through adjustment, the tensile strength of the NBR rubber material is not less than 10 Mpa, a compression set test shows that a compression set rate does not exceed 20% under the conditions of compression of 25% and 150 DEG C * 70 h in ASTM 903, and comprehensive performance is good.

Description

technical field [0001] The invention relates to the technical field of rubber seals, in particular to a low compression set NBR rubber compound and a preparation process thereof. Background technique [0002] Rubber products are used to prevent the fluid medium from leaking from the sealed device, and also prevent external dust, sand and air (for vacuum) from entering the inside of the sealed device. Although this type of seal is small, it plays an important role in ensuring the performance of various devices and facilities, saving materials and energy, and preventing environmental pollution. It is widely used in various machinery, instruments, pipelines, household appliances, vehicles and other transportation tools, and the construction industry, etc. Rubber sealing products will produce permanent deformation under the joint action of mechanical force, medium, oxygen and temperature, which will eventually lead to seal failure. Therefore, the compression permanent deformati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L25/12C08K13/04C08K3/04C08K7/26C08K5/14C08K3/06C08K5/47C08K5/40C08K5/39C08K5/37C08K5/3437C08K3/22
CPCC08L9/02C08L2201/08C08L2205/025C08K2003/2296C08L25/12C08K13/04C08K3/04C08K7/26C08K5/14C08K3/06C08K5/47C08K5/40C08K5/39C08K5/378C08K5/3437C08K3/22Y02T10/86
Inventor 樊红星马雷王铁忠刘元英王晓博朱建波李蕾曹正理
Owner 南阳天一密封股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com