Terbium metal complex constructed by furantetracarboxylic acid and preparation method thereof

A technology of metal complexes and furan tetraacid, applied in the direction of 3/13 group organic compounds without C-metal bonds, compounds containing periodic table group 3/13 elements, chemical instruments and methods, etc.

Inactive Publication Date: 2021-04-23
TIANJIN POLYTECHNIC UNIV
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are few researches on rare earth metal complexes with furan tetraacid as the ligand, so there is a lot of room for development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Terbium metal complex constructed by furantetracarboxylic acid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The synthesis of embodiment 1 complex:

[0014] TbCl 3 ·6H 2 O (0.0373g, 0.1mmol) and K 4 fta (0.0400g, 0.1mmol) was dissolved in 8mL of distilled water, and 1 drop of concentrated hydrochloric acid was added dropwise. After stirring evenly, the mixed solution was transferred to a 10ml polytetrafluoroethylene lining, put into the reaction kettle and placed in an oven. , react at 160°C for 2 days, cool down for 1 day, and obtain the target product after the reaction is completed. Potassium salt of furan tetraacid and TbCl 3 ·6H 2 The mass ratio of O is: 1:0.93.

Embodiment 2

[0015] The infrared spectrometry of embodiment 2 complexes:

[0016] The infrared spectrum of the complex was determined by the KBr tablet method, with a Nicolet330 FT-IR infrared spectrometer at 4000-500cm -1 Recorded within the range, see the specific peak value figure 1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a terbium metal complex constructed by furantetracarboxylic acid and a preparation method thereof. The chemical composition of the complex contains a furantetracarboxylic acid (H4fa) ligand. The synthesis scheme comprises the following steps of: respectively dissolving potassium salt of furantetracarboxylic acid and TbCl3.6H2O in distilled water according to a stoichiometric ratio, mixing, and adding 1d HCl; and putting the obtained solution into a polytetrafluoroethylene lining, then putting the polytetrafluoroethylene lining into a reaction kettle, putting the reaction kettle into a drying oven, and carrying out heating reaction for 3 days to obtain a target product. The mass ratio of the potassium salt of the furantetracarboxylic acid to the TbCl3.6H2O is 1: 0.93.

Description

technical field [0001] The invention relates to a terbium metal complex constructed by furan tetraacid and a preparation method thereof, belonging to the field of metal complex science and technology. [0002] technical background [0003] Metal-organic complex materials constructed by metal ions and organic ligands have broad application prospects in the fields of gas storage, optoelectronic materials, magnetic materials, and catalysis due to their diverse structures and unique properties. Compared with the d-group transition metal organic complexes and the main group metal organic complexes, the properties of the rare earth metal organic complexes are significantly different. This is because the rare earth metal ions have the characteristics of large radius and high coordination number, which are more conducive to Coordination and activation of compounds. The 4f orbital does not participate in bond formation due to the strong shielding effect, and the 18-electron rule of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F5/00
CPCC07F5/003
Inventor 夏军李温馨
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com