A method for eliminating short process to produce 1.175mm high-strength steel coiled oval coil

A high-strength steel, short-process technology, applied in the direction of manufacturing tools, tension/pressure control, metal rolling, etc., can solve problems affecting production efficiency, product degradation or scrapping, increasing manpower and material resources, etc., to achieve the elimination of oval The effect of shape roll defects, promotion of tissue phase transformation, and simple and easy method

Active Publication Date: 2022-07-15
武汉钢铁有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The elliptical steel coil needs to take certain measures to be equipped with the leveling unit, such as artificial flame cutting of the inner ring of the steel coil to expand the inner diameter, which will increase extra manpower, material resources, and increase production costs, seriously affecting production efficiency and product quality Rate
At the same time, the circumferential speed of the steel coil with large ellipticity is inconsistent during the unleveling process, and the tension fluctuates violently, which may easily cause scratches on the surface of the steel coil, which will eventually affect the use of the user, resulting in product degradation or rejection, resulting in large economic losses; serious ellipse The steel coils cannot be finished even if the internal control is manually expanded. They can only be scrapped.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for eliminating short process to produce 1.175mm high-strength steel coiled oval coil
  • A method for eliminating short process to produce 1.175mm high-strength steel coiled oval coil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] WJX750-NH was produced on December 4, 2018, size: 1.175mm*1115mm.

[0032] control process method unit Specific parameters Strip unit tension N / mm 2

[0033] Effect: 20 coils of steel were produced, totaling 308.35 tons, and the non-elliptical rate of coils was 100%.

example 2

[0034] Example 2: WJX750-NH was produced on December 10, 2018, June 7, 2019, and June 12, 2019, size: 1.175mm*1175mm.

[0035] control process method unit Specific parameters Strip unit tension N / mm 2

[0036] Effect: 30 coils of steel were produced, totaling 531.68 tons, and the non-oval rate of coils was 100%.

Embodiment 3

[0038] On March 30, 2019, and April 10, 2019, WJX750-NH was produced. Size specification: 1.175mm*1195mm.

[0039]

[0040]

[0041] Effect: 24 coils of steel were produced, totaling 378.94 tons, and the non-oval rate of coils was 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing 1.175mm high-strength steel coiling elliptical coils by eliminating short process flow. The method includes controlling the strip steel unit tension, reducing the pinch roller pressure, adjusting the coil diameter tension, and adjusting the tension during the strip steel coiling process. distribution, and clockwise rotation after the coil stays after coiling. The invention can eliminate the short-flow production of 1.175mm high-strength steel coiled oval coils.

Description

technical field [0001] The invention belongs to the technical field of hot-rolled sheet and strip manufacturing, and in particular relates to a method for producing 1.175mm high-strength steel WJX750-NH coiled elliptical coils by eliminating short processes. Background technique [0002] The process flow of high-strength steel developed by WISCO Thin Slab Continuous Casting and Rolling CSP is: desulfurization → converter → argon blowing → ladle furnace → vacuum furnace → continuous casting → soaking furnace → finishing rolling → layer cooling → coiling → packing → smoothing →Weighing→Outgoing. [0003] When using the above process flow to produce 1.175mm high-strength steel WJX750-NH, the phenomenon of steel coil oval coil is prone to occur. The oval shape of the steel coil means that after the steel coil is pulled out from the reel of the coiler, the gravity of the steel coil will be completely borne by the steel coil itself, and the steel coil presents an oval shape under...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B15/00B21B37/48
CPCB21B15/00B21B37/48B21B2015/0057
Inventor 田军利余晓龙高智宋义纯张兴涛王成
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products