A high-strength, low-rebound fire-resistant spray coating and its preparation method

A low-rebound and paint-spraying technology, applied in the field of refractory materials, can solve the problems of high rebound rate and low strength, and achieve the effects of low rebound rate, good construction performance and increased fineness

Active Publication Date: 2022-04-19
HENAN HONGDA FURNACE IND
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is: in order to solve the problems of low strength and high rebound rate of the existing lightweight spray paint, the present invention provides a high-strength, low rebound fire-resistant spray paint and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength, low-rebound fire-resistant spray coating and its preparation method
  • A high-strength, low-rebound fire-resistant spray coating and its preparation method
  • A high-strength, low-rebound fire-resistant spray coating and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-strength, low-rebound fire-resistant spray coating, using the following raw materials and weight percentages: 35% coke gemstones, 20% porous mullite, 8% expanded vermiculite, 5% floating beads, 32% composite binder .

[0023] Burnt Gem Al 2 o 3 Content 40%, bulk density 2.32g / cm 3 , particle size 3 ~ 1.2mm.

[0024] Porous mullite Al 2 o 3 Content 40%, bulk density 1.2g / cm 3 , particle size 1.2 ~ 0.3mm.

[0025] Expanded vermiculite is calcined at 850-880°C, with a bulk density of 160kg / m 3 , Al 2 o 3 The content is 42%, and the particle size is less than 0.3mm.

[0026] Bead Al 2 o 3 Content 40%, SiO 2 Content 55%, Fe 2 o 3 Content 2.5%, R 2 The O content is 1.2%, and the particle size is less than 200 μm.

[0027] The composite binder uses 20% Portland cement, 30% CA-60 aluminate cement, 20% CA-80 aluminate cement, and 12% active SiO 2 Micropowder, 15% of 200 mesh raw pottery clay powder, 1.5% of NaOH, 1.5% of triethanolamine, adopt horizontal...

Embodiment 2

[0036] A high-strength, low-rebound fire-resistant spray coating, using the following raw materials and weight percentages: 30% coke gemstones, 25% porous mullite, 7% expanded vermiculite, 6% floating beads, 32% composite binder .

[0037] Burnt Gem Al 2 o 3 Content 36%, bulk density 2.35g / cm 3 , particle size 3 ~ 1.2mm.

[0038] Porous mullite Al 2 o 3 Content 36%, bulk density 1.15g / cm 3 , particle size 1.2 ~ 0.3mm.

[0039] Expanded vermiculite is calcined at 860-880°C, with a bulk density of 120kg / m 3 , Al 2 o 3 42%, the particle size is less than 0.3mm.

[0040] Bead Al 2 o 3 Content 35%, SiO 2 Content 60%, Fe 2 o 3 Content 3.5%, R 2 The O content is 1.2%, and the particle size is less than 200 μm.

[0041] The composite binder uses 25% Portland cement, 30% CA-60 aluminate cement, 20% CA-80 aluminate cement, and 8% active SiO 2 Micropowder, 15% of 200-mesh raw clay powder, 1.0% of NaOH, 1.0% of triethanolamine, was prepared by co-grinding with a horizont...

Embodiment 3

[0050] A high-strength, low-rebound fire-resistant spray coating, using the following raw materials and weight percentages: 33% coke gemstones, 23% porous mullite, 8% expanded vermiculite, 6% floating beads, 30% composite binder .

[0051] Burnt Gem Al 2 o 3 Content 38%, bulk density 2.31g / cm 3 , particle size 3 ~ 1.2mm.

[0052] Porous mullite Al 2 o 3 Content 38%, bulk density 1.18g / cm 3 , particle size 1.2 ~ 0.3mm.

[0053] Expanded vermiculite is calcined at 860-880°C, with a bulk density of 130kg / m 3 , Al 2 o 3 The content is 41%, and the particle size is less than 0.3mm.

[0054] Bead Al 2 o 3 Content 36%, SiO 2 Content 57%, Fe 2 o 3 Content 2.0%, R 2 The O content is 1.0%, and the particle size is less than 200 μm.

[0055] The composite binder uses 22% Portland cement, 31.6% CA-60 aluminate cement, 21% CA-80 aluminate cement, and 8% active SiO 2 Micropowder, 15% of 200 mesh raw pottery clay powder, 1.2% of NaOH, 1.2% of triethanolamine, was prepared b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength, low-rebound fire-resistant spray coating and a preparation method thereof, relates to the technical field of refractory materials, and solves the problems of low strength and high rebound rate of the existing light-weight spray coating. Porous mullite 20% to 25%, expanded vermiculite 6% to 8%, floating beads 5% to 6%, composite binder 28.5% to 32%, Portland cement, CA‑60 aluminate cement , CA‑80 aluminate cement, activated SiO 2 Micropowder, 200 mesh raw clay powder, NaOH and triethanolamine are used to make a composite binder by horizontal dry ball milling; then the composite binder is mixed with expanded vermiculite and floating beads using a planetary mixer; finally coke gemstones, porous mullite Stone is added and then planetary stirring to obtain the finished product; the compactness of the sprayed coating of the present invention is effectively enhanced, the adhesion and sintering property of the overall binder are good, the strength of the sprayed coating is high, and the rebound rate is low; when preparing, a horizontal dry ball mill and a planetary mixer are used three times. One-step mixing, high uniformity and activity of spray paint.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to a high-strength, low-rebound refractory spray coating and a preparation method thereof. Background technique [0002] Refractory spray coating is an unshaped refractory material constructed by mechanical spraying method using pneumatic tools. It is a bulk material made of clay clinker as raw material. Refractory spray coating is an important branch of unshaped refractory material. It has good high temperature performance and Construction performance, when applied to high-temperature industrial furnace lining, the construction efficiency is high, and the construction time can be effectively shortened. It is widely used in high-temperature industrial furnace refractory linings such as iron and steel metallurgy and building materials. [0003] Spray coatings are generally composed of aggregates, powders, binders and admixtures, and are constructed by dry or semi-dry met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
CPCC04B35/66C04B35/62222C04B2235/349C04B2235/3463C04B2235/36C04B2235/3427C04B2235/3222C04B2235/3418C04B2235/3201C04B2235/77C04B2235/9615C04B2235/96
Inventor 何贯通郭宏相李放万俊张群英石立光
Owner HENAN HONGDA FURNACE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com