A kind of preparation method of crepe fabric

A technology of fabrics and raw materials, applied in textiles, filament/thread forming, and patterned fabrics, etc., can solve the problems of elastic chiffon product quality and complex processing processes, and achieve easy control of processing technology, low processing costs, and high fiber quality. Guaranteed effect

Active Publication Date: 2021-10-19
JIANGSU HENGLI CHEM FIBER
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a method for preparing a wrinkled fabric, aiming to solve the problem that spandex in elastic chiffon in the prior art will be damaged during textile processing and daily use, which will affect the quality of elastic chiffon products and the processing process is complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of crepe fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A preparation method of wrinkled fabric, the steps are as follows:

[0051] (1) Preparation of crescent-shaped composite fiber: PET (intrinsic viscosity is 0.53dL / g) and PTT (intrinsic viscosity is 1.2dL / g) with a mass ratio of 50:50 are juxtaposed by FDY process and circular composite fiber (will The spinneret holes on the spinneret are changed from circular to crescent-shaped) to prepare crescent-shaped composite fibers; wherein, when preparing side-by-side composite fibers, PET melt and PTT melt are distributed from the same spinneret The spinneret m (crescent spinneret) and spinneret n (crescent spinneret) on the top are extruded;

[0052] The distribution refers to distributing the PTT melt through the distribution hole A, while distributing the PET melt through the distribution hole B to the spinneret m, distributing the PTT melt through the distribution hole C, and simultaneously distributing the PET melt through the distribution hole D To the spinneret hole n; ...

Embodiment 2

[0067] A preparation method of wrinkled fabric, the steps are as follows:

[0068] (1) Preparation of crescent-shaped composite fiber: PET (intrinsic viscosity is 0.52dL / g) and PTT (intrinsic viscosity is 1.1dL / g) with a mass ratio of 50:50 are juxtaposed by FDY process and circular composite fiber (will be The spinneret holes on the spinneret are changed from circular to crescent-shaped) to prepare crescent-shaped composite fibers; wherein, when preparing side-by-side composite fibers, PET melt and PTT melt are distributed from the same spinneret The spinneret m (crescent spinneret) and spinneret n (crescent spinneret) on the top are extruded;

[0069] The distribution refers to distributing the PTT melt through the distribution hole A, while distributing the PET melt through the distribution hole B to the spinneret m, distributing the PTT melt through the distribution hole C, and simultaneously distributing the PET melt through the distribution hole D To the spinneret hole ...

Embodiment 3

[0084] A preparation method of wrinkled fabric, the steps are as follows:

[0085] (1) Preparation of crescent-shaped composite fiber: PET (intrinsic viscosity is 0.56dL / g) and PTT (intrinsic viscosity is 1.11dL / g) with a mass ratio of 50:50 are juxtaposed by FDY process and circular composite fiber (will The spinneret holes on the spinneret are changed from circular to crescent-shaped) to prepare crescent-shaped composite fibers; wherein, when preparing side-by-side composite fibers, PET melt and PTT melt are distributed from the same spinneret The spinneret m (crescent spinneret) and spinneret n (crescent spinneret) on the top are extruded;

[0086] The distribution refers to distributing the PTT melt through the distribution hole A, while distributing the PET melt through the distribution hole B to the spinneret m, distributing the PTT melt through the distribution hole C, and simultaneously distributing the PET melt through the distribution hole D To the spinneret hole n;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
angleaaaaaaaaaa
Basis weightaaaaaaaaaa
Basis weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a wrinkled fabric. The crescent-shaped composite fiber is used as a crepe raw material, and the crescent-shaped composite fiber and cotton fiber are used as a crepe weft raw material, which is interwoven into a plain weave and then subjected to relaxation heat treatment to obtain a wrinkled fabric; The twist direction of the warp and crepe weft is opposite; the preparation process of the crescent-shaped composite fiber is as follows: in the process of preparing circular side-by-side composite fibers from PET and PTT according to the FDY process, the spinneret holes on the spinneret plate are changed from circular to Crescent shape, cooled by circular air blowing, and controlling the arrangement of spinneret holes to meet certain conditions, to obtain crescent-shaped composite fibers; when preparing side-by-side composite fibers, PET melt and PTT melt are distributed from the same spinneret The spinneret m and the spinneret n are extruded; the spinneret m and the spinneret n are crescent-shaped spinneret holes; the contact surface of PET melt and PTT melt flows in the guide holes of each spinneret hole parallel to each other. The invention adopts a simple method to prepare a wrinkled fabric with stable quality and easy processing.

Description

technical field [0001] The invention belongs to the technical field of textile fabrics and relates to a preparation method of wrinkled fabrics. Background technique [0002] Chiffon fabric is a very light and thin chemical fiber fabric, suitable for women's summer clothes, and it feels a little frizzy; generally it can be divided into silk chiffon and imitation silk chiffon. Fabrics vary greatly. The most common chiffon fabric is made of polyester filaments, because the chiffon made of polyester filaments is crisp, wear-resistant and can also be blended with other fiber materials to give chiffon more performance. , such as the use of spandex blending, the chiffon fabric has a certain degree of elasticity. When spandex is used to weave elastic chiffon, spandex will cause the molecular chains in the spandex molecular chain to break or slip during heat treatment and washing. The strength and elasticity of spandex Response decreases; and in the weaving, pre-treatment, printing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/47D03D15/37D03D15/292D03D15/217D03D15/49D03D15/56D03D21/00D01D5/30D01D5/253D01D5/23
CPCD03D15/00D03D21/00D01D5/23D01D5/253D01D5/30D03D15/46D03D15/47
Inventor 张元华尹立新黄金刚魏存宏
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com