Sound-absorbing and sound-insulation material and preparation method thereof

A sound insulation material and rubber technology, applied in the direction of film/flake adhesives, adhesives, etc., can solve the problems of affecting health status, high noise, etc., to improve uniformity, ensure sound absorption effect, increase toughness and stability. Effect

Inactive Publication Date: 2019-12-06
廊坊腾博保温材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] There are reports of porous sound-absorbing materials disclosed in the prior art, but the products on the market still have deficiencies in the sound-absorbing effect. Aiming at the problems existing in the prior art, the present invention provides a sound-absorbing material, which has sound insulation and sound-absorbing effects. , protect people affected by noise in entertainment places, factories, etc., and solve the problem that more and more noise affects people's health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A method for preparing a sound-absorbing and sound-insulating material, comprising the following:

[0041] 1) Take the raw materials of each component for later use, put 10 parts of rubber and 10 parts of PVC into the internal mixer for internal mixing, the temperature of the internal mixer is 115°C, and the internal mixing time is 10 minutes;

[0042] 2) Put the rubber and PVC mixed in step 1) in an open mill, add 18 parts of filler, 3 parts of carbon black, 17 parts of paraffin wax, 2 parts of chlorinated polyethylene, and 1 part of board wax in proportion , 1 part of soybean oil, 0.5 part of surfactant, and 0.5 part of calcium stearate were kneaded at a temperature of 120°C and the time for setting the glue was 5 minutes, and sliced;

[0043] 3) Put the chips obtained in step 2) into the twin-screw extruder, and control the temperature of each zone of the twin-screw extruder: Zone 1 125°C, Zone 2 140°C, Zone 3 160°C, Zone 4 170°C, Zone 5 170°C , 180°C in the sixth z...

Embodiment 2

[0046] A method for preparing a sound-absorbing and sound-insulating material, comprising the following:

[0047] 1) Take the raw materials of each component for later use, put 12 parts of rubber and 10 parts of PVC into the internal mixer for internal mixing, the temperature of the internal mixer is 118°C, and the internal mixing time is 13 minutes;

[0048] 2) Put the rubber and PVC after internal mixing in step 1) in an open mill, add 20 parts of filler, 4 parts of carbon black, 19 parts of paraffin wax, 3 parts of chlorinated polyethylene, and 2 parts of board wax in proportion , 2 parts of soybean oil, 1 part of surfactant, and 1 part of calcium stearate were kneaded at a temperature of 120°C, and the time for setting the glue was 6 minutes, and sliced;

[0049] 3) Put the chips obtained in step 2) into the twin-screw extruder, and control the temperature of each zone of the twin-screw extruder: 130°C in the first zone, 143°C in the second zone, 165°C in the third zone, 1...

Embodiment 3

[0052] A method for preparing a sound-absorbing and sound-insulating material, comprising the following:

[0053] 1) Take the raw materials of each component for later use, put 15 parts of rubber and 15 parts of PVC into the internal mixer for internal mixing, the temperature of the internal mixer is 125°C, and the internal mixing time is 15 minutes;

[0054] 2) Put the rubber and PVC after internal mixing in step 1) in an open mill, add 24 parts of filler, 7 parts of carbon black, 22 parts of paraffin wax, 5 parts of chlorinated polyethylene, and 5 parts of board wax in proportion , 4 parts of soybean oil, 3 parts of surfactant, and 4 parts of calcium stearate were kneaded at a temperature of 125°C and the time for setting the glue was 8 minutes, and sliced;

[0055] 3) Put the chips obtained in step 2) into the twin-screw extruder, and control the temperature of each zone of the twin-screw extruder: Zone 1 135°C, Zone 2 155°C, Zone 3 170°C, Zone 4 175°C, Zone 5 180°C , 185°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
elongation at breakaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a sound-absorbing and sound-insulation material. The sound-absorbing and sound-insulation material comprises the following components in parts by weight: 10-15 parts of rubber,10-15 parts of PVC, 10-15 parts of a foaming agent, 18-24 parts of a filler, 3-7 parts of carbon black, 17-22 parts of paraffin, 2-5 parts of chlorinated polyethylene, 1-5 parts of slab beeswax, 1-4 parts of soybean oil, 0.5-3 parts of a surfactant and 0.5-4 parts of calcium stearate. By adding a mixed material comprising the PVC, the rubber and the foaming agent, and optimizing the usage amountsof the components, the purpose that the prepared material has large and small holes can be effectively achieved; and the overall sound-absorbing performance of the sound-absorbing material is effectively ensured.

Description

technical field [0001] The invention belongs to the technical field of noise-reducing materials, and in particular relates to a sound-absorbing and sound-insulating material and a method for preparing the sound-absorbing and sound-insulating material. [0002] technical background [0003] In today's society, various high-speed vehicles, industrial equipment, construction machinery, household appliances and audio equipment are widely used, resulting in increasingly serious noise pollution in our living environment. It will not only affect people's normal work, study and life, but also harmful People's physical and mental health will also affect the normal operation and service life of some precision instruments and equipment, so noise pollution is one of the four major public hazards that we urgently need to solve. [0004] We all know that sound is caused by the vibration of objects. From a physical point of view, noise refers to the sound produced by an object doing a seri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/06C08L27/06C08L9/00C08L9/06C08L83/04C08L23/28C08K3/04C08K5/098C08J9/10C08J9/30C09J7/26
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/103C08J9/105C08J9/30C08J2203/04C08J2391/06C08J2409/00C08J2409/06C08J2423/28C08J2427/06C08J2483/04C08K3/04C08K5/098C09J7/26
Inventor 王宝靓
Owner 廊坊腾博保温材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap