A kind of antibacterial light textile fabric and preparation method thereof

A kind of textile fabric and light technology, applied in the field of textile fabrics, can solve the problem that the fabric cannot meet the health, antibacterial, intelligent temperature and comfort of the fabric at the same time, and achieves good temperature regulation and anti-ultraviolet and far-infrared effects. Antibacterial effect

Active Publication Date: 2022-05-27
JIANGSU DAMAONIU NEW MATERIAL TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fabrics obtained by these preparation methods cannot meet people's needs for health care, antibacterial properties, intelligent temperature regulation and comfort of fabrics at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial light textile fabric and preparation method thereof
  • A kind of antibacterial light textile fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Embodiment 1 provides an antibacterial lightweight textile fabric, and the antibacterial lightweight textile fabric is woven from antibacterial temperature-regulating aerogel fibers.

[0061] The preparation method of the antibacterial temperature-adjusting aerogel fiber is as follows: polyester chips are melted to obtain polyester spinning solution, and then modified aerogel and negative ion temperature-adjusting material are added to the spinning solution, wherein the polyester spinning solution, The mass ratio of the modified aerogel and the negative ion temperature-adjusting material is 1:0.2:0.12, and the mixture is uniform; then it is sprayed out through the spinneret, and then the fiber is formed, the primary fiber is drawn and oriented, and the fiber is heat-set and wound. Antibacterial temperature-adjusting aerogel fibers were obtained.

[0062] The preparation method of the modified aerogel is as follows: at 0 to 4° C., a silver nitrate solution with a concent...

Embodiment 2

[0076] The difference between embodiment 2 and embodiment 1 is:

[0077] The preparation method of the antibacterial temperature-adjusting aerogel fiber is as follows: polyester chips are melted to obtain polyester spinning solution, and then modified aerogel and negative ion temperature-adjusting material are added to the spinning solution, wherein the polyester spinning solution, The mass ratio of the modified aerogel and the negative ion temperature-adjusting material is 1:0.23:0.15, and the mixture is uniform; then it is sprayed out through the spinneret hole, and then subjected to fiber forming, primary fiber drawing and orientation, fiber heat-setting and winding to make the product. Antibacterial temperature-adjusting aerogel fibers were obtained.

[0078] The preparation method of the modified aerogel is as follows: at 0 to 4° C., a silver nitrate solution with a concentration of 2.3 g / L is added to a chlorogenic acid solution with a concentration of 3.8 g / L, and the s...

Embodiment 3

[0080] The difference between Example 3 and Example 1 is:

[0081]The preparation method of the antibacterial temperature-adjusting aerogel fiber is as follows: polyester chips are melted to obtain polyester spinning solution, and then modified aerogel and negative ion temperature-adjusting material are added to the spinning solution, wherein the polyester spinning solution, The mass ratio of the modified aerogel and the negative ion temperature-adjusting material is 1:0.18:0.09, and the mixture is uniform; then it is sprayed out through the spinneret, and then through fiber forming, primary fiber drawing orientation, fiber heat-setting and winding, the system is prepared. Antibacterial temperature-adjusting aerogel fibers were obtained.

[0082] The preparation method of the modified aerogel is as follows: at 0 to 4° C., a silver nitrate solution with a concentration of 2.3 g / L is added to a chlorogenic acid solution with a concentration of 3.8 g / L, and the sol is added immed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of textile fabrics, in particular to an antibacterial light textile fabric and a preparation method thereof. The antibacterial lightweight textile fabric is woven from antibacterial temperature-regulating airgel fibers, and the preparation method of the antibacterial temperature-regulating airgel fibers is as follows: polyester chips are melted to obtain polyester spinning solution, and then the modified airgel 1. The negative ion temperature-regulating material is added to the spinning solution, mixed evenly, sprayed out through the spinneret hole, and then through fiber forming, primary fiber drafting orientation, fiber heat setting and winding, to obtain antibacterial temperature-regulating airgel fiber. The antibacterial and lightweight textile fabric prepared by the present invention has simple structure, reasonable raw material preparation, soft and smooth texture, has the function of intelligent temperature control, and can freely adjust the internal temperature of the fabric within a certain temperature range according to the change of the external environment temperature, and also has Durable antibacterial performance, has great application value.

Description

technical field [0001] The invention belongs to the field of textile fabrics, and more particularly, the invention relates to an antibacterial lightweight textile fabric and a preparation method thereof. Background technique [0002] With the update and iteration of the times, people's demand for the health and comfort of textile fabrics is increasing. In order to meet people's pursuit of these high-performance textiles, the improvement and optimization of textile fabrics has become a hot competition in the textile fabric industry. [0003] In the prior art, the effect of keeping warm is achieved by adding aerogel particles into the traditional thermal insulation material or by adding a gel thermal insulation layer in the fabric. performance is optimized. However, the fabrics obtained by these preparation methods cannot simultaneously meet people's needs for health care, antibacterial properties, intelligent temperature adjustment and comfort of fabrics. SUMMARY OF THE IN...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G18/76C08G18/66C08G18/48C08G18/32C08G18/10
CPCD01F6/92D01F1/103D01F1/10C08G18/7614C08G18/4854C08G18/3206C08G18/10
Inventor 白朋
Owner JIANGSU DAMAONIU NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com