Preparation method of non-surface glazed ceramic tile with concave convex color changing metal effect and ceramic tile

A technology for color-changing metal and ceramic tiles, applied in the field of ceramic tiles and their preparation, can solve the problems of high production cost, unsatisfactory color development effect of ceramic tiles, single pattern, etc., and achieve the effect of improving ornamental quality

Inactive Publication Date: 2019-10-08
FOSHAN OCEANO CERAMICS
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies of the prior art above, the purpose of the present invention is to provide a method for preparing a glazed ceramic tile with a concave-convex color-changing metal effect and ceramic tiles, aiming at solving the problem of high production costs and single patterns of ceramic tiles with a concave-convex effect in the prior art. etc., as well as the technical problem of the unsatisfactory coloring effect of metal coloring effect tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for preparing a non-glazed tile with a concave-convex discoloration metal effect, comprising the following steps:

[0036] Using the method for preparing ceramic tile bodies in the prior art to prepare ceramic tiles, and remove excess water;

[0037] Mix the frit, white latex water and water in a ratio of 1:4:3 at room temperature to make dry pellets; then put the dry pellets into the high-pressure glaze spray cabinet, set the high-pressure spray glaze cabinet The working pressure is 5.5MPa, and the dry pellets are evenly sprayed on the surface of the brick by using a high-pressure spray glaze cabinet, and the amount of cloth is 500-518g / m 2 ;

[0038] Put the sprayed brick adobe into the kiln, fire at 1200°C for 60 minutes, and cool to get the finished product.

[0039] Wherein, the frit includes the following components by mass percentage: 50% of silicon oxide, 5% of aluminum oxide, 6% of calcium oxide, 0.8% of magnesium oxide, 5% of potassium oxide, 2% of ...

Embodiment 2

[0042] A method for preparing a non-glazed tile with a concave-convex discoloration metal effect, comprising the following steps:

[0043]Using the method for preparing ceramic tile bodies in the prior art to prepare ceramic tiles, and remove excess water;

[0044] Mix the frit, white latex water and water in a ratio of 1:4:4 at room temperature to make dry pellets; then put the dry pellets into the high-pressure glaze spray cabinet, set the high-pressure spray glaze cabinet The working pressure is 5.2MPa, and the dry pellets are evenly sprayed on the surface of the bricks by using a high-pressure spray glaze cabinet, and the amount of cloth is 500-518g / m 2 ;

[0045] Put the sprayed adobe into a kiln, fire at 1190°C for 65 minutes, and cool to obtain the finished product.

[0046] Wherein, the frit includes the following components by mass percentage: silicon oxide 55%, aluminum oxide 6%, calcium oxide 5%, magnesium oxide 0.1%, potassium oxide 3%, sodium oxide 1%, zinc oxid...

Embodiment 3

[0049] A method for preparing a non-glazed tile with a concave-convex discoloration metal effect, comprising the following steps:

[0050] Using the method for preparing ceramic tile bodies in the prior art to prepare ceramic tiles, and remove excess water;

[0051] Mix the frit, white latex and water in a ratio of 1:5:5 at room temperature to make dry pellets; then put the dry pellets into the high-pressure glaze spray cabinet, set the high-pressure spray glaze cabinet The working pressure is 5.3MPa, and the dry pellets are evenly sprayed on the surface of the bricks by using a high-pressure spray glaze cabinet, and the amount of cloth is 500-518g / m 2 ;

[0052] The sprayed brick adobe is put into the kiln, fired at 1220°C for 70 minutes, and cooled to obtain the finished product.

[0053] Wherein, the frit includes the following components by mass percentage: silicon oxide 58%, aluminum oxide 5.5%, calcium oxide 3%, magnesium oxide 2%, potassium oxide 6%, sodium oxide 1.2%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a non-surface glazed ceramic tile with concave convex color changing metal effect and the ceramic tile. The preparation method comprises the steps thatvarious metal powder is added into a frit, firstly the frit is mixed with white milk glue and water in a mass ratio of 1 to 4-5 to 3-5, and then is sprayed on the surface of a brick, the frit is burntto form the uneven effect on the surface of the ceramic tile, the various metal powder cannot be settled in the process of spraying and burning, under the illumination of different lights, various color emitting effects are presented, the ornamental of the ceramic tile is improved, and the production process of the ceramic tile with the concave convex effect on the surface is simplified.

Description

technical field [0001] The invention relates to the technical field of ceramic tiles and their preparation, in particular to a method for preparing glazed ceramic tiles with a discoloration effect and the ceramic tiles. Background technique [0002] With the development of the economy and the improvement of living standards, people pay more and more attention to the aesthetics of products while pursuing the practicality of products, and the requirements for the aesthetics of products are increasing day by day. At present, tiles with concave-convex decorative effects are generally made by moulding, and then glazed; but this method is costly, has a single effect, and is difficult to adjust the pattern. In addition, ceramic tiles with concavo-convex effects are prepared by means of screen, roller, glaze, frit, etc.; this method has high production costs, single pattern, and low stability; The pursuit of innovative art. [0003] Distributing different metal powders on the surf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/12C03C8/20C03C8/18C04B41/86
CPCC03C8/12C03C8/18C03C8/20C04B41/5022C04B41/86C04B41/4545C04B41/4521C04B41/0072
Inventor 匡木庆刘俊荣
Owner FOSHAN OCEANO CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products