A technology of water-based polymers and dispersants, applied in applications, coatings, inks, etc., can solve the problems of low polarity on the surface of pigments and ink particles, partial solid content in products, and impact on product quality, and achieve hydrophilicity and Moderate proportion of hydrophobicity, good stretching, and quality-improving effect

Inactive Publication Date: 2019-06-21
NANTONG HANTAI CHEM
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of industry and people's living standards, the application of pigments and inks is becoming more and more extensive. Due to the low polarity of the surface of pigments and ink particles, it is not easy to disperse stably in the water medium, which leads to the problem of solid content in the product and the generation of particles. Therefore, people adopt dispersants to improve the dispersion performance of pigments and printing inks, but the general dispersion performance of dispersants on the market is relatively weak, which affects the quality of products. Drawbacks of Dispersants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A water-based polymer dispersant, the water-based polymer dispersant includes acrylic acid, styrene-butadiene copolymer, strong oxidizing agent, pH value adjustment agent and initiator; the mole of described acrylic acid and styrene-butadiene copolymer The mass ratio is 1:1; the strong oxidizing agent is potassium permanganate solution; the pH adjusting agent is ammonia water.

[0013] A water-based polymer dispersant, comprising preparing a water-based polymer dispersant described in this embodiment, the method may further comprise the steps:

[0014] S1, select corresponding acrylic acid and styrene-butadiene copolymer according to the molar mass ratio 1:1 of acrylic acid and styrene-butadiene copolymer;

[0015] S2, put the selected acrylic acid and styrene butadiene copolymer into mixing equipment and stir and mix, and dropwise add potassium permanganate solution while stirring, so that acrylic acid and styrene butadiene copolymer fully react, and the reaction tempe...

Embodiment 2

[0019] A water-based polymer dispersant, the water-based polymer dispersant includes acrylic acid, styrene-butadiene copolymer, strong oxidizing agent, pH value adjustment agent and initiator; the mole of described acrylic acid and styrene-butadiene copolymer The mass ratio is 1:1; the strong oxidizing agent is potassium permanganate solution; the pH adjusting agent is ammonia water.

[0020] A water-based polymer dispersant, comprising preparing a water-based polymer dispersant described in this embodiment, the method may further comprise the steps:

[0021] S1, select corresponding acrylic acid and styrene-butadiene copolymer according to the molar mass ratio 1:1 of acrylic acid and styrene-butadiene copolymer;

[0022] S2, put the selected acrylic acid and styrene butadiene copolymer into mixing equipment and stir and mix, and dropwise add potassium permanganate solution while stirring, so that acrylic acid and styrene butadiene copolymer fully react, and the reaction tempe...

Embodiment 3

[0026] A water-based polymer dispersant, the water-based polymer dispersant includes acrylic acid, styrene-butadiene copolymer, strong oxidizing agent, pH value adjustment agent and initiator; the mole of described acrylic acid and styrene-butadiene copolymer The mass ratio is 1:1; the strong oxidizing agent is potassium permanganate solution; the pH adjusting agent is ammonia water.

[0027] A water-based polymer dispersant, comprising preparing a water-based polymer dispersant described in this embodiment, the method may further comprise the steps:

[0028] S1, select corresponding acrylic acid and styrene-butadiene copolymer according to the molar mass ratio 1:1 of acrylic acid and styrene-butadiene copolymer;

[0029] S2, put the selected acrylic acid and styrene-butadiene copolymer into the mixing equipment to stir and mix, and dropwise add potassium permanganate solution while stirring, so that acrylic acid and styrene-butadiene copolymer fully react, and the reaction te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous polymer dispersant, and belongs to the field of polymer materials. The aqueous polymer dispersant is mainly formed by acrylic acid, a styrene-butadiene copolymer, astrong oxidant, a pH value blender and an initiating agent. In the aqueous polymer dispersant, a benzene ring of the styrene-butadiene copolymer is firmly bonded with an aromatic ring in a pigment molecule, so that the aqueous polymer dispersant is not separated from the surface of pigment easily; the proportion of hydrophilcity and hydrophobicity is moderate, so that the aqueous polymer dispersant can be well spread in water and is relatively strong in binding force with paint, therefore, the dispersing capacity of the aqueous polymer dispersant is relatively high, the dispersing performancesof the pigment and printing ink can be effectively improved, and the product quality is improved.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a water-based polymer dispersant. Background technique [0002] With the improvement of industry and people's living standards, the application of pigments and inks is becoming more and more extensive. Due to the low polarity of the surface of pigments and ink particles, it is not easy to disperse stably in the water medium, which leads to the problem of solid content in the product and the generation of particles. Therefore, people adopt dispersants to improve the dispersion performance of pigments and printing inks, but the general dispersion performance of dispersants on the market is relatively weak, which affects the quality of products. Deficiencies of dispersants. Contents of the invention [0003] The object of the present invention is to provide a water-based polymer dispersant to solve the problems raised in the above-mentioned background techno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F257/02C08F220/06C09D7/65C09D11/03
Inventor 杨伦张方志严存安赵飞吉让力陈其华
Owner NANTONG HANTAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap