Porous ceramic material, porous ceramic and preparation method thereof

A technology of porous ceramics and ceramic layers, applied in the field of porous ceramic materials, porous ceramics and their preparation, can solve problems such as poor distribution of pores, small amount of smoke, and affecting experience, so as to improve experience and increase atomization rate , Reduce the effect of uneven atomization or damage

Active Publication Date: 2019-05-07
DONGGUAN XINBO STRUCTURAL CERAMICS CO LTD
View PDF15 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current distribution of pores in porous ceramics is not good, and the amount of smoke generated is not large, which affects the overall experience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous ceramic material, porous ceramic and preparation method thereof
  • Porous ceramic material, porous ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The present invention also provides a preparation method of the above-mentioned porous ceramics, comprising the following steps:

[0043] S100: Prepare ceramic powder, each ceramic powder includes the following components in mass percentage: 50%-75% of alumina, 15%-40% of silicon dioxide and 5%-10% of pore-forming agent;

[0044] The organic slurry is prepared, and each organic slurry includes the following components in mass percentage: 65%-95% of solvent, 0.5%-15% of dispersant and 5%-20% of binder.

[0045]S110: Mix several parts of ceramic powder and several parts of organic slurry according to 40%wt-70%wt of ceramic powder and 30%wt-60%wt of organic slurry one by one, and put them into different ball mills for ball milling, Or put them into the same ball mill for ball milling at different time periods to obtain several uniformly dispersed casting slurries, so that the D50 particle size of the alumina in each casting slurry is different.

[0046] In one embodiment,...

Embodiment 1

[0059] The porous ceramic of this embodiment includes two layers of ceramic layers, the two layers of ceramic layers are respectively the first ceramic layer and the second ceramic layer, both of the first ceramic layer and the second ceramic layer have pores, the first ceramic layer is the bottom layer, and the second ceramic layer The ceramic layer is the top layer, and the pore diameter of the first ceramic layer is smaller than the pore diameter of the second ceramic layer.

[0060] The preparation method of above-mentioned porous ceramics comprises the following steps:

[0061] S100: preparing ceramic powder

[0062] The ceramic powder of the first ceramic layer includes the following components in mass percentage: 68% of alumina, 22% of silicon dioxide and 10% of pore-forming agent;

[0063] The ceramic powder of the second ceramic layer includes the following components in mass percentage: 50% of alumina, 40% of silicon dioxide and 10% of pore-forming agent.

[0064] ...

Embodiment 2

[0079] The porous ceramic of this embodiment includes four layers of ceramic layers, the four layers of ceramic layers are respectively the first ceramic layer, the second ceramic layer, the third ceramic layer and the fourth ceramic layer, the first ceramic layer, the second ceramic layer, the third ceramic layer Both the ceramic layer and the fourth ceramic layer have pores, the first ceramic layer is the bottom layer, the fourth ceramic layer is the top layer, the pore diameter of the first ceramic layer<the pore diameter of the second ceramic layer<the pore diameter of the third ceramic layer The pore diameter<the pore diameter of the pores of the fourth ceramic layer.

[0080] The preparation method of above-mentioned porous ceramics comprises the following steps:

[0081] S100: preparing ceramic powder

[0082] The ceramic powder of the first ceramic layer includes the following components in mass percentage: 75% of alumina, 15% of silicon dioxide and 5% of pore-forming...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a porous ceramic material, a porous ceramic and a preparation method as well as application thereof in electronic cigarette. The porous ceramic includes several superposed ceramic layers, each of which has pores, the porous ceramic includes a bottom layer and a top layer, and the pore size of the porous ceramic's pores increases layer by layer from the bottom layer to thetop layer. The porous ceramic can be applied to the atomization core of electronic cigarette, wherein the bottom layer can control the oil absorption amount, and avoids the problems of low atomizationrate and small smoke amount caused by excessive oil absorption at a time. A heating element can be printed on the top layer, the electronic cigarette liquid flows to the top layer, because of the increase of the pore size, the contact surface of the electronic cigarette liquid and the heating element is enlarged, the cigarette liquid atomization rate is increased, and then the smoke volume is increased. Layer-by-layer increase of the pores' pore size can bring smooth guidance of cigarette liquid, reduces the problem of uneven atomization or damage caused by obstructed guidance of cigarette liquid, and enhances the user's experience. The porous ceramic can also be applied to products needing pores to control substance flux.

Description

technical field [0001] The invention relates to the technical field of ceramic materials, ceramic products and preparation techniques, in particular to porous ceramic materials, porous ceramics and preparation methods thereof. Background technique [0002] E-cigarette is an electronic product that imitates cigarettes. It has the same appearance, smoke, taste and feeling as cigarettes. It is a product that turns e-liquid into steam by means of atomization and other means, and allows users to smoke. [0003] The vaporizer core of the electronic cigarette is the core component of the electronic cigarette, which determines the size and taste of the smoke produced by the electronic cigarette. Because the smoke produced by the atomizing core made of porous ceramics has no peculiar smell, most of the atomizing cores for electronic cigarettes on the market use porous ceramic atomizing cores. However, the current distribution of pores in porous ceramics is not good, and the amount o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/117C04B35/622C04B35/634C04B38/06A24F47/00
Inventor 刘锋吴国亮郭剑唐杰黄荣林周培成
Owner DONGGUAN XINBO STRUCTURAL CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com