Eye shadow and preparation method thereof

A technology of eye shadow and talcum powder, which is applied in the field of eye shadow and its preparation, can solve the problems of not being able to enhance the three-dimensional sense of the eye, prone to itching and pain in allergic skin, and poor durability of eye shadow, so as to achieve good smudging effect, Enhanced three-dimensional, easy-to-apply effect

Inactive Publication Date: 2019-02-05
宁波金蒂化妆品有限公司
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Eye shadow is an indispensable part of makeup, and most eye shadow raw materials on the market currently contain heavy metal ingredients, which are highly irritating and prone to itching and pain for allergic skin, which leads some people not to use eye shadow
In addition, some eye shadows have poor durability, are easy to take off when exposed to water, and appear smudged, and cannot well enhance the three-dimensional effect of the eyes, thus failing to meet people's needs for makeup

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Eye shadow and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The raw material of the eye shadow of the present embodiment comprises following parts by weight:

[0051] 40 parts of talcum powder;

[0052] 6 parts mica powder;

[0053] Lubricant 1-part;

[0054] 2 parts mineral oil;

[0055] 2 parts emollient;

[0056] 1 part diisostearyl malate;

[0057] 3 parts emulsifier;

[0058] Catalyst 2 parts;

[0059] 3 parts preservative;

[0060] 10 parts of inorganic pigments;

[0061] 10 parts of deionized water.

[0062] Among them, the surface treatment process of talc powder is as follows: first mix polydimethylsiloxane and absolute ethanol at a volume ratio of 10%, then add 200 mesh talc powder and stir for 5 minutes, send it into an oven and bake it at 60°C 1h, natural cooling.

[0063] Specifically, the mica powder has a particle size of 2 μm and a silicon dioxide content of 44.1%.

[0064] The lubricant is a mixture of magnesium stearate and petrolatum.

[0065] The emollient is isooctyl palmitate.

[0066] The emul...

Embodiment 2

[0075] The raw material of the eye shadow of the present embodiment comprises following parts by weight:

[0076] 60 parts of talcum powder;

[0077] 10 parts of mica powder;

[0078] 3 parts lubricant;

[0079] 5 parts of mineral oil;

[0080] Emollient 5 parts;

[0081] 4 parts of diisostearyl malate;

[0082] 5 parts of emulsifier;

[0083] 8 parts of catalyst;

[0084] 9 parts of preservatives;

[0085] 28 parts of inorganic pigments;

[0086] 20 parts of deionized water.

[0087] Among them, the surface treatment process of talc powder is as follows: first mix polydimethylsiloxane and absolute ethanol at a volume ratio of 15%, then add 300 mesh talc powder and stir for 8 minutes, then put it into an oven and bake it at 80°C 1.5h, natural cooling.

[0088] Specifically, the mica powder has a particle size of 4 μm and a silicon dioxide content of 45.6%.

[0089] The lubricant is polyethylene wax.

[0090]The emollient is hydrogenated polyisobutylene.

[0091] T...

Embodiment 3

[0100] The raw material of the eye shadow of the present embodiment comprises following parts by weight:

[0101] 45 parts of talcum powder;

[0102] 7 parts mica powder;

[0103] 2 parts lubricant;

[0104] 3 parts mineral oil;

[0105] 2 parts emollient;

[0106] 4 parts of diisostearyl malate;

[0107] 3 parts emulsifier;

[0108] 4 parts of catalyst;

[0109] 8 parts of preservatives;

[0110] 15 parts of inorganic pigments;

[0111] 15 parts of deionized water.

[0112] Among them, the surface treatment process of talc powder is as follows: first mix polydimethylsiloxane and absolute ethanol at a volume ratio of 12%, then add 230 mesh talc powder and stir for 6 minutes, then put it into an oven and bake it at 67°C 1h, natural cooling.

[0113] Specifically, the mica powder has a particle size of 3 μm and a silicon dioxide content of 45.0%.

[0114] The lubricant is magnesium stearate.

[0115] The emollient is isooctyl palmitate.

[0116] The emulsifier is tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides eye shadow which is prepared from the following raw materials: talc powder, mica powder, a lubricant, mineral oil, an emollient, diisostearyl malate, an emulsifier, a preservative, a catalyst and inorganic pigment; the preparation method of the eye shadow comprises the following steps: mixing deionized water, the talc powder, the mica powder and the inorganic pigment and stirring to obtain a first mixture; adding the lubricant, the mineral oil, the emollient, the emulsifier and the diisostearyl malate into the first mixture, and stirring to obtain a second mixture; adding the preservative and the catalyst into the second mixture, and stirring uniformly; heating, putting into a mould and performing compression moulding to obtain the eye shadow. Since the raw materialsare natural minerals, the eye shadow provided by the invention is mild and non-irritant and thus is suitable for the users of various skin types; by combining the emollient, the emulsifier and the lubricant, the eye shadow has the advantages of easiness in smearing and lasting makeup, and further effectively covers the edema of eyes to achieve an aim of enhancing the stereoscopic impression of the eyes.

Description

technical field [0001] The invention belongs to the technical field of cosmetics, and in particular relates to an eye shadow and a preparation method thereof. Background technique [0002] Eye shadow is an indispensable part of makeup, but most eye shadow raw materials on the market currently contain heavy metal components, which are highly irritating and prone to itching and pain for allergic skin, which leads some people not to use eye shadow. In addition, some eye shadows have poor durability, are easy to take off when exposed to water, and appear smudged, and cannot well enhance the three-dimensional effect of the eyes, thus failing to meet people's needs for make-up. Contents of the invention [0003] The present invention aims at the deficiencies in the prior art, and the first purpose is to provide a mild and non-irritating eye shadow that can enhance the three-dimensional effect of the eyes. [0004] The second object of the present invention is to provide a metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/92A61K8/81A61K8/37A61K8/36A61K8/26A61K8/19A61K8/25A61Q1/10
CPCA61K8/19A61K8/25A61K8/26A61K8/361A61K8/37A61K8/8111A61K8/92A61K2800/72A61Q1/10
Inventor 李金辉
Owner 宁波金蒂化妆品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com