Jianzhan firing process

A kind of technology and green body technology, which is applied in the field of Jianzhan firing technology, can solve the problems of low yield rate and achieve the effect of high yield rate, sufficient combustion and easy control

Active Publication Date: 2019-01-29
南平市建阳区山石建盏陶瓷有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of the Jianzhan fired by the dragon kiln firewood method is smooth, the patterns are beautiful, and the pores are few, but the good product rate is very low (generally no more than 10%)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jianzhan firing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Jianzhan firing process includes the following steps:

[0033] (1) Provide body raw materials and glaze slurry, among which,

[0034] The raw material of the green body is prepared by the following method: 3 parts by weight of white clay, 3 parts by weight of red clay and 3 parts by weight of red clay are mixed, crushed, washed, passed through an 80-mesh sieve, settled, bagged, filtered and stale , Get the raw material of the green body;

[0035] The glaze slurry is prepared by the following method: mixing 10 parts by weight of glaze ore and 10 parts by weight of water, grinding with a ball mill for 2 hours, and adding 0.225 parts by weight of talc, 0.275 parts by weight of limestone, 0.09 parts by weight of bovine ashes, and 0.06 parts by weight. Parts by weight of iron red, 0.225 parts by weight of potash feldspar, 0.3 parts by weight of clay and 0.10 parts by weight of plant ash, grind for another 2 hours, pass through an 80-mesh sieve to obtain a glaze slurry;

[0036] (2)...

Embodiment 2

[0048] Jianzhan firing process includes the following steps:

[0049] (1) Provide body raw materials and glaze slurry, among which,

[0050] The raw material of the green body is prepared by the following method: 4 parts by weight of white clay, 2.5 parts by weight of red clay and 3.6 parts by weight of red clay are mixed, crushed, elutriated, passed through an 85-mesh sieve, settled, bagged, filtered, and aged , Get the raw material of the green body;

[0051] The glaze slurry is prepared by the following method: mixing 11 parts by weight of glaze ore and 12 parts by weight of water, grinding by a ball mill for 2.3 hours, and then adding 0.25 parts by weight of talc, 0.25 parts by weight of limestone, 0.95 parts by weight of bovine ashes, 0.05 parts by weight of iron red, 0.25 parts by weight of potash feldspar, 0.28 parts by weight of clay, and 0.15 parts by weight of plant ash, then grind for 2.5 hours and pass through a 90-mesh sieve to obtain a glaze slurry;

[0052] (2) Refinin...

Embodiment 3

[0064] Jianzhan firing process includes the following steps:

[0065] (1) Provide body raw materials and glaze slurry, among which,

[0066] The raw material of the green body is prepared by the following method: mixing 3.5 parts by weight of white clay, 3.5 parts by weight of red clay and 2.8 parts by weight of red clay, mixing, pulverizing, elutriating, passing through an 80-mesh sieve, precipitating, bagging, filtering, and aging , Get the raw material of the blank;

[0067] The glaze slurry is prepared by the following method: mixing 12 parts by weight of glaze ore, 11 parts by weight of water, grinding by a ball mill for 2.5 hours, then adding 0.24 parts by weight of talc, 0.30 parts by weight of limestone, 0.10 parts by weight of bovine ashes, 0.07 parts by weight of iron red, 0.23 parts by weight of potash feldspar, 0.33 parts by weight of clay and 0.12 parts by weight of plant ash, and then grind for 2.2 hours, pass through a 100-mesh sieve to obtain a glaze slurry;

[0068] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
areaaaaaaaaaaa
areaaaaaaaaaaa
areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Jianzhan firing process, comprising the steps of: providing green-body raw materials and a glaze slurry, conducting pugging on the green-body raw materials, conducting throwing shaping, and conducting trimming to obtain a green body; and putting the green body in an electric kiln for bisque firing, then conducting glazing, loading the glazed body in a sagger, sending thesagger into a chamber of a down draught kiln for sintering, conducting natural cooling, and taking the product out of the kiln. The formula, the firing atmosphere, the temperature curve and other technological flow are clear, easy to master and good in stability, the yield is high, the cost is low, prepared Jianzhan has less small pores, beautiful layered patterns, and a fine and moisture glaze surface, and can be favorably compared with Jianzhan produced through wood firing by a Dragon kiln.

Description

Technical field [0001] The invention relates to the technical field of porcelain, in particular to a Jianzhan firing process. Background technique [0002] Jianzhan is produced by Jian kiln. Jian kiln is one of the famous ancient kilns in my country. There are a large number of sites located in Jianyang District, Nanping City, Fujian Province (in ancient times, it was affiliated to Jianning Fu Ou Ning County). Its products have been famous in the Song Dynasty , Once sold overseas via the Maritime Silk Road. After the Song Dynasty, due to wars and other factors, Jianzhan firing skills were lost for hundreds of years. [0003] After the reform and opening up, the 800-year-old Jianzhan firing technique was restored and developed. On May 23, 2011, "Building Kiln and Building Burning Techniques" was included in the third batch of National Intangible Cultural Heritage Protection List. [0004] Since the development of Jianzhan in recent years, there are mainly two forms of production. On...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/34C03C8/00C04B41/86
CPCC03C8/00C04B33/04C04B33/34C04B41/5022C04B41/86C04B2235/656C04B2235/661C04B41/4539C04B41/0072
Inventor 吴继旺
Owner 南平市建阳区山石建盏陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com