High-tension copper-clad aluminum varnished wire processing method

A copper-clad aluminum wire, processing technology, applied in the direction of conductor/cable insulation, electrical components, circuits, etc., can solve the problem of large amount of enameled wire, and achieve high tension effect

Inactive Publication Date: 2018-11-27
深圳市广南电子有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to technical problems, the field of large-scale wire used in large transformers has been blank in China, and the amount of enameled wire used in this field is very large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The technical solutions of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0015] Copper-clad aluminum enameled wire processing technology in the present embodiment, it comprises the following steps:

[0016] Step 1, preparing a copper clad aluminum wire core with a copper content of 0.1 to 0.63 wt %;

[0017] Step 2, drawing the copper-clad aluminum wire core multiple times to obtain a wire with a predetermined diameter;

[0018] Step 3, performing internal oxidation treatment on the copper-clad aluminum wire core to obtain a copper-clad aluminum wire core with an Al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a copper-clad aluminum varnished wire processing method which comprises the following steps of 1, preparing a copper-clad aluminum wire core having copper content of 0.1-0.63wt%; 2, drawing the copper-clad aluminum wire core multiple times to obtain a wire having a predetermined diameter; 3, subjecting the copper-clad aluminum wire core to internal oxidation to obtain a copper-clad aluminum wire core having Al2O3 content of substantially 0.2 to 1.2 wt%; drawing the obtained Cu-Al2O3 copper-clad aluminum wire core having the predetermined size; 4, varnishing the copper-clad aluminum wire multiple times; 5, annealing the varnished copper-clad aluminum wire core in an annealing furnace, and placing the annealed copper-clad aluminum wire core in an oven for drying; and 6, collecting the copper-clad aluminum wire core. The produced copper-clad aluminum wire core has high tension.

Description

technical field [0001] The invention relates to a copper-clad aluminum enameled wire processing technology for enameled wire production. Background technique [0002] Enameled wire is the most representative product in electronic wire. Enameled wire is a main variety of winding wire, including copper-clad aluminum core and paint layer coated on the outside of copper-clad aluminum core. After the bare wire is annealed and softened, it is then passed through Painted and baked many times, it has four major properties: mechanical properties, chemical properties, electrical properties, and thermal properties. Copper-clad aluminum enameled wire is a new type of electromagnetic wire that uses copper-clad aluminum material as the inner conductor. Its characteristics are between copper and aluminum, combining the advantages of copper's excellent conductivity and aluminum's light weight. Micro motor rotor coils and various electromagnetic wires are widely used. [0003] With the rap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/06H01B13/16C22F1/08C22F1/04
Inventor 郑和阳
Owner 深圳市广南电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products