A method of using black sand waste to make environmentally friendly bricks

An environmentally friendly brick and waste technology, applied in the field of brick production, to achieve the effect of more holes, increased smoothness, and stable structure

Active Publication Date: 2021-01-08
荥经县朱氏砂器有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there has not been any kind of technology that specifically solves these wastes, so after years of research, the applicant's R&D team finally found a solution: on the one hand, it can help other manufacturers to process these wastes to achieve environmental protection; on the other hand, it can It can turn waste into wealth and generate market value and benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for making environmentally friendly bricks from black sand waste, comprising the following steps in sequence:

[0028] Pulverization: Send the black sand waste into the pulverizer and pulverize it to a black sand waste powder with a fineness of 60 mesh;

[0029] Ingredients: After adding additives to the black sand waste powder, stir evenly to obtain a mixture. The weight percentage of black sand waste powder and additive in the mixture is 11:9;

[0030] Making mud: After adding water to the mixture, stir it evenly to get the mud, the weight percentage of the mixture and water in the mud is 6:4;

[0031] Compression molding: send the mud into the compression molding machine and extrude to obtain bricks;

[0032] Drying: send the adobe into the drying room for drying; the drying temperature is 40°C, and the drying time is 10 hours;

[0033] Spraying mud: put the soil into the ball mill and add water to grind it into 180-mesh mud, put the mud into the spraying ...

Embodiment 2

[0038] A method for making environmentally friendly bricks from black sand waste, comprising the following steps in sequence:

[0039] Pulverization: Send the black sand waste into the pulverizer and pulverize it to a black sand waste powder with a fineness of 100 mesh;

[0040] Ingredients: After adding additives to the black sand waste powder, stir evenly to obtain a mixture. The weight percentage of black sand waste powder and additives in the mixture is 12:8;

[0041] Making mud: After adding water to the mixture, stir it evenly to get the mud, the weight percentage of the mixture and water in the mud is 6:4;

[0042] Compression molding: send the mud into the compression molding machine and extrude to obtain bricks;

[0043] Drying: send the adobe into the drying room for drying; the drying temperature is 45°C, and the drying time is 11 hours;

[0044] Spray mud: Put the soil into the ball mill and add water to grind it into 200-mesh mud, put the mud into the spraying m...

Embodiment 3

[0049] A method for making environmentally friendly bricks from black sand waste, comprising the following steps in sequence:

[0050] Pulverization: Send the black sand waste into the pulverizer and pulverize it to a black sand waste powder with a fineness of 180 mesh;

[0051] Ingredients: After adding additives to the black sand waste powder, stir evenly to obtain a mixture. The weight percentage of black sand waste powder and additives in the mixture is 13:7;

[0052] Making mud: After adding water to the mixture, stir it evenly to get the mud. The weight percentage of the mixture and water in the mud is 7:3;

[0053] Compression molding: send the mud into the compression molding machine and extrude to obtain bricks;

[0054] Drying: send the adobe into the drying room for drying; the drying temperature is 50°C, and the drying time is 12 hours;

[0055] Spraying mud: send the soil into the ball mill, add water and grind it into 300-mesh mud, put the mud into the spraying...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for making an environmental-friendly brick by black sand waste materials. The method sequentially comprises the following steps of crushing, material proportioning, mud material preparation, mold pressing shaping, drying, slurry spraying, firing and cooling. The method has the advantages that the process is simple; the operation is convenient; black sand waste materials generated in the black sand industry can be used for producing environmental-friendly bricks, so that the black sand waste materials which are always useless in many years are changed into valuable materials; the pollution of the black sand waste materials on the peripheral environment is effectively avoided; the treatment cost is reduced; the environmental-friendly effect is good.

Description

technical field [0001] The invention relates to the field of brick production, in particular to a method for making environmentally friendly bricks by using black sand waste. Background technique [0002] Gucheng Village (Guchengping), Liuhe Township, Yingjing County, Ya'an City, Sichuan Province is the main production place of Yingjing sandware and the location of the "Yandao Ancient City Site", a provincial-level cultural relic protection unit in Sichuan Province. The sandware produced here was called "Yingjing casserole" before 1981. After 1981, with the development of diversified technology of products, tea sets, food cooking utensils and appearance crafts can be made, which are collectively called "Yingjing casserole". Sand Ware" or "Yingjing Black Sand Ware". [0003] With the continuous development of "Yingjing black sand ware", the reputation is gradually radiating all over the world, and the production scale and output are increasing year by year. According to the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132C04B33/13
CPCC04B33/131C04B33/132C04B33/1324Y02P40/60
Inventor 朱庆平
Owner 荥经县朱氏砂器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com