Novel efficient energy-saving type mortar and preparation method thereof

An energy-saving and high-efficiency technology, applied in the field of mortar, can solve the problems of poor water penetration resistance, poor thermal insulation performance, and poor mortar strength, and achieves improved water penetration resistance, high use value, and good thermal insulation. The effect of thermal insulation

Inactive Publication Date: 2018-07-10
HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The strength of the existing mortar is not very good, and the thermal insulation performance is not good at the same time. In addition, the water penetration resistance is poor, and further improvement is still needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A new high-efficiency and energy-saving mortar of the present embodiment includes the following raw materials in parts by weight:

[0031] 36 parts of cement, 28 parts of quartz sand, 18 parts of modified methyl cellulose, 16 parts of vinyl ester resin, 14 parts of cellulose diacetate, 12 parts of nano calcium carbonate, 6 parts of magnesia lime, 4 parts of melamine, water retaining agent 1 part, thickener 1 part, water reducing agent 1 part.

[0032] The preparation method of the modified methyl cellulose of this embodiment is to add methyl cellulose to the sulfuric acid solution, the stirring speed is 135r / min, and the stirring time is 45min, and then it is added into the sodium hydroxide solution for alkalization until the solution is Neutral, add benzoyl peroxide and silane coupling agent to it, continue to stir for 35 minutes, then add nano-silica microspheres, increase the stirring speed to 155r / min, and stir for 25 minutes to obtain the modified methyl cellulose...

Embodiment 2

[0042] A new high-efficiency and energy-saving mortar of the present embodiment includes the following raw materials in parts by weight:

[0043] 42 parts of cement, 32 parts of quartz sand, 22 parts of modified methyl cellulose, 20 parts of vinyl ester resin, 18 parts of cellulose diacetate, 14 parts of nano calcium carbonate, 10 parts of magnesia lime, 8 parts of melamine, water retaining agent 3 parts, thickener 2 parts, water reducing agent 3 parts.

[0044] The preparation method of the modified methyl cellulose of this embodiment is to add methyl cellulose to the sulfuric acid solution, the stirring speed is 145r / min, and the stirring time is 55min, and then it is added into the sodium hydroxide solution for alkalization until the solution is Neutral, add benzoyl peroxide and silane coupling agent to it, continue to stir for 45 minutes, then add nano-silica microspheres, increase the stirring speed to 165r / min, and stir for 35 minutes to obtain the modified methyl cellu...

Embodiment 3

[0054] A new high-efficiency and energy-saving mortar of the present embodiment includes the following raw materials in parts by weight:

[0055] 39 parts of cement, 30 parts of quartz sand, 20 parts of methyl cellulose, 18 parts of vinyl ester resin, 16 parts of cellulose diacetate, 13 parts of nano calcium carbonate, 8 parts of magnesia lime, 6 parts of melamine, 2 parts of water retaining agent , 1.5 parts of thickener, 2 parts of water reducer.

[0056] The preparation method of the modified methyl cellulose of this embodiment is to add methyl cellulose to the sulfuric acid solution, the stirring speed is 140r / min, and the stirring time is 50min, and then it is added into the sodium hydroxide solution for alkalization until the solution is Neutral, then add benzoyl peroxide and silane coupling agent to it, continue to stir for 35-45min, then add nano-silica microspheres, increase the stirring speed to 160r / min, and stir for 30min to obtain the modified Methylcellulose.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses novel efficient energy-saving type mortar, which is prepared from the following raw materials in parts by weight: 36 to 42 parts of cement, 28 to 32 parts of quartz sand, 18 to22 parts of modified methylcellulose, 16 to 20 parts of vinyl ester resin, 14 to 18 parts of cellulose diacetate, 12 to 14 parts of nano calcium carbonate, 6 to 10 parts of magnesium limestone, 4 to8 parts of melamine, 1 to 3 parts of water-retaining agents, 1 to 2 parts of thickening agents and 1 to 3 parts of water reducing agents. The invention aims at providing the novel efficient energy-saving type mortar; the mortar has high strength and excellent water penetration resistant capability; in addition, good heat preservation and heat insulation effects are achieved; compared with the prior art, the mortar has the advantages that the effect is obviously improved; the use values are higher; the application prospects are good.

Description

technical field [0001] The invention relates to the technical field of mortar, in particular to a novel high-efficiency and energy-saving mortar and a preparation method thereof. Background technique [0002] Mortar is a bonding substance used in building bricks. It is composed of a certain proportion of sand and cementing materials (cement, lime paste, clay, etc.) It is called cement lime mortar), lime mortar and clay mortar. According to the composition materials, ordinary mortar can also be divided into: lime mortar: it is made of lime paste, sand and water according to a certain ratio. It is generally used for low-strength requirements. Wet masonry and plastering layer; cement mortar: made of cement, sand and water according to a certain ratio, generally used for masonry, wall or ground in wet environment or water; mixed mortar: in cement or lime mortar It is made by adding appropriate admixtures such as fly ash and diatomaceous earth to save the amount of cement or lim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/12C04B111/27
CPCC04B28/12C04B2111/27C04B14/06C04B24/383C04B24/26C04B14/28C04B7/00C04B24/128C04B2103/44C04B2103/302C04B2103/465
Inventor 王磊
Owner HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap